Flambe furry tiger skin fancy glaze, ceramic product and preparation method thereof

A technology of ceramic products and silk wool, which is applied in the field of ceramics, can solve the problems of difficult upgrading of products, many glaze defects, poor gloss, etc., to solve the contradiction between glaze color rendering effect and texture, and the surface of the bottle body is smooth and flat without defects , Solve the effect of reducing glaze defects

Inactive Publication Date: 2017-04-19
江苏省宜兴彩陶工艺厂
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The preparation of traditional flower glaze glazes for ceramic products requires multiple glazes. The production process is cumbersome and there are many defects on the glaze surface, such as pinholes, glaze shrinkage, etc., and the color is relatively light, the gloss is poor, and the color is monotonous. It is difficult to upgrade and upgrade, and cannot meet the cultural needs of multi-level and multi-field consumer groups for ceramic wine bottles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) To prepare kiln-transformed tiger skin glaze for ceramic wine bottles, the ratio is as follows:

[0034] 19 parts of feldspar, 5.4 parts of quartz, 3 parts of Suzhou soil, 7 parts of titanium oxide, 13 parts of calcite, 9.6 parts of glass powder, 29 parts of boron frit, 1.7 parts of strontium carbonate, 1 part of nickel oxide, 3.4 parts of chromium titanium antimony yellow , 2.7 parts of cerium praseodymium yellow, 1.6 parts of tin oxide, and 1 part of neodymium oxide.

[0035] (2) According to the ratio of the above ingredients: ball: water = 1: 1.29: 1.32, ball mill for 46 hours, and pass through a 120-mesh sieve after ball milling to obtain the kiln-changed silky tiger skin glaze.

[0036] (3) Then bisque-fire the wine bottle body, the bisque firing temperature is 1040°C, the blank formula is 52.7 parts of kaolin, 6.8 parts of quartz, 15.7 parts of Changxing white clay, 12.4 parts of Fujian porcelain clay, 10.6 parts of feldspar, and 1.8 parts of talc . Through...

Embodiment 2

[0041] (1) To prepare kiln-transformed tiger skin glaze for ceramic wine bottles, the ratio is as follows:

[0042]20.7 parts of feldspar, 4 parts of quartz, 4.5 parts of Suzhou soil, 5 parts of titanium oxide, 14.3 parts of calcite, 8 parts of glass powder, 27.4 parts of boron frit, 1 part of strontium carbonate, 0.5 parts of nickel oxide, 2 parts of chromium titanium antimony yellow , 2 parts of cerium praseodymium yellow, 2 parts of tin oxide, 2 parts of neodymium oxide.

[0043] (2) According to the above ingredients: ball: water = 1: 1.25: 1.35, the ball milling time is 41 hours, after ball milling, pass through a 120 mesh sieve to get the kiln-changing silky tiger skin glaze

[0044] (3) Then bisque-fire the wine bottle body, the bisque firing temperature is 1040°C, the blank formula is 52.7 parts of kaolin, 6.8 parts of quartz, 15.7 parts of Changxing white clay, 12.4 parts of Fujian porcelain clay, 10.6 parts of feldspar, and 1.8 parts of talc .

[0045] (4) Apply ki...

Embodiment 3

[0049] (1) To prepare kiln-transformed tiger skin glaze for ceramic wine bottles, the ratio is as follows:

[0050] 22 parts of feldspar, 6 parts of quartz, 5 parts of Suzhou soil, 6.5 parts of titanium oxide, 15 parts of calcite, 10 parts of glass powder, 26 parts of boron frit, 2 parts of strontium carbonate, 0.8 parts of nickel oxide, 4 parts of chromium titanium antimony yellow , 3 parts of cerium praseodymium yellow, 1 part of tin oxide, and 1.4 parts of neodymium oxide.

[0051] (2) According to the above ingredients: ball: water = 1: 1.35: 1.25, the ball milling time is 50 hours, and after ball milling, pass through a 120 mesh sieve to get the kiln-changing silky tiger skin glaze

[0052] (3) Then bisque-fire the wine bottle body, the bisque firing temperature is 1040°C, the blank formula is 52.7 parts of kaolin, 6.8 parts of quartz, 15.7 parts of Changxing white clay, 12.4 parts of Fujian porcelain clay, 10.6 parts of feldspar, and 1.8 parts of talc .

[0053] (4) Ap...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramics and particularly relates to a flambe furry tiger skin fancy glaze, a ceramic product and a preparation method thereof. The flambe furry tiger skin fancy glaze includes the following raw materials: feldspar, quartz, Suzhou earth, titanium oxide, glass powder, calcite, boron frit, strontium carbonate, nickel oxide, chromium titanium antimony yellow, cerium praseodymium yellow, tin oxide, and neodymium oxide. A biscuited ceramic green body is applied by the flambe furry tiger skin fancy glaze in a soak-glazing manner, and when the glaze is dried, the ceramic green body is subjected to glaze firing. The prepared glaze slurry has good process performances and allows glaze application in a one-time soak-glazing manner. The fired glaze surface has good quality. A fired bottle has a smooth and flat surface and has no defects.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to kiln-transformed silk-haired tiger skin glaze, ceramic products and a preparation method thereof. Background technique [0002] The preparation of traditional flower glaze glazes for ceramic products requires multiple glazes. The production process is cumbersome and there are many defects on the glaze surface, such as pinholes, glaze shrinkage, etc., and the color is relatively light, the gloss is poor, and the color is monotonous. It is difficult to upgrade and cannot meet the cultural needs of multi-level and multi-field consumer groups for ceramic wine bottles. With the further changes of social development and the improvement of people's living standards and aesthetics, there are higher requirements for the appearance and decoration of ceramic wine bottles, and higher requirements for taste and cultural connotation. In order to meet market demand and improve product grades, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C04B33/13C04B41/86C04B33/34C03C1/06
CPCC03C8/20C03C1/06C04B33/13C04B33/34C04B41/009C04B41/5023C04B41/86C04B2235/3418C04B2235/3463C04B41/4535
Inventor 周玉萍巫俠
Owner 江苏省宜兴彩陶工艺厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com