Anion health-care viscose fabric

A health care viscose fiber and negative ion technology, applied in the field of clothing fabrics, can solve the problems of low quality and high price, and achieve good physical properties, good compatibility and good antibacterial effect

Active Publication Date: 2016-11-09
江苏华拓纺织科技有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the domestic market, clothing fabrics are generally dominated by acrylic and polyester, with a small amount of cotton and wool. The quality is low or the price is expensive, which cannot meet market demand. Therefore, it has become a trend to develop clothing fabrics that can meet consumer needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anion health-care viscose fabric
  • Anion health-care viscose fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A negative ion health-care viscose fabric, which is formed by weaving after blending negative ion health-care viscose fibers and cotton fibers into yarn;

[0028]Wherein, the preparation process of the negative ion health-care viscose fiber includes: dissolving sodium alginate in a sodium hydroxide solution with a concentration of 5 wt%, stirring at 90°C for 1 hour to obtain sodium alginate colloid; Purpose negative ion powder is added in described sodium alginate colloid under stirring condition, after stirring evenly, obtain the sodium alginate colloid containing negative ion powder; Soak in sodium hydroxide solution for 1 h at 40°C to obtain a cellulose alkalized product; add 37% CS based on the total fiber weight to the cellulose alkalized product 2 , stirring and reacting at -10°C for 2h to obtain a viscose solution; adding 0.2% of the sodium alginate colloid containing negative ion powder based on the total weight of the fiber to the viscose solution and stirring ...

Embodiment 2

[0030] A negative ion health-care viscose fabric, which is formed by weaving after blending negative ion health-care viscose fibers and cotton fibers into yarn;

[0031] Wherein, the preparation process of the negative ion health-care viscose fiber includes: dissolving sodium alginate in a sodium hydroxide solution with a concentration of 8 wt%, stirring at 70°C for 3 hours to obtain sodium alginate colloid; Purpose negative ion powder is added in described sodium alginate colloid under stirring condition, after stirring evenly, obtain the sodium alginate colloid containing negative ion powder; Soak in sodium hydroxide solution for 1.5h at 30°C to obtain a cellulose alkalized product; add 35% CS based on the total fiber weight to the cellulose alkalized product 2 , stirred and reacted at 20°C for 1 hour to obtain a viscose solution; 3% of the sodium alginate colloid containing negative ion powder based on the total weight of the fiber was added to the viscose solution and stir...

Embodiment 3

[0037] A negative ion health-care viscose fabric, which is formed by weaving after blending negative ion health-care viscose fibers and cotton fibers into yarn;

[0038] Wherein, the preparation process of the negative ion health-care viscose fiber includes: dissolving sodium alginate in a sodium hydroxide solution with a concentration of 6 wt%, stirring at 80°C for 2 hours to obtain sodium alginate colloid; Purpose negative ion powder is added in described sodium alginate colloid under stirring condition, after stirring evenly, obtain the sodium alginate colloid containing negative ion powder; Soak in sodium hydroxide solution for 1.2h at 35°C to obtain a cellulose alkalized product; add 36% CS based on the total fiber weight to the cellulose alkalized product 2 , stirring and reacting at 5°C for 1.5h to obtain a viscose solution; adding 1.6% of the sodium alginate colloid containing anion powder based on the total weight of the fiber to the viscose solution and stirring even...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anion health-care viscose fabric. The anion health-care viscose fabric is formed by weaving yarns which are formed by blending anion health-care viscose and cotton fibers; a preparation technology of the anion health-care viscose fabric comprises the steps that sodium alginate colloid is prepared; anion powder is added into the sodium alginate colloid, and uniform stirring is conducted, colloid containing the anion powder is obtained; bamboo fibers, taxus chinensis fibers and microporous lignocellulose are added into sodium hydroxide for soaking, CS2 is added, a stirring reaction is conducted, and a viscose solution is obtained; the colloid containing the anion powder is added into the viscose solution to be stirred to be uniform, grinding is conducted, and a viscose mixed solution before spinning is obtained; filtering, defoaming, curing, spinning, desulfurization, water washing, oiling and drying are conducted, and the anion health-care viscose fabric is obtained. The anion health-care viscose fabric has the advantages of being good in skin adaptability, moisture absorption and liberation and air permeability, resistant to bacteria, healthy, green, environmentally friendly and the like.

Description

technical field [0001] The invention relates to the technical field of clothing fabrics, in particular to a negative ion health-care viscose fabric. Background technique [0002] With the improvement of people's material and cultural level, people's requirements for textiles are also increasing, not only requiring warmth and beauty, but also paying more attention to comfort and functionality. Functional textiles have become one of the future development trends of the textile industry, and together with fine-denier fiber textiles, non-woven fabrics, composite materials, and environmentally friendly materials, they will constitute the major trend of future textiles. The development of today's science and technology provides a guarantee for the development of functional textiles. At the same time, it also plays a greater role in promoting the development of textile enterprises and product structure adjustment and increases the added value of textiles. Research and production o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/02D01F8/18D01F1/10D03D15/00D02G3/04D01D1/02D06C3/00D06C7/02D03D15/217D03D15/225D03D15/47D03D15/50
CPCD01D1/02D01F1/10D01F8/02D01F8/18D02G3/04D06C3/00D06C7/02D10B2201/24D10B2201/02D03D15/47
Inventor 邱再明
Owner 江苏华拓纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap