Release paper for adhesive tape and preparation method of release paper

A technology of release paper and tape, applied in the direction of paper, papermaking, paper coating, etc., can solve the problems of high price, toxicity, increase production cost, etc., and achieve the effect of reducing production cost, good release performance and reducing usage

Inactive Publication Date: 2016-10-12
湖南省和祥润新材料有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the existing production process of anti-adhesive paper, a layer of silicone oil with anti-adhesive effect is coated on the entire surface of the backing paper, and the raw material price of the silicone oil is expensive, which increases the production cost, and most of the silicone oil is diluted with organic solvents. Organic solvents are volatile and difficult to completely recycle. The production process is not only toxic, but also not conducive to environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of release paper for adhesive tape, comprises base material, coating layer, release agent layer, film layer, mist coating and release agent coating, and described coating layer and release agent layer are respectively positioned at base material On both sides of the surface, the film layer, matte coating and release agent coating are sequentially coated on the anti-adhesive layer; the raw materials of the coating layer include: 30 parts of polyethylene, modified polyolefin 5 parts, 3 parts of stabilizer, and 0.5 part of plasticizer; the raw materials of the matte coating according to parts by weight include: 0.1 part of nano-silica powder, 0.2 part of nano-alumina powder, 8 parts of silane coupling agent , 30 parts of vinyl siloxane, 2 parts of hydrogen-containing siloxane, 80 parts of solvent, 0.1 part of platinum, 0.5 part of initiator; the raw materials of the release agent coating include: 40 parts of amino silicone oil, 3 parts of joint agent, 10 parts of ch...

Embodiment 2

[0035] A kind of release paper for adhesive tape, comprises base material, coating layer, release agent layer, film layer, mist coating and release agent coating, and described coating layer and release agent layer are respectively positioned at base material On both sides of the surface, the film layer, matte coating and release agent coating are sequentially coated on the anti-adhesive layer; the raw materials of the coating layer include: 32 parts of polyethylene, modified polyolefin 6 parts, 3.5 parts of stabilizer, and 0.6 part of plasticizer; the raw materials of the matte coating according to parts by weight include: 0.15 parts of nano-silica powder, 0.25 part of nano-alumina powder, and 9 parts of silane coupling agent , 35 parts of vinyl siloxanes, 2.5 parts of hydrogen-containing siloxanes, 82 parts of solvents, 0.12 parts of platinum, and 0.6 parts of initiators; the raw materials of the release agent coating according to parts by weight include: 45 parts of amino si...

Embodiment 3

[0045] A kind of release paper for adhesive tape, comprises base material, coating layer, release agent layer, film layer, mist coating and release agent coating, and described coating layer and release agent layer are respectively positioned at base material On both sides of the surface, the film layer, the matte coating and the release agent coating are sequentially coated on the anti-adhesive layer; the raw materials of the coating layer include: 35 parts of polyethylene, modified polyolefin 8 parts, 4 parts of stabilizing agent, 0.8 part of plasticizer; The raw material of described matte coating comprises according to weight part: 0.2 part of nano-silica powder, 0.3 part of nano-alumina powder, 10 parts of silane coupling agent , 40 parts of vinyl siloxane, 3 parts of hydrogen-containing siloxane, 85 parts of solvent, 0.15 part of platinum, and 0.8 part of initiator; the raw materials of the release agent coating include: 50 parts of amino silicone oil, 4 parts of joint a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a release paper for an adhesive tape and a preparation method thereof. The release paper for an adhesive tape comprises a base material, a coating layer, a release agent layer, a film layer, a fog surface coating and a release agent coating; the fog surface The raw materials of the coating include: nano-silica powder, nano-alumina powder, silane coupling agent, vinyl siloxane, hydrogen-containing siloxane, solvent, platinum, initiator; release agent coating The raw materials of the layer include: amino silicone oil, cross-linking agent, chromium-containing organic complex, reactive diluent, antioxidant, photoinitiator, high-viscosity methyl silicone oil, methyl pentynol, azo compound foaming agent. The recesses of the present invention are not coated with anti-adhesive agent, thereby reducing the amount of silicone oil used and the amount of organic solvent used, and the produced anti-adhesive paper has good anti-adhesive performance, which not only reduces production costs, but also meets the requirements of environmental protection and energy saving , has great development potential and market demand.

Description

technical field [0001] The invention relates to the technical field of release materials, in particular to a release paper for adhesive tape and a preparation method thereof. Background technique [0002] The release paper is mainly pasted on the glued surface of the tape to protect the adhesive layer on the surface of the tape. The anti-adhesive paper is composed of a base paper, an isolation layer and an anti-adhesive layer. The preparation process is to coat a layer of release agent on the entire surface of the base paper (the release agent used mainly includes polyethylene), and then coat the surface of the coating layer with a layer of release agent. A layer of release agent (adopted release agent is mainly silicone oil) is coated to obtain release paper. [0003] In the existing production process of anti-adhesive paper, since the entire surface of the backing paper is coated with a layer of anti-adhesive silicone oil, the raw material of the silicone oil is expensive...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/84D21H19/82D21H23/30D21H23/46D21H23/22D21H25/00D21H19/22D21H19/14D21H19/16
CPCD21H19/84D21H19/14D21H19/16D21H19/22D21H19/82D21H23/22D21H23/30D21H23/46D21H25/005
Inventor 廖平湘
Owner 湖南省和祥润新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap