Thermal insulation mortar and production method thereof

A technology of thermal insulation mortar and glass fiber, applied in the field of construction mortar, can solve the problem of easy cracking of thermal insulation mortar, and achieve the effects of strong adhesion, improved tensile strength and wear resistance, and high bonding strength

Inactive Publication Date: 2017-01-11
柳州市国正机电物资有限责任公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a thermal insulation mortar and its production method, which can solve the problem that the existing expanded perlite thermal insulation mortar is easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal insulation mortar and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The thermal insulation mortar in this example is prepared from the following raw materials in parts by weight: 50 parts of expanded perlite, 15 parts of cement, 14 parts of river sand, 20 parts of fly ash, 4 parts of polypropylene particles, 3 parts of glass fiber, modified 1 part of seaweed, 2 parts of anti-cracking agent; wherein, the anti-cracking agent is mixed by hydrogenated castor oil, calcium sulfoaluminate and epoxy resin, and the mass ratio of hydrogenated castor oil, calcium sulfoaluminate and epoxy resin is 1 : 3: 7; The diameter of the glass fiber in this embodiment is 6 microns, and the length is 7 nanometers.

[0014] The method for making thermal insulation mortar in this embodiment is characterized in that it includes the following steps: adding expanded perlite, river sand, and fly ash to a pulverizer for grinding, adjusting the rotating speed to 100r / min, and grinding for 5 hours to obtain granules A mixture with a thickness of 1mm; then mix evenly wi...

Embodiment 2

[0017] The thermal insulation mortar in this example is prepared from the following raw materials in parts by weight: 55 parts of expanded perlite, 12 parts of cement, 12 parts of river sand, 23 parts of fly ash, 6 parts of polypropylene particles, 5 parts of glass fiber, modified 1.5 parts of seaweed, 4 parts of anti-cracking agent; wherein, the anti-cracking agent is mixed by hydrogenated castor oil, calcium sulfoaluminate and epoxy resin, and the mass ratio of hydrogenated castor oil, calcium sulfoaluminate and epoxy resin is 1 : 4: 3.5; The diameter of the glass fiber in this embodiment is 15 microns, and the length is 5 nanometers.

[0018] The method for making thermal insulation mortar in this embodiment is characterized in that it includes the following steps: adding expanded perlite, river sand, and fly ash to a pulverizer for grinding, adjusting the rotating speed to 100r / min, and grinding for 5 hours to obtain granules A mixture with a thickness of 0.7mm; then mix e...

Embodiment 3

[0021] The thermal insulation mortar in this example is prepared from the following raw materials in parts by weight: 60 parts of expanded perlite, 10 parts of cement, 17 parts of river sand, 28 parts of fly ash, 8 parts of polypropylene particles, 7.5 parts of glass fiber, modified 1.2 parts of seaweed, 5 parts of anti-cracking agent; wherein, the anti-cracking agent is mixed by hydrogenated castor oil, calcium sulfoaluminate and epoxy resin, and the mass ratio of hydrogenated castor oil, calcium sulfoaluminate and epoxy resin is 1 : 5: 5; The glass fiber in this embodiment has a diameter of 10 microns and a length of 10 nanometers.

[0022] The method for making thermal insulation mortar in this embodiment is characterized in that it includes the following steps: adding expanded perlite, river sand, and fly ash to a pulverizer for grinding, adjusting the rotating speed to 100r / min, and grinding for 5 hours to obtain granules The mixture with a thickness of 0.5mm; then mix it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses thermal insulation mortar and a production method thereof and relates to the technical field of building mortar. The thermal insulation mortar is produced from expanded perlite, cement, river sand, coal ash, ethylene propylene rubber particles, glass fibers, modified seaweed and an anti-cracking agent, wherein the anti-cracking agent is formed by mixing hydrogenated castor oil, calcium sulphoaluminate and epoxy resin. The thermal insulation mortar can carry out thermal insulation for a long time and is difficult to crack, high in bonding strength with a basement layer, and hollowing is hardly caused; meanwhile, tensile strength and abrasion resistance can be obviously improved, so that the thermal insulation mortar is smoother, has strong adhesive force with a base material and hardly falls off.

Description

technical field [0001] The invention relates to the technical field of building mortar, in particular to a thermal insulation mortar and a manufacturing method thereof. Background technique [0002] Insulation mortar is a kind of ready-mixed dry powder mortar made of various lightweight materials as aggregates, cement as cementitious material, mixed with some modified additives, and mixed by the production enterprise; among them, light aggregates are mostly For expanded perlite. Expanded perlite thermal insulation mortar is made of high-quality acidic volcanic glass rock, which is crushed, dried, put into a high-temperature roasting furnace, and expanded instantaneously. It can be used as loose-fill thermal insulation materials for buildings and thermal equipment; cement, water glass, asphalt, resin, etc. can be used as cementing materials to make various shapes of thermal insulation products, such as plate tubes. [0003] Expanded perlite has a wide range of applications ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/34
CPCC04B28/00C04B2111/343C04B2201/20C04B2201/32C04B2201/50C04B14/185C04B14/068C04B18/08C04B24/2611C04B14/42C04B18/24C04B24/08C04B22/14C04B24/281
Inventor 郝世文
Owner 柳州市国正机电物资有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap