Bismaleimide modified calcium carbonate filler with functions of sound absorption and sound isolation

A technology of calcium carbonate filler and polyimide, which is applied in the field of calcium carbonate filler, can solve the problem that the application performance has not been improved, and achieve the effect of good filling reinforcement and enhanced damping and shock absorption

Inactive Publication Date: 2016-12-07
凤台县精华助剂有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the dispersibility of the calcium carbonate filler obtained by this method has been improved, the application performance has not been improved yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The sound-absorbing and sound-insulating bismaleic polyimide modified calcium carbonate filler of the present embodiment is made of the following raw materials in parts by weight: 200 parts of calcium carbonate powder, 5 parts of acrylate rubber powder, 2 parts of quartz powder, spray carbon 2 parts of black, 100 parts of hydrogen peroxide, 10 parts of peroxidase, 6 parts of polyethylene glycol octylphenyl ether, 250 parts of dimethylformamide, 2 parts of 5-hydroxylevulinic acid, 4,4-diphenyl 3 parts of methyl methane bismaleimide, 3 parts of diethyl malonate, 0.5 parts of catalyst, 2 parts of cetyltrimethylammonium bromide, 2 parts of titanium dioxide, isooctyl dimethyl dimercaptoacetate 3 parts of tin, 3 parts of sodium lignosulfonate, 3 parts of hydroxyl silicone oil, appropriate amount of acetone, appropriate amount of deionized water.

[0014] A sound-absorbing and sound-insulating bismaleic polyimide modified calcium carbonate filler is prepared by the following s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a bismaleimide modified calcium carbonate filler with the functions of sound absorption and sound isolation. The filler is prepared from the following raw materials in parts by weight: 200 parts of calcium carbonate powder, 4 to 5 parts of acrylic ester rubber powder, 1 to 2 parts of quartz powder, 1 to 2 parts of spraying carbon black, 80 to 100 parts of hydrogen peroxide, 8 to 10 parts of peroxidase, 6 to 8 parts of polyethylene glycol octylphenol ether, 200 to 250 parts of dimethylformamide, 1 to 2 parts of 5-hydroxylevulinic acid, 2 to 3 parts of 4,4-diphenylmethane bimaleimide, 2 to 3 parts of ethyl malonate, 0.5 to 1 part of catalysts, 1 to 2 parts of hexadecyl trimethyl ammonium bromide, 1 to 2 parts of titanium dioxide, 2 to 3 parts of dimethyl octyltin mercaptide, 2 to 3 parts of sodium lignin sulfonate, 2 to 3 parts of hydroxyl silicone oil and a proper amount of acetone and de-ionized water. The filler has the advantages that the added acrylic ester rubber powder, the quartz powder and the spraying carbon black are used in a matched way, so that the functions of damping vibration attenuation, sound absorption and sound isolation of calcium carbonate are greatly enhanced.

Description

technical field [0001] The invention relates to a calcium carbonate filler, in particular to a sound-absorbing and sound-insulating bismaleimide-modified calcium carbonate filler. Background technique [0002] Calcium carbonate is an important class of functional inorganic fillers. It has the advantages of low price, abundant reserves, stable performance, easy processing, and non-toxicity. It can significantly improve the processing performance and physical properties of materials and reduce production costs. It is widely used In the fields of plastics, rubber, coatings, papermaking, etc., because calcium carbonate is a hydrophilic compound, there are defects such as insufficient compatibility with polymers and poor dispersion in practical applications, and satisfactory filling and reinforcing effects cannot be achieved. Therefore, Calcium carbonate needs to be modified to improve its dispersion and compatibility in various materials, so as to achieve the effect of improving...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08K13/06C08K9/04C08K3/26C08K3/36C08K3/04
CPCC08K3/04C08K3/26C08K3/36C08K9/08C08K13/06C08K2003/265
Inventor 王俊华朱传路
Owner 凤台县精华助剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products