Strong-acid-resisting high-strength hanging beam and preparation method thereof

A strong acid-resistant, high-strength technology, used in coatings, anti-corrosion coatings, fire-resistant coatings, etc., can solve problems such as damage, easy accidents, corrosion, etc., and achieve the effect of reducing production costs, excellent mechanical properties, and simplifying the preparation method.

Inactive Publication Date: 2017-04-26
苏州富艾姆工业设备有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The hanging beam is an extremely important part of industrial equipment. With the continuous development of the economy, people's requirements for the hanging beam are also increasing. There are still many defects in the hanging beam in the prior art. The hanging beam has been exposed to the sun for a long time outdoors and Wind and rain are easy to cause corrosion, resulting in a great damage rate and easy to cause accidents. In order to improve work efficiency and reduce the accident rate, the invention proposes a strong acid-resistant high-strength suspension beam and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] This embodiment provides a strong-acid-resistant high-strength hanging beam, including the hanging beam. The outer surface of the hanging beam is coated with a layer of strong-acid-resistant paint. The strong-acid-resistant paint is composed of two components A and B in a ratio of A:B=4:3. into, A and B comprise the following components in parts by mass:

[0024] Component A includes the following components in parts by mass: epoxy resin: 11 parts, polyurethane: titanium dioxide: 19 parts, graphite fluoride: 12 parts, barium sulfate: 19 parts, thixotropic additives: 21 parts, ring Oxygen diacrylate: 13 parts, polydimethylsiloxane: 8 parts, active amine: 4 parts, pH regulator: 13 parts, silane coupling agent: 9 parts, excipients: 16 parts;

[0025] Component B includes the following components in parts by mass: tributylphenol polyoxyethylene ether: 13 parts, fine-grained alumina: 12 parts, carboxymethyl cellulose: 9 parts, barium sulfate: 13 parts, six Methylcyclotrisil...

Embodiment 2

[0033] This embodiment provides a strong-acid-resistant high-strength hanging beam, including the hanging beam. The outer surface of the hanging beam is coated with a layer of strong-acid-resistant paint. The strong-acid-resistant paint is composed of two components A and B in a ratio of A:B=4:3. into, A and B comprise the following components in parts by mass:

[0034] Component A includes the following components in parts by mass: epoxy resin: 14 parts, polyurethane: titanium dioxide: 23 parts, graphite fluoride: 17 parts, barium sulfate: 24 parts, thixotropic additives: 24 parts, ring Oxygen diacrylate: 19 parts, polydimethylsiloxane: 13 parts, active amine: 9 parts, pH regulator: 17 parts, silane coupling agent: 14 parts, excipients: 22 parts;

[0035] Component B includes the following components in parts by mass: tributylphenol polyoxyethylene ether: 18 parts, fine-grained alumina: 18 parts, carboxymethyl cellulose: 14 parts, barium sulfate: 19 parts, six Methylcyclotri...

Embodiment 3

[0043] This embodiment provides a strong-acid-resistant high-strength hanging beam, including the hanging beam. The outer surface of the hanging beam is coated with a layer of strong-acid-resistant paint. The strong-acid-resistant paint is composed of two components A and B in a ratio of A:B=4:3. into, A and B comprise the following components in parts by mass:

[0044] Component A includes the following components in parts by mass: epoxy resin: 13 parts, polyurethane: titanium dioxide: 20 parts, graphite fluoride: 15 parts, barium sulfate: 22 parts, thixotropic additives: 23 parts, ring Oxygen diacrylate: 15 parts, polydimethylsiloxane: 10 parts, active amine: 5 parts, pH regulator: 14 parts, silane coupling agent: 12 parts, excipients: 19 parts;

[0045] Component B includes the following components in parts by mass: tributylphenol polyoxyethylene ether: 15 parts, fine-grained alumina: 16 parts, carboxymethyl cellulose: 11 parts, barium sulfate: 16 parts, six Methylcyclotri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a strong-acid-resisting high-strength hanging beam. A component A and a component B contain the following components in parts by weight: the component A comprises the following components in parts by weight: 11-14 parts of epoxy resin, 19-23 parts of polyurethane: titanium dioxide, 12-17 parts of graphite fluoride, 19-24 parts of barium sulfate, 21-24 parts of a thixotropic agent, 13-19 parts of epoxy diacrylate, 8-13 parts of polydimethylsiloxane, 4-9 parts of active amine, 13-17 parts of a pH (Potential of Hydrogen) regulator, 9-14 parts of a silane coupling agent and 16-22 parts of an auxiliary material; the component B comprises the following components in parts by weight: 13-18 parts of tributylphenol polyoxyethylene ether, 12-18 parts of fine-grained aluminum oxide, 9-14 parts of carboxymethyl cellulose, 13-19 parts of barium sulfate, 2-7 parts of hexamethyl cyclotrisiloxane, 3-11 parts of light calcium carbonate, 25-31 parts of de-ionized water, 13-18 parts of a de-foaming agent, 4-9 parts of a coupling agent and 2-9 parts of a flame retardant.

Description

technical field [0001] The invention relates to the technical field of industrial accessories, in particular to an acid-resistant high-strength suspension beam and a preparation method thereof. Background technique [0002] The hanging beam is an extremely important part of industrial equipment. With the continuous development of the economy, people's requirements for the hanging beam are also increasing. There are still many defects in the hanging beam in the prior art. The hanging beam has been exposed to the sun for a long time outdoors and Wind and rain easily lead to corrosion, resulting in a great damage rate and accidents. In order to improve work efficiency and reduce the accident rate, the invention proposes a strong acid-resistant high-strength suspension beam and a preparation method thereof. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a strong acid-resistant high-strength hanging beam, which inclu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D163/10C09D163/00C09D183/04C09D5/10C09D7/12
CPCC09D175/04C08K2201/014C08L2201/08C08L2205/02C08L2205/025C08L2205/035C09D5/10C09D5/18C09D7/61C09D7/62C09D7/63C09D7/65C09D7/70C09D163/10
Inventor 翁华明
Owner 苏州富艾姆工业设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com