Hydrophobic geogrid and preparation method thereof

A soil and water grid technology, applied in the field of hydrophobic geogrid and its preparation, can solve the problems of inability to meet requirements, unfavorable environmental protection, poor mechanical properties, etc., and achieve improved mechanical properties, strong corrosion resistance, and anti-leakage. good effect

Inactive Publication Date: 2016-10-12
ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to literature reports, the preparation of thermotropic liquid crystal copolyester / graphene composites adopts the process of in-situ solution polymerization, which needs to consume a large amount of solvent during the preparation process, which is not conducive to environmental protection, and is prepared by in-situ solution polymerization. The thermotropic liquid crystal copolyester / graphene composite material has poor mechanical properties and cannot meet the requirements of practical applications;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A kind of hydrophobic geogrid, it is made up of the following raw materials by weight:

[0018] Isothiazolinone 0.1, dodecyl dimethyl betaine 1, graphene oxide 5, p-hydroxybenzoic acid 40, acetic anhydride 10, zinc acetate 0.08, 6-hydroxynaphthoic acid 20, high-density polyethylene 180, hexafluoro Acetylacetone 0.2, Calcium Palmitate 1, Glyceryl Caprylate 2, Zinc Dialkyl Dithiophosphate 1, Hexamethylcyclotrisiloxane 1, Calcium Stearate 3, Epoxidized Soybean Oil 5.

[0019] A kind of preparation method of described hydrophobic geogrid, comprises the following steps:

[0020] (1) Take 60% of the weight of the above acetic anhydride, mix it with p-hydroxybenzoic acid, add it to an oil bath at 138°C, keep stirring for 10 minutes, add 0.01% of the weight of the mixture, 96% sulfuric acid dropwise, and keep warm for 3 hours, discharge the material, pour it into ice water 1.6 times its weight while it is hot, let it stand for 3 minutes, blow dry, send it into a vacuum drying ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrophobic geogrid which is prepared from the following raw materials in parts by weight: 0.1-0.4 part of isothiazolinone, 1-2 parts of dodecyl dimethyl betaine, 5-7 parts of graphene oxide, 40-50 parts of para-hydroxybenzoic acid, 10-17 parts of acetic anhydride, 0.08-0.1 part of zinc acetate, 20-30 parts of 6-hydroxy-2-naphthoic acid, 180-200 parts of high-density polyethylene, 0.2-0.3 part of hexafluoroacetylacetone, 1-2 parts of calcium palmitate, 2-3 parts of glyceryl caprylate-caprate, 1-2 parts of zinc dialkyl dithiophosphate, 1-2 parts of hexamethyl cyclotrisiloxane, 3-4 parts of calcium stearate and 5-7 parts of epoxy soybean oil. The geogrid has the advantages of favorable hydrophobicity, favorable anti-seepage effect and high corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of geogrids, in particular to a hydrophobic geogrid and a preparation method thereof. Background technique [0002] Thermotropic liquid crystal copolyester has excellent comprehensive properties, such as high strength, high modulus, good thermal stability and molding processability, etc., so that it can be widely used in aerospace, national defense and military industry, optical fiber communication, electronic appliances and other high-tech industries. technology field. Although thermotropic liquid crystal copolyester has excellent comprehensive properties, the development of science and technology has put forward higher requirements for this material, especially in some special fields, it needs to have higher modulus, strength and thermal stability. Therefore, it is necessary to modify the thermotropic liquid crystal copolyester materials. A large number of studies have shown that nanomaterials such as car...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L67/04C08K13/06C08K9/06C08K9/04C08K3/04C08G63/06
CPCC08G63/06C08L23/06C08L2205/03C08L2207/062C08L67/04C08K13/06C08K9/06C08K9/04C08K3/04
Inventor 叶磊
Owner ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products