High-wear-resistant and high-oil-resistant fireproof coating and preparation method thereof

A fire retardant coating, high wear resistance technology, used in fire retardant coatings, antifouling/underwater coatings, cement coatings, etc., can solve the problems of film surface adhesion, wear resistance, oil resistance, frost resistance, flame Taking into account other issues, to achieve the effect of improving moisture resistance, excellent oil resistance, and inhibiting water infiltration

Inactive Publication Date: 2017-03-15
TONGLING XIANGYUN FIRE FIGHTING TECH
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing fire retardant coatings have the problems of coating film surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1:

[0016] A highly wear-resistant, oil-resistant and fire-resistant coating made of the following parts by weight of raw materials: 3 parts of Portland cement, 15 parts of corundum powder, 5 parts of fluorinated graphite, 15 parts of diatomaceous earth, 8 parts of rice husk ash, and talc 5 parts, 8 parts of tung oil, 3 parts of metakaolin, 3 parts of modified tourmaline powder, 5 parts of aluminum dihydrogen phosphate, 10 parts of acrylic resin, 5 parts of ammonium polyphosphate, 1 part of titanate coupling agent, 5 parts of pentaerythritol, 6 parts of porous starch, 2 parts of zinc borate, 3 parts of palm fiber, 10 parts of chlorohydrin rubber tackifying resin.

[0017] The modified tourmaline powder is prepared by the following method: the tourmaline powder and the silane coupling agent are mixed at a weight ratio of 5:1, and then water equal to 2 times the amount of the mixture is added, and the slurry is mixed and poured into a ball mill. Ultra-fine grinding, ...

Example Embodiment

[0023] Example 2:

[0024] A highly wear-resistant, oil-resistant and fire-retardant coating made of the following parts by weight of raw materials: 40 parts of Portland cement, 12 parts of corundum powder, 6 parts of fluorinated graphite, 12 parts of diatomaceous earth, 9 parts of rice husk ash, and talc 6 parts, 9 parts of tung oil, 4 parts of metakaolin, 4 parts of modified tourmaline powder, 6 parts of aluminum dihydrogen phosphate, 12 parts of acrylic resin, 5 parts of ammonium polyphosphate, 2 parts of titanate coupling agent, 5 parts of pentaerythritol, 7 parts of porous starch, 3 parts of zinc borate, 4 parts of palm fiber, 11 parts of chlorohydrin rubber tackifying resin.

[0025] The modified tourmaline powder is prepared by the following method: the tourmaline powder and the silane coupling agent are mixed at a weight ratio of 5:1, and then water equal to 2 times the amount of the mixture is added, and the slurry is mixed and poured into a ball mill. Ultra-fine grinding...

Example Embodiment

[0031] Example 3:

[0032] A high wear-resistant, oil-resistant and fire-retardant coating made of the following raw materials by weight: 50 parts of Portland cement, 10 parts of corundum powder, 8 parts of fluorinated graphite, 15 parts of diatomaceous earth, 10 parts of rice husk ash, and talc 6 parts, 10 parts of tung oil, 5 parts of metakaolin, 5 parts of modified tourmaline powder, 7 parts of aluminum dihydrogen phosphate, 15 parts of acrylic resin, 6 parts of ammonium polyphosphate, 3 parts of titanate coupling agent, 6 parts of pentaerythritol, 7 parts of porous starch, 3 parts of zinc borate, 5 parts of palm fiber, 12 parts of chlorohydrin rubber tackifying resin.

[0033] The modified tourmaline powder is prepared by the following method: the tourmaline powder and the silane coupling agent are mixed at a weight ratio of 5:1, and then water equal to 2 times the amount of the mixture is added, and the slurry is mixed and poured into a ball mill. Ultra-fine grinding, ball mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-wear-resistant and high-oil-resistant fireproof coating and a preparation method thereof. The high-wear-resistant and high-oil-resistant fireproof coating comprises, by weight, 30-50 parts of silicate cement, 10-15 parts of alundum powder, 5-8 parts of carbon monofluoride, 10-15 parts of kieselguhr, 8-10 parts of rice hull ash, 5-6 parts of talcum powder, 8-10 parts of tung oil, 3-5 parts of partial kaolinite, 3-5 parts of modified electric powder, 5-7 parts of aluminum dihydrogen phosphate, 10-15 parts of acrylic resin, 5-6 parts of ammonium polyphosphate, 1-3 parts of a titanate coupling agent, 5-6 parts of pentaerythritol, 6-7 parts of porous starch, 2-3 parts of zinc borate, 3-5 parts of palm fiber and 10-12 parts of chlorohydrin rubber viscosity resin. The high-wear-resistant and high-oil-resistant fireproof coating is good in fireproof and heat insulation performance, good in oil resistance, wear resistance, freezing resistance and fireproofness, high in adhesion and less prone to falling off.

Description

technical field [0001] The invention relates to the technical field of fire-fighting materials, in particular to a high wear-resistant and oil-resistant fireproof coating and a preparation method thereof. Background technique [0002] At present, fire retardant coatings are more and more widely used in petrochemical, electric power, industrial and civil construction, machinery and other industries. Fireproof coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. However, the existing fireproof coatings have the problems of difficult balance of coating film surface adhesion, wear resistance, oil resistance, frost resistance and flame retardancy. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, to provide a high wear-r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D1/08C09D5/18C09D5/14C09D7/12
CPCC09D1/08C09D5/14C09D5/18C09D7/61C09D7/62C09D7/65
Inventor 何益庆
Owner TONGLING XIANGYUN FIRE FIGHTING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap