Automobile air conditioner blower shell based on diatomaceous earth modification, and preparation method thereof

A technology of automobile air conditioner and diatomite, which is applied in the field of automobile air conditioner components, can solve the problems affecting the performance of fan blades, deformation, and mechanical performance reduction, and achieve excellent weather resistance and mechanical properties, easy to obtain raw materials, and simple steps Effect

Inactive Publication Date: 2017-02-22
芜湖德鑫汽车空调有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because there is a large temperature difference between the temperature of the blower shell of the automobile air conditioner during the working process and the temperature after it stops working, under such a large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention provides a method for preparing a diatomite-based modified automobile air-conditioning blower shell, comprising:

[0014] 1) ball milling starch, silica gel, cyclodextrin, dodecyl ethoxy sulfobetaine, graphene and ornithine to obtain modified starch;

[0015] 2) calcining diatomite, graphite, molybdenite and sodium tungstate in the presence of protective gas to obtain a modified composition;

[0016] 3) PC (polycarbonate), PP (polypropylene), PA (polyamide), rosin, hydroxyethyl cellulose, glass fiber, titanate, simethicone, diisodecyl phthalate , zinc oxide, modified starch and the modified composition are mixed and shaped to prepare a diatomite-based modified automobile air-conditioning blower housing.

[0017] In step 1) of the present invention, the specific conditions of ball milling can be selected in a wide range, but in order to make the automobile air-conditioning blower shell modified based on diatomite have more excellent weather resistance and ...

Embodiment 1

[0029] 1) Starch, silica gel, cyclodextrin, dodecyl ethoxy sulfobetaine, graphene and ornithine were ball milled at 120°C for 14 hours at a weight ratio of 100:28:39:20:8:25 to produce modified starch.

[0030] 2) Mix diatomite, graphite, molybdenite and sodium tungstate in a weight ratio of 100:51:10:38; and in the presence of nitrogen, heat up from 25°C to 380°C at a rate of 2°C / min °C and keep it for 1.5h, then raise the temperature to 580°C at a rate of 0.8°C / min and keep it for 4h to prepare the modified composition.

[0031] 3) PC (weight average molecular weight is 4000), PP (weight average molecular weight is 7000), PA (weight average molecular weight is 6000), rosin, hydroxyethyl cellulose, glass fiber, titanate, simethicone, Diisodecyl phthalate, zinc oxide, modified starch and the modified composition are mixed according to the weight ratio of 100:68:29:21:6:25:12:38:31:27:39:20, and Kneading at 190°C for 3 hours and molding to obtain diatomaceous earth-based blow...

Embodiment 2

[0033] 1) Starch, silica gel, cyclodextrin, dodecyl ethoxy sulfobetaine, graphene and ornithine were ball milled at 110°C for 12 hours according to the weight ratio of 100:22:34:14:6:22 to produce modified starch.

[0034] 2) Mix diatomaceous earth, graphite, molybdenite and sodium tungstate in a weight ratio of 100:45:7:32; and in the presence of helium, heat up from 15°C at a rate of 1°C / min to 350°C and keep it for 1h, then raise the temperature to 550°C at a rate of 0.5°C / min and keep it for 3h to prepare the modified composition.

[0035] 3) PC (weight average molecular weight is 2000), PP (weight average molecular weight is 6000), PA (weight average molecular weight is 4000), rosin, hydroxyethyl cellulose, glass fiber, titanate, simethicone, Diisodecyl phthalate, zinc oxide, modified starch and the modified composition are mixed according to the weight ratio of 100:66:22:15:5:20:9:33:28:20:30:17, and Kneading at 185°C for 2 hours and molding to obtain diatomaceous eart...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an automobile air conditioner blower shell based on diatomaceous earth modification, and a preparation method thereof. The preparation method comprises the following steps: (1) carrying out ball milling on starch, silica gel, cyclodextrin, dodecyl ethoxy sulphobetaine, graphene and ornithine to obtain modified starch; (2) calcining diatomaceous earth, graphite, molybdenite and sodium wolframate in existence of a shielding gas to obtain a modified composition; and (3) carrying out mixing and molding on PC, PP, PA, rosin, hydroxy ethyl cellulose, glass fibers, titanate, dimethyl silicon oil, diisodecyl phthalate, zinc oxide, the modified starch and the modified composition to obtain the automobile air conditioner blower shell based on diatomaceous earth modification. The automobile air conditioner blower shell based on diatomaceous earth modification prepared by the method has excellent weather resistance and mechanical properties, and simultaneously the preparation method has simple steps and easily available raw materials.

Description

technical field [0001] The invention relates to automobile air-conditioning components, in particular to a diatomite-based modified automobile air-conditioning blast shell and a preparation method thereof. Background technique [0002] The car air conditioner blower shell is an important part of the car air conditioner blower. The car air conditioner blower mainly plays the role of blowing hot or cold air to play the role of gas circulation, and the car air conditioner blower shell plays the role of protecting the car air conditioner. The internal parts of the blower also play the role of forming the air duct. [0003] At present, the blower shell of the automobile air conditioner is generally made of polymer materials. Because there is a large temperature difference between the temperature of the blower shell of the automobile air conditioner during the working process and the temperature after it stops working, under such a large temperature difference, the blower shell o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L23/12C08L77/00C08L93/04C08L1/28C08L83/04C08L3/04C08K13/06C08K9/00C08K7/14C08K5/12C08K3/22C08K3/36C08K3/04C08K3/24
CPCC08L69/00C08L2201/08C08L2205/035C08L23/12C08L77/00C08L93/04C08L1/286C08L83/04C08L3/04C08K13/06C08K9/00C08K7/14C08K5/12C08K2003/2296C08K3/36C08K3/04C08K3/24
Inventor 李茂勇陈天祥
Owner 芜湖德鑫汽车空调有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap