Dyeing composition, preparation method and dyeing technology

A composition and process technology, applied in the field of dyeing, can solve the problems of color paste polluting the environment and processing equipment, the concentration of color paste cannot be higher, and the amount of color paste added is small. The effect of poor performance and low dye usage

Active Publication Date: 2016-10-12
上海顺茁塑胶科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The color paste dyeing has the following problems: 1. The storage performance is poor, and the color paste will settle and delaminate if it is not used for a day; 2. The color paste has the defects of polluting the environment and processing equipment
Because the color paste is difficult to clean, workers need to spend a lot of time cleaning equipment, hoppers and the environment after each production. They can only wipe it with organic solvents. The volatiles are discharged into the atmosphere and cause exhaust gas pollution. There will be a certain amount of residue and waste every time; 3. The concentration of the color paste cannot be made higher (currently 5%)
Since the amount of color paste added in this industry is usually 3 to 8 / 10,000, if the concentration of color paste is increased, the amount of color paste added will be less. If the dispersion is not uniform enough, the problem of color inaccuracy will easily occur.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] The preparation method of dyeing composition of the present invention comprises the following steps:

[0048] (1) In terms of weight percentage, mix and stir 3% to 75% of pigments, 1% to 3% of dispersants, 5% to 10% of high molecular polymers, and 12% to 91% of low molecular polymers ;

[0049] (2) Transport the material in step (1) to the melting reactor for heating and stirring, and the heating temperature is set as required, preferably 120°C-260°C, more preferably 120°C-150°C;

[0050] (3) Transport the material in step (2) to the internal mixing equipment, heat and knead, and set the heating temperature during kneading as required, preferably 120°C-260°C, more preferably 120°C-150°C;

[0051] (4) Transport the material in step (3) to granulation equipment for granulation, dry and remove water and collect the material to obtain the dyeing composition.

[0052] The processing process of the above-mentioned dyeing composition is cold processing, the investment in equ...

Embodiment 1

[0055] This embodiment provides a black dyeing composition for PP non-woven fabrics, including: 60 parts of high-pigment carbon black+3 parts of antistatic agent 264+10 parts of EVA resin+27 parts of special lubricant for PP.

[0056] In the present embodiment, the pigment adopts high pigment carbon black, the dispersant adopts antistatic agent 264 (BASF), the high molecular polymer adopts EVA resin (Mitsui P2807), and the low molecular polymer adopts modified polypropylene wax (PP special lubricant ).

[0057] Preparation:

[0058] Send the mixed material into a high-speed mixer and stir for 1 hour. The material that comes out is in the form of a lump, and then enters the melting reactor to heat and stir at a temperature of 120 ° C to 260 ° C. After 1 hour, the material is qualified and discharged.

[0059] The hot material that comes out is immediately input into the internal mixer and kneaded for 1 hour, the temperature is 120 ° C ~ 150 ° C, enters the granulator through t...

Embodiment 2

[0064] This embodiment provides a blue PVB plastic sheet dyeing composition, comprising: 15 parts of 15:4 phthalocyanine blue K7014, 1 part of modified polysiloxane, 1 part of antioxidant 1010, 1 part of 3GO enhancer Plastic agent, 10 parts of polyvinyl butyral resin, 72 parts of low molecular weight EVA wax.

[0065] In this embodiment, the pigment adopts 15:4 phthalocyanine blue K7014 (BASF), the dispersant adopts modified polysiloxane, antioxidant 1010 and 3GO plasticizer (triethylene glycol diisocaprylate), and the polymer The polymer adopts polyvinyl butyral resin, and the low molecular polymer adopts low molecular EVA wax (BASFEVA3).

[0066] The preparation method is the same as that in Example 1, and the average particle size of the prepared dyeing composition can be in the range of 0.1 mm to 3 mm.

[0067] The advantages of the dyeing composition of this embodiment:

[0068] The dyeing composition of this embodiment is used for dyeing. Because the particles of the d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a dyeing composition, a preparation method and a dyeing technology. The dyeing composition is solid particles and is prepared from, by weight, 3%-75% of pigments, 1%-3% of a dispersing agent, 5%-10% of a high-molecular polymer and 12%-91% of a low-molecular polymer, wherein a resin polymer is adopted as the high-molecular polymer, and a wax substance is adopted as the low-molecular polymer. The pigment content of the dyeing composition can reach up to 75%, the dispersity is good, and equipment and an environment are easy to clean when the dyeing composition is used.

Description

technical field [0001] The invention relates to the technical field of dyeing, in particular to a dyeing composition, a preparation method and a dyeing process. Background technique [0002] In the current plastic dyeing market, there are three main types of dyeing materials, namely toner, masterbatch, and color paste, as follows: [0003] Regarding toner, in plastic products, most companies still use toner, such as carbon black. The advantage of toner is that the unit price is relatively low, which is more suitable for enterprises with stricter cost requirements. The disadvantages are also obvious: first, during the processing, the toner dust pollution is very large, and will cause secondary pollution of the product; second, since the toner is usually a chemical, the dust of the toner is very harmful to the health of the employees. And in the processing process, the reusability of resin added with toner is poor, especially some important colors. [0004] Masterbatches ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09B67/20C09B67/42C09C3/10C09C3/12C09C3/08D06P3/79
CPCC01P2004/61C09B67/006C09B67/0092C09B67/0095C09C3/006C09C3/08C09C3/10C09C3/12D06P3/79
Inventor 孙建谢栋梁魏信龙
Owner 上海顺茁塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com