A hydrogen-producing material for hydrogen-rich water and its preparation method and application

A technology for hydrogen-rich water and raw materials, which is applied in the production of hydrogen, added material water/sewage treatment, etc., can solve the problems of poor durability of hydrogen production, inconvenient use, and ineffective utilization of magnesium hydroxide as a precipitate.

Active Publication Date: 2017-12-01
HUBEI UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the magnesium hydroxide produced by the reaction will prevent the further reaction of the hydrogen-producing agent and water, and the hydrogen production has poor durability. After a period of use, it must be cleaned and removed with acid, which brings inconvenience to use. use efficiently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The present invention provides a method for preparing a hydrogen-producing material for hydrogen-rich water provided by the above scheme, comprising the following steps:

[0032] (1) the raw materials Al, Ga, In, Sr and Bi 2 o 3 Mix to obtain a mixed material;

[0033] (2) Grinding the mixed material obtained in the step (1) to obtain a hydrogen-producing material for hydrogen-rich water;

[0034] The step (1) and the step (2) are carried out under an inert gas atmosphere.

[0035] The invention mixes the raw materials to obtain the mixed material. In the present invention, the mixing is preferably carried out under an inert gas atmosphere. The present invention has no special requirements for the mixing method, and the mixing method well known to those skilled in the art can be used. In the embodiment of the present invention, the specific use of the The manner in which raw materials are mixed in a ball milling pot, the ball milling pot is specifically a ball milli...

Embodiment 1

[0048] (1) 94.5wt% Al, 1.0wt% Ga, 1.0wt% In, 1.5wt% Sr and 2wt% Bi by mass percentage 2 o 3 , weigh the raw materials, put a total of 20g into a ball mill jar made of aluminum alloy, in which Ga is added in a liquid state, and other raw materials are added in the form of metal powder, the particle size is in the range of 300-400 mesh, Sr and Bi 2 o 3 The purity of Al and In is greater than 99.99%, and the purity of Al and In is greater than 99%. After all raw materials are mixed evenly, the ball milling tank is sealed in a glove box filled with argon.

[0049] (2) Ball milling parameters are set, and the mixed raw materials are ball milled, wherein the ball to material ratio: 12:1, ball milling time: 12h, spindle speed: 200r / min.

[0050] (3) After the ball milling is completed, screen the sieves with a pore size of 200 mesh and 100 mesh to obtain particles with a particle size of 100 to 200 mesh, pack the particles in a glove box filled with argon protection, and vacuumize ...

Embodiment 2

[0053] (1) 93.0wt% Al, 1.0wt% Ga, 1.5wt% In, 2.5wt% Sr and 2wt% Bi by mass percentage 2 o 3, weigh the raw materials, put a total of 20g into a ball mill jar made of aluminum alloy, in which Ga is added in a liquid state, and other raw materials are added in the form of metal powder, the particle size is in the range of 300-400 mesh, Sr and Bi 2 o 3 The purity of Al and In is greater than 99.99%, and the purity of Al and In is greater than 99%. After all raw materials are mixed evenly, the ball milling tank is sealed in a glove box filled with argon.

[0054] (2) Set ball milling parameters, and ball mill the mixed raw materials, wherein the ball-to-material ratio: 15:1, ball milling time: 11 hours, spindle speed: 3000r / min.

[0055] (3) After the ball milling is completed, screen the sieves with a pore size of 200 mesh and 100 mesh to obtain particles with a particle size of 100 to 200 mesh, pack the particles in a glove box filled with argon protection, and vacuumize the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a hydrogen-producing material for hydrogen-rich water, which is made by grinding raw materials including the following mass percentages: Al 60-97.5wt%, Ga 0.5-10wt%, In 0.5-10wt%, Sr 0.5-10wt%, Bi2O3 1.0-10wt%. The present invention also provides a method for preparing hydrogen-producing materials for hydrogen-rich water. During the grinding process, defects formed between components and the presence of intermetallic compounds destroy the dense oxides on the aluminum surface, and Bi2O3 reacts with metal aluminum to generate Bi , Destroy the oxide film on the surface of metal aluminum, which is conducive to the continuous progress of the hydrolysis hydrogen production reaction, and improves the durability of the hydrogen production material in the process of producing hydrogen. The hydrogen-producing material for hydrogen-rich water provided by the present invention has strong controllability in the hydrogen production process, and there will be no accumulation of relatively high-concentration hydrogen gas; 1g of hydrogen-producing material can realize continuous hydrogen production for 1 to 2 minutes to stabilize hydrogen production and stable hydrogen supply .

Description

technical field [0001] The invention belongs to the technical field of hydrogen production materials, and in particular relates to a hydrogen production material for hydrogen-rich water and a preparation method and application thereof. Background technique [0002] Water is an important part of human tissue. The content of water in the human body is as high as 70%. 60% of the water in the human body exists in cells, and 40% exists in fluids such as blood, digestive juice, and saliva. Medical research shows that many diseases, including aging, are caused by the accumulation of free radicals in the body that cannot be removed in time. Oxygen entering the body is transported to each cell through the red blood cells in the blood, and sugar and fat are burned and consumed in order to generate energy in each cell. Among them, 2% of the oxygen will become active oxygen, so a large amount of active oxygen will be produced in the human body. The peroxidative lethality of oxygen fre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C32/00C22C1/05C01B3/08C02F1/68
CPCY02E60/36
Inventor 董仕节罗平王辉虎常鹰官旭熊灿谢志雄
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap