Rat-proof EPDM (ethylene-propylene-diene monomer) cable material and preparation method thereof

A technology of EPDM100 and cable material, which is applied in the field of rodent-proof EPDM cable material and its preparation, can solve the problems of not being able to effectively avoid rodent damage and not having rodent-proof performance, and achieve improved rodent-proof performance, good fire resistance, and improved flame-retardant performance Effect

Inactive Publication Date: 2017-01-11
FOSHAN FEISHIDA NEW MATERIAL TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this cable material, like common EPDM cable material, does not ha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Anti-rat EPDM cable material, its components by weight are as follows: 100 parts of EPDM, 5 parts of activator made by mixing zinc oxide and stearic acid in a mass ratio of 3:1, 23 parts of fumed white carbon black, 8 parts of paraffin oil 2.5 parts of anti-aging agent MB, 2.4 parts of DCP, 1.2 parts of TAC, 24 parts of calcined clay, 10 parts of maleic anhydride grafted EPDM, and 5 parts of rodent control agent.

[0031] The steps of its preparation method are as follows:

[0032] (1) Add beryllium sulfate tetrahydrate into ultrapure water, stir magnetically until completely dissolved to obtain a beryllium sulfate solution, add ammonia water dropwise to the beryllium sulfate solution under stirring conditions, adjust the pH value to 10 and continue stirring for 3 hours, transfer Put it into an autoclave, put the autoclave into an oven, take it out after reacting at 110°C for 4 hours, cool it to room temperature, and centrifuge it, wash it with deionized water and aceto...

Embodiment 2

[0037] Anti-rat EPDM cable material, its components by weight are as follows: 100 parts of EPDM, 7 parts of active agent made by mixing zinc oxide and stearic acid in a mass ratio of 3:1, 21 parts of fumed white carbon black, 6 parts of paraffin oil 3 parts, 3 parts of anti-aging agent MB, 2 parts of DCP, 2 parts of TAC, 26 parts of calcined clay, 8 parts of maleic anhydride grafted EPDM, 5.2 parts of rodent control agent.

[0038] Its preparation method is identical with embodiment 1.

Embodiment 3

[0040] Anti-rat EPDM cable material, its components by weight are as follows: 100 parts of EPDM, 9 parts of active agent made by mixing zinc oxide and stearic acid in a mass ratio of 3:1, 19 parts of fumed white carbon black, 4 parts of paraffin oil 4 parts, 4 parts of anti-aging agent MB, 2.1 parts of DCP, 1.8 parts of TAC, 28 parts of calcined clay, 6 parts of maleic anhydride grafted EPDM, 5.4 parts of rodent control agent.

[0041] Its preparation method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rat-proof EPDM (ethylene-propylene-diene monomer) cable material, which is prepared from the following ingredients in parts by weight: 100 parts of EPDM, 5 to 10 parts of active agents, 18 to 23 parts of reinforcing agents, 4 to 9 parts of plasticizers, 2 to 4 parts of anti-aging agents, 2 to 3 parts of cross-linking agents, 1 to 2 parts of assistant crosslinkers, 23 to 28 parts of filling agents, 6 to 11 parts of compatilizers and 5 to 6 parts of anti-rat agents. The invention also discloses a preparation method of the rat-proof EPDM cable material. The rat-proof EPDM cable material provided by the invention has the advantages that the rat-proof performance is better; the rat damage can be effectively avoided.

Description

technical field [0001] The invention relates to a cable material, in particular to a rodent-proof EPDM cable material and a preparation method thereof. Background technique [0002] EPDM, or ethylene propylene diene rubber, is a terpolymer of ethylene, propylene, and non-conjugated diene, which is crosslinked chemically or by irradiation. EPDM cable material has the advantages of polyolefin insulated wire and ordinary rubber insulated wire: [0003] 1) Soft, flexible, elastic, non-adhesive at high temperature, long-term aging resistance, and resistance to harsh weather (-60 ~ 125 ° C). [0004] 2) Ozone resistance, UV resistance, electrical insulation resistance, and chemical corrosion resistance. [0005] 3) Oil resistance and solvent resistance are comparable to those of general-purpose neoprene rubber insulation. It is processed by ordinary hot extrusion processing equipment and irradiated cross-linking, which is easy to process and low in cost. [0006] The publicatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L91/06C08L51/04C08K13/06C08K9/10C08K9/06C08K3/22C08K5/09H01B7/18
CPCC08L23/16C08K2201/011C08L2201/02C08L2203/202C08L2205/03H01B7/1805C08L91/06C08L51/04C08K13/06C08K9/10C08K9/06C08K3/22C08K2003/2296C08K5/09C08L51/003
Inventor 叶青
Owner FOSHAN FEISHIDA NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka