Redispersible latex type flexible binder for manganese-slag lightweight ceramic tiles and preparation method for redispersible latex type flexible binder

A technology for redispersing latex and ceramic tiles, applied in the field of building materials, can solve problems such as difference in effect, and achieve the effect of wide application, wide pH value range and low operating cost

Inactive Publication Date: 2016-11-09
XUZHOU INSTITUTE OF TECHNOLOGY
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even if the same product from different manufacturers is applied to different manufacturers, there are cases where the effect is quite different

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Redispersible latex type flexible binder for manganese-slag lightweight ceramic tiles and preparation method for redispersible latex type flexible binder
  • Redispersible latex type flexible binder for manganese-slag lightweight ceramic tiles and preparation method for redispersible latex type flexible binder
  • Redispersible latex type flexible binder for manganese-slag lightweight ceramic tiles and preparation method for redispersible latex type flexible binder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Prepare a kind of redispersible latex type manganese slag light-weight ceramic brick flexible binder of the present invention according to the following steps, and by weight:

[0027] Step 1: In the continuous stirred tank reactor, add 226.78 parts of demineralized water, 18.225 parts of C12-15-fatty alcohol polyoxyethylene ether sulfate, start the mixer in the continuous stirred tank reactor, and set the speed at 19.586 rpm, start the dual-zone heating device in the continuous stirred tank reactor, make the temperature rise to 34.924°C, add α-methyl-ω-[(tetrahydro-2-furyl)methoxy]poly[oxygen(formyl) base-1,2-ethylidene)] 21.518 parts, stirred evenly, carried out iodolactonization reaction for 11.288 minutes, added 17.986 parts of p-ethylbenzenesulfonamide, and the flow rate was 10.794m 3 The neon gas of / min is 0.19 hours; Add 20.579 parts of 2,6-dinitro-p-toluene in the continuous stirred tank reactor afterwards, start the double zone heating device in the continuous ...

Embodiment 2

[0035] Prepare a kind of redispersible latex type manganese slag light-weight ceramic brick flexible binder of the present invention according to the following steps, and by weight:

[0036]Step 1: In the continuous stirred tank reactor, add 451.269 parts of demineralized water, 60.562 parts of C12-15-fatty alcohol polyoxyethylene ether sulfate, start the mixer in the continuous stirred tank reactor, and set the speed at 65.960 rpm, start the dual-zone heating device in the continuous stirred tank reactor, make the temperature rise to 35.578°C, add α-methyl-ω-[(tetrahydro-2-furyl)methoxy]poly[oxygen(formyl) Base-1,2-ethylene)] 130.702 parts, stir evenly, carry out iodolactonization reaction. 22.270 minutes, add 34.630 parts of p-ethylbenzenesulfonamide, and the flow rate is 51.0m 3 The neon gas of / min is 0.84 hours; Add 77.60 parts of 2,6-dinitro-p-toluene in the continuous stirred tank reactor afterwards, start the double zone heating device in the continuous stirred tank re...

Embodiment 3

[0044] Prepare a kind of redispersible latex type manganese slag light-weight ceramic brick flexible binder of the present invention according to the following steps, and by weight:

[0045] Step 1: In the continuous stirred tank reactor, add 226.978 parts of demineralized water, 18.9225 parts of C12-15-fatty alcohol polyoxyethylene ether sulfate, start the mixer in the continuous stirred tank reactor, and set the speed at 19.9586 rpm, start the dual-zone heating device in the continuous stirred tank reactor, make the temperature rise to 34.9924°C, add α-methyl-ω-[(tetrahydro-2-furyl)methoxy]poly[oxygen(formyl) base-1,2-ethylidene)] 21.9518 parts, stirred evenly, carried out iodolactonization reaction for 11.9288 minutes, added 17.9986 parts of p-ethylbenzenesulfonamide, and the flow rate was 10.9794m 3 The neon gas of / min is 0.919 hour; Add 20.9579 parts of 2,6-dinitro-p-toluene in the continuous stirred tank reactor afterwards, start the double zone heating device in the co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a redispersible latex type flexible binder for manganese-slag lightweight ceramic tiles and a preparation method for the redispersible latex type flexible binder. The redispersible latex type flexible binder is prepared from the following ingredients in parts by weight: demineralized water, C12-15-fatty alcohol-polyoxyethylene ether sulfate, alpha-methyl-omega-[(tetrahydro-2-furyl)methoxy]poly[oxo(methyl-1,2-ethylene)], p-ethylbenzenesulfonamide, 2,6-dinitro-p-methylaniline, 1-amino-2-[4-[(hexahydro-2-oxo-1H-azepin-1-yl)methyl]phenoxy]-4-hydroxyl-9,10-anthraquinone, 4-hydroxyanthraquinone-2-carboxylic acid, AR-methoxybenzyl alcohol, copper micro / nanoparticles, 4,4'-diamino-3,3'-dichlorodiphenylmethane, dodecenyl succinic anhydride, p-tetramethylene xylene diisocyanate, benzotriazole-N,N,N',N'-tetramethylurea hexafluorophosphate, (Z)-2-(2-aminothiazol-4-yl)-2-triphenylmethoxyimino(2-mercaptobenzothiazole)acetate and alpha-bromoethyl isovalerate. According to the method, the saponification of the flexible binder is prevented, the surface tension of materials is lowered, and the building materials can be attached more firmly.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a flexible binder for redispersible latex-type manganese slag light-weight ceramic tiles and a manufacturing method thereof. Background technique [0002] According to statistics, in 2015, the national ceramic tile output was 10.18 billion square meters, and the ceramic tile soil output was more than 2 billion cubic meters, 40% of which were mixed with various additives. Furthermore, my country's construction industry is developing rapidly. For 1544.54 million square meters and 1066.51 million square meters, due to the needs of these development situations, the research and development of high-performance ceramic tiles and soil additives for ceramic tiles is imminent. [0003] Since the thirties in the 20th century, Englishman Goddard has obtained a patent with resin as a grinding aid. People have tested grinding aids such as acetic acid, phosphate, lignosulfonate, ethylene glyc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/632C04B33/138
CPCC04B33/138C04B35/632Y02P40/60
Inventor 梁峙梁骁
Owner XUZHOU INSTITUTE OF TECHNOLOGY
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com