Preparation method of high-sensitivity stretchable biosensor for in-situ detection

An in-situ detection and sensitive technology, applied in applications, instruments, household appliances, etc., can solve the problems of low sensitivity, difficult stretching, and insufficient stretching stability of biosensors, and achieve simple and controllable methods, low defect peaks, High effect of chemisorption and physical enhancement mechanisms

Active Publication Date: 2017-03-15
SHANDONG NORMAL UNIV
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the shortcomings of current biosensors such as low sensitivity, difficult stretching, and insufficient stretching stability, the present invention proposes a preparation method for a highly sensitive stretchable biosensor that can be used for in-situ detection; Materials with extensibility (stretch length greater than 300%) - stretchable molybdenum disulfide structure - preparation method and combining it with silver nanoparticles to enhance sensitivity and prepare stretchable hybrid structures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-sensitivity stretchable biosensor for in-situ detection
  • Preparation method of high-sensitivity stretchable biosensor for in-situ detection
  • Preparation method of high-sensitivity stretchable biosensor for in-situ detection

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Three-dimensional molybdenum disulfide is obtained by growing molybdenum disulfide on nickel foam on a three-dimensional three-dimensional substrate, and finally a mixed structure of molybdenum disulfide / silver nanoparticles is obtained, such as figure 1 The preparation roadmap includes the following preparation steps:

[0056] 1. Add 0.25g (NH 4 ) 2 MoS 4 Add to 20ml of dimethylformamide (DMF) to form a concentration of 1.25wt% and sonicate for 20min.

[0057] 2. Take the nickel foam with a size of 8cm×8cm and wash it in acetone.

[0058] 3. Dry at 80°C for 10 minutes.

[0059] 4. Dip the dried nickel foam in (NH 4 ) 2 MoS 4 Formed in solution (NH 4 ) 2 MoS 4 film.

[0060] 5. Dry at 120°C for 30 minutes.

[0061] 6. Place in a tube furnace.

[0062] 7. Turn on the vacuum pump to pump the air pressure of the tube furnace to the ultimate vacuum state of 3×10 -6 Torr;

[0063] 8. Keep vacuum 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 m...

Embodiment 2

[0089] The three-dimensional molybdenum disulfide is obtained by growing molybdenum disulfide on the copper foam of the three-dimensional substrate, and finally the mixed structure of molybdenum disulfide / silver nanoparticles is obtained, including the following preparation steps:

[0090] 1. Add 0.25g (NH 4 ) 2 MoS 4 Add to 20ml of dimethylformamide (DMF) to form a concentration of 1.25wt% and sonicate for 20min.

[0091] 2. Take the copper foam with a size of 7cm×8cm and place it in acetone for cleaning.

[0092]3. Dry at 80°C for 10 minutes.

[0093] 4. Dip the dried copper foam in (NH 4 ) 2 MoS 4 Formed in solution (NH 4 ) 2 MoS 4 film.

[0094] 5. Dry at 120°C for 30 minutes.

[0095] 6. Place in a tube furnace.

[0096] 7. Turn on the vacuum pump to pump the air pressure of the tube furnace to the ultimate vacuum state of 3×10 -6 Torr;

[0097] 8. Keep vacuum 3×10 -6 After Torr for 15 minutes (the effect of vacuum for 15 minutes is to remove impurities, ai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a high-sensitivity stretchable biosensor for in-situ detection. The preparation method includes: adopting a chemical vapor deposition method to grow molybdenum disulfide on a three-dimensional substrate; soaking prepared molybdenum disulfide / foamed metal in an etching solution, removing a metal substrate by controlling concentration and temperature of the etching solution to obtain a stretchable molybdenum disulfide / metal particle mixed structure, fishing out the mixed structure, cleaning, using a pre-stretched 3M stretchable adhesive tape to cover the surface of the stretchable molybdenum disulfide / metal particle mixed structure to fish the mixed structure out, naturally airing, restoring to original length or area, soaking the mixed structure in a mixed solution of stannous chloride, silver nitrate, ascorbic acid and silver nitrate to enable the same to grow silver particles so as to prepare the high-sensitivity stretchable biosensor. The biosensor is excellent in performance, high in stability and sensitivity, low in cost, controllable and supportive of large-scale production and has great application value.

Description

technical field [0001] The invention belongs to the field of stretchable material preparation, in particular to a preparation method of a highly sensitive stretchable biosensor for in-situ detection. Background technique [0002] For today's biosensors, high sensitivity, high stability, and high efficiency are crucial. The highly sensitive in situ SERS technology can detect environmental and agricultural product pollution and the canceration caused by it in real time and quickly, which plays an important role in pollution control and medical diagnosis and treatment. At present, the progress of related research is relatively slow, mainly because it is difficult to prepare highly sensitive stretchable materials. [0003] The three-dimensional molybdenum disulfide material prepared on the three-dimensional substrate has excellent chemical properties of two-dimensional molybdenum disulfide, and at the same time has a larger specific surface area and better flexibility, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N33/00B32B9/04B32B1/06C04B35/547C04B38/04C04B41/88B32B1/00
CPCG01N33/00C04B35/547C04B38/045C04B41/009C04B41/5116C04B41/88B32B3/08B32B9/04B32B2264/105C04B41/4535C04B41/455
Inventor 杨诚刘子函欧佳瑜李天明潘萧萧徐媛媛刘玫姜守振满宝元
Owner SHANDONG NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com