Low-friction-coefficient and solvent-free type polyurethane adhesive and preparation method thereof

A polyurethane adhesive and low friction coefficient technology, applied in the field of polyurethane adhesive preparation, can solve the problems of high friction coefficient of composite film, composite film cannot be pulled, and can not be opened, so as to achieve good coating performance, wide application range, and reduce crystallinity Effect

Inactive Publication Date: 2017-03-22
BEIJING COMENS NEW MATERIALS
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The friction coefficient of the composite film is high, and the friction force on the bag making machine is large, which will cause the composite film to be unable to pull, stre

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] The embodiment of the present invention also provides a method for preparing the above-mentioned low friction coefficient solvent-free polyurethane adhesive, which includes the following steps:

[0037] Prepare the modified polyester polyol of component A and the modified polyester polyol of component B according to the above-mentioned adhesive formula;

[0038] Preparation of component A: adding polyisocyanate, keeping the kettle temperature at 25-35°C, adding the modified polyester polyol prepared, reacting at 70-80°C for 3 to 4 hours, and reducing to room temperature to obtain component A;

[0039] The prepared component A and component B are used according to the molar ratio of functional groups: -NCO: -OH=(1.1-1.8):1 to form the solvent-free polyurethane adhesive.

[0040] Two surfaces in contact with each other, when at rest, the contact between the two surfaces will form a strong bonding force, which is the static friction force. Unless the bonding force is destroyed, one...

Example Embodiment

[0043] Example one

[0044] This embodiment provides a solvent-free two-component polyurethane adhesive, which is composed of components A and B, wherein component A is formed by the reaction of modified polyester polyol and polyisocyanate, which is a modified Isocyanate adduct; component B is polyester polyol, which is a modified polyol;

[0045] The A component and the B component can be combined to form the adhesive according to the molar ratio of functional groups: -NCO: -OH=1.54:1.0.

[0046] The preparation method of the adhesive includes the following steps:

[0047] 1. Preparation of component A:

[0048] (1) Prepare polyester polyol first, including:

[0049] (1) Raw materials: 0.5mol 2-methyl-2,4-pentanediol, 0.8mol 1,6-hexanediol, 0.8mol adipic acid, 0.2mol sebacic acid;

[0050] (2) Preparation steps:

[0051] Add all the small molecular polyols (ie 0.5mol 2-methyl-2,4-pentanediol, 0.8mol 1,6-hexanediol) into the polyester reactor and mix well to form a small molecular polyol ...

Example Embodiment

[0062] Example two

[0063] The embodiment of the present invention provides a solvent-free two-component polyurethane adhesive, which is composed of components A and B, wherein component A is formed by the reaction of polyester polyol and polyisocyanate, which is a modified isocyanate The adduct; B component is polyester polyol, which is a modified polyol;

[0064] The A component and the B component can be combined to form the adhesive according to the molar ratio of functional groups: -NCO: -OH=1.75:1.0.

[0065] The preparation method of the adhesive includes the following steps:

[0066] 1. Preparation of component A:

[0067] (1) Preparation of polyester polyols, including:

[0068] (1) Material preparation: 0.8mol diethylene glycol, 0.2mol ethylene glycol, 0.5mol 1,2-propanediol, 1.0mol adipic acid;

[0069] (2) Preparation steps: refer to the steps of preparing polyester polyol in the preparation of component A in Example 1;

[0070] Prepared polyester polyol with a hydroxyl value...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses low-friction-coefficient and solvent-free type polyurethane adhesive and a preparation method thereof and belongs to the field of polyurethane adhesive preparation. The adhesive is prepared from A component and B component, wherein the A component is prepared from modified polyester polyol and polyisocyanate which react with each other, and the B component is prepared from modified polyester polyol. By means of molecular design, the appropriate proportion of branched chain is introduced into the adhesive; thus, the regularity of the adhesive is reduced, a solidified adhesive layer of the adhesive has certain microcosmic unevenness, the microcosmic unevenness of a composite membrane is further obtained, the bonding force between surfaces is reduced, and the composite membrane has a low friction coefficient; as the branched chain is introduced into the adhesive, the crystalline of the molecular chain is reduced, the transparency of the adhesive is improved, the adhesive also can obtain lower viscosity and good coating performance, and the adhesive is wider in application range in the field of composite flexible package. The solvent-free adhesive has no solvent residue and is high in safety.

Description

technical field [0001] The invention relates to the field of polyurethane adhesive preparation, in particular to a low friction coefficient solvent-free polyurethane adhesive for composite flexible packaging in the fields of food, daily necessities, medicines and the like and a preparation method thereof. Background technique [0002] Solvent-free polyurethane adhesives for composite flexible packaging have outstanding environmental protection and safety, and at the same time have outstanding advantages such as low cost, low energy consumption, stable composite film quality, and high composite efficiency. It is used in all kinds of composite flexible packaging for food, daily necessities, medicines, agricultural products, industrial products, cosmetics, electronic products, etc. [0003] Solvent-free composite adhesives have been widely used. However, during the application of solvent-free adhesives, the problem of high friction coefficient of flexible packaging composite fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/06C08G18/42C08G18/10
Inventor 田立云赫长生
Owner BEIJING COMENS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap