Outdoor billboard based on electrochromic device and manufacturing method thereof

A technology of electrochromic device and manufacturing method, applied in the field of manufacturing, can solve problems such as being difficult to realize

Inactive Publication Date: 2016-12-07
吴桂广
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the particularity of its outdoor location, outdoor billboards are required to be able to adjust the brightness of information display according to the i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Outdoor billboard based on electrochromic device and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] The billboard component 10 , the electrochromic device 20 and the regulation module 30 are assembled.

[0067] Making the electrochromic device 20 includes:

[0068] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0069] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 320nm;

[0070] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 220nm; W film is used as WO 3 a growth source for the nanowires;

[0071] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtaine...

Embodiment 2

[0086] The billboard component 10 , the electrochromic device 20 and the regulation module 30 are assembled.

[0087] Making the electrochromic device 20 includes:

[0088] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0089] a. Magnetron sputtering fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 360nm;

[0090] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 200nm; W film is used as WO 3 a growth source for the nanowires;

[0091] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained pr...

Embodiment 3

[0106] The billboard component 10 , the electrochromic device 20 and the regulation module 30 are assembled.

[0107] Making the electrochromic device 20 includes:

[0108] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0109] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film on the surface of tempered glass 1 with a specific size, with a thickness of about 340nm;

[0110] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 210nm; W film is used as WO 3 a growth source for the nanowires;

[0111] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an outdoor billboard based on an electrochromic device and a manufacturing method thereof. The structure and a manufacturing process of the electrochromic device are improved, so that the electrochromic device has self-energizing characteristic, the obtained novel electrochromic device is short in discolouration response time, extremely high in photoelectric energy conversion efficiency, prolonged in life and good in freezing tolerance, the manufacturing method disclosed by the invention is simple and easy to operate, and industrial production can be easily realized.

Description

technical field [0001] The invention belongs to the field of manufacturing, and more specifically relates to an outdoor billboard based on an electrochromic device and a manufacturing method thereof. Background technique [0002] Billboard is a display system for displaying information such as products and services, and generally refers to all media that transmit information. Due to the particularity of its outdoor location, outdoor billboards are required to be able to adjust the brightness of information display according to the intensity of sunlight. However, the existing outdoor billboards are all made of metal, wood, glass and other materials. It is difficult to achieve this function. Contents of the invention [0003] Aiming at the problems existing in the background technology, the present invention provides an outdoor billboard based on an electrochromic device and its manufacturing method, which improves the structure and manufacturing process of the self-powered...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G02F1/155G09F9/00
CPCG02F1/155G09F9/00
Inventor 吴桂广
Owner 吴桂广
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap