Water-based detergent for aluminum alloy

A cleaning agent, water-based technology, applied in the field of aluminum alloy water-based cleaning agent, can solve problems such as affecting product appearance, corroding parts, polluting the environment, etc., to improve the processing environment and sanitation, eliminate dirt, and clean metal surfaces. Effect

Inactive Publication Date: 2017-02-01
WUHAN UN LUBRICANT TECH
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] After various processing of aluminum alloy, some lubricating oil stains are often left on the surface of the aluminum material. If the oil stains are not completely removed, serious brown oil spots will appear in the later processing, which will seriously affect the appearance of the product.
At present, cleaning agents for aluminum alloys at home and abroad generally use solvent cleaning or strong acid and strong alkali cleaning, which will cause some problems such as environmental pollution and corrosion of parts. Under the requirements of modern industry, higher requirements are put forward for aluminum alloy cleaning agents. Therefore, need a kind of aluminum alloy water-based cleaning agent to change the above-mentioned problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The water-based cleaning agent for aluminum alloy parts of the present embodiment includes the following components by weight percentage: 6% alcohol ether carboxylate, 6% polycarboxylate, 12% alcohol ether surfactant, 7.5% oleamide, 1.75% Diethanolamine, 1.75% Triethanolamine, 1.2% Benzoate, 0.8% Polyglycolate, 1.2% Carbonate, 1.5% Borax, 0.5% Sodium Hydroxide, 6% Alcohol, the rest is deionized Water was added to 100%.

[0015] In this embodiment, the polycarboxylate is disodium edetate. In this embodiment, the disodium edetate is replaced by tetrasodium edetate, lemon One of sodium oxyacetate and sodium glycolate; or a mixture of disodium edetate, tetrasodium edetate, sodium citrate, and sodium hydroxyacetate in the same weight percentage, all of which are qualified cleaning agents , there was no significant difference in the properties of the obtained products.

[0016] In this embodiment, the alcohol ether surfactant is fatty alcohol polyoxyethylene ether; in this ...

Embodiment 2

[0022] The water-based cleaning agent for aluminum alloy parts of the present embodiment comprises the following components by weight percentage: 2% alcohol ether carboxylate, 2% polycarboxylate, 5% alcohol ether surfactant, 5% oleamide, 1% diethanolamine, 1% triethanolamine, 0.5% benzoate, 2.1% polyglycolic acid salt, 1.5% carbonate, 0.5% borax, 0.3% sodium hydroxide, 2% alcohol, the rest is deionized Water was added to 100%.

[0023] In this embodiment, the polycarboxylate is tetrasodium edetate. In this embodiment, the tetrasodium edetate is replaced by disodium edetate, lemon One of sodium oxyacetate and sodium glycolate; or a mixture of tetrasodium edetate, disodium edetate, sodium citrate, and sodium hydroxyacetate in the same weight percentage, all of which are qualified cleaning agents , there was no significant difference in the properties of the obtained products.

[0024] In this embodiment, the alcohol ether surfactant is alkylphenol polyoxyethylene ether; in thi...

Embodiment 3

[0030] The water-based cleaning agent for aluminum alloy parts of the present embodiment comprises the following components by weight percentage: 10% alcohol ether carboxylate, 10% polycarboxylate, 20% alcohol ether surfactant, 10% oleamide, 2.5% diethanolamine, 2.5% triethanolamine, 2% benzoate, 2.5% polyglycolic acid salt, 0.8% carbonate, 0.5% borax, 0.2% sodium hydroxide, 10% alcohol, balance deionized Water was added to 100%.

[0031] In this embodiment, the polycarboxylate is sodium citrate. In this embodiment, the sodium citrate is replaced by tetrasodium edetate, disodium edetate, hydroxyl One of sodium acetate; or replace it with a mixture of sodium citrate, tetrasodium edetate, disodium ethylenediaminetetraacetate, and sodium glycolate according to the same weight percentage to obtain a qualified cleaning agent. No significant difference.

[0032] In this embodiment, the alcohol ether surfactant is sorbitan monooleate; in this embodiment, sorbitan monooleate is repl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-based detergent for an aluminum alloy. The detergent comprises the following components in percentages by weight: 1-30% of a surfactant, 1-20% of polybasic carboxylic acid, 5-10% of oleamide, 0.5-5% of polyhydroxyacetate, 1-5% of carbonate, 0.05-0.1% of sodium hydroxide, 1-15% of alcohols and deionized water, totaling 100%. The water-based detergent can effectively remove greasy dirt and oxidation films on the surface of the aluminum alloy, so that the surface quality of the aluminum alloy is good.

Description

technical field [0001] The invention relates to a water-based cleaning agent for aluminum alloys. Background technique [0002] After various processing of aluminum alloy, some lubricating oil stains are often left on the surface of the aluminum material. If the oil stains are not completely removed, serious brown oil spots will appear in the later processing, which will seriously affect the appearance of the product. At present, cleaning agents for aluminum alloys at home and abroad generally use solvent cleaning or strong acid and strong alkali cleaning, which will cause some problems such as environmental pollution and corrosion of parts. Under the requirements of modern industry, higher requirements are put forward for aluminum alloy cleaning agents. Therefore, there is a need for a water-based cleaning agent for aluminum alloys to change the above problems. Contents of the invention [0003] The purpose of the present invention is to provide a water-based cleaning ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/22C23G5/024
CPCC23G1/22C23G5/024
Inventor 赵建平
Owner WUHAN UN LUBRICANT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap