Low-temperature-resistant and anti-cracking waterborne coating

A water-based coating, anti-cracking technology, used in anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of low temperature resistance and crack resistance, etc., to increase mechanical properties and decorative properties, The effect of increasing mechanical properties and increasing low temperature resistance

Active Publication Date: 2017-04-26
滁州市瑞景园林股份有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the complicated repair process and long construction period, it is best to complete the repair work at one time. In the low temperature environment in winter, in order to avoid multiple repairs in the later period, it is best to use water-based

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] A low-temperature resistant and anti-cracking water-based paint. Its raw materials by weight include: 90 parts of modified polyurethane emulsion, 30 parts of acrylic emulsion, 23 parts of pigments, 17 parts of fillers, 5 parts of propylene glycol methyl ether acetate, and dodecyl sulfonic acid 4 parts of sodium, 0.5 part of leveling agent, 0.05 part of polydimethylsiloxane, 0.06 part of emulsified silicone oil, 0.5 part of wetting agent, 0.7 part of sodium carboxymethyl cellulose, γ-methacryloxypropyl 1.4 parts of trimethoxysilane and 19 parts of water.

Example Embodiment

[0019] Example 2

[0020] A low-temperature resistant and anti-cracking water-based paint. Its raw materials in parts by weight include: 80 parts of modified polyurethane emulsion, 40 parts of acrylic emulsion, 20 parts of pigments, 20 parts of fillers, 4 parts of propylene glycol methyl ether acetate, and dodecyl sulfonic acid 5 parts of sodium, 0.4 parts of leveling agent, 0.06 parts of polydimethylsiloxane, 0.05 parts of emulsified silicone oil, 0.6 parts of wetting agent, 0.6 parts of sodium carboxymethyl cellulose, γ-methacryloxypropyl 1.6 parts of trimethoxysilane, 18 parts of water;

[0021] Among them, in the preparation process of the modified polyurethane emulsion, in a nitrogen atmosphere, N-methylpyrrolidone, 2,4-toluene diisocyanate, dimethylolpropionic acid, hydroxy-terminated polybutadiene, dilauric acid two Mix the butyl tin, heat up, keep stirring, add modified montmorillonite, continue to keep stirring, add 1,4-butanediol, continue to keep stirring, then add hydr...

Example Embodiment

[0022] Example 3

[0023] A low-temperature resistant and anti-cracking water-based paint. Its raw materials in parts by weight include: 100 parts of modified polyurethane emulsion, 20 parts of acrylic emulsion, 25 parts of pigments, 15 parts of fillers, 6 parts of propylene glycol methyl ether acetate, and dodecyl sulfonic acid 3 parts of sodium, 0.6 parts of leveling agent, 0.04 parts of polydimethylsiloxane, 0.07 parts of emulsified silicone oil, 0.4 parts of wetting agent, 0.8 parts of sodium carboxymethyl cellulose, γ-methacryloxypropyl 1.2 parts of trimethoxysilane, 20 parts of water;

[0024] Among them, the filler is composed of 800 mesh pottery clay and 800 mesh diatomite, wherein the weight ratio of pottery clay to diatomite is 3:2;

[0025] In the preparation process of the modified polyurethane emulsion, N-methylpyrrolidone, 2,4-toluene diisocyanate, dimethylolpropionic acid, hydroxy-terminated polybutadiene, and dibutyltin dilaurate were mixed in a nitrogen atmosphere. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature-resistant and anti-cracking waterborne coating. The coating is prepared from raw materials in parts by weight as follows: 80-100 parts of a modified polyurethane emulsion, 20-40 parts of an acrylic emulsion, 20-25 parts of pigments, 15-20 parts of filler, 4-6 parts of propylene glycol methyl ether acetate, 3-5 parts of sodium dodecyl sulfonate, 0.4-0.6 parts of a leveling agent, 0.04-0.06 parts of polydimethylsiloxane, 0.05-0.07 parts of emulsified silicone oil, 0.4-0.6 parts of a wetting agent, 0.6-0.8 parts of sodium carboxymethyl cellulose, 1.2-1.6 parts of gamma-methacryloxy propyl trimethoxyl silane and 18-20 parts of water. The waterborne coating has good low temperature resistance, high low-temperature toughness and good anti-cracking performance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a low-temperature-resistant and crack-resistant water-based coating. Background technique [0002] Ancient buildings have extremely high historical, scientific and artistic value. If they are destroyed, they cannot exist anymore; and ancient buildings are old and will inevitably be damaged by nature or man-made. Therefore, we need to repair and maintain ancient buildings . Coatings are often used in the process of repairing ancient building rooms, door walls, inner and outer eaves, palms, floors, and walls. Due to the complicated repair process and long construction period, it is best to complete the repair work at one time. In the low temperature environment in winter, in order to avoid multiple repairs in the later period, it is best to use water-based paint with good low temperature resistance and crack resistance. The low temperature resistance and crack resistance of wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/16C09D133/00C09D5/08C09D7/12C08G18/69C08G18/67C08G18/65C08G18/34C08G18/32
CPCC08G18/672C08G18/69C08K2201/011C08K2201/014C08L2205/025C08L2205/035C09D5/08C09D7/61C09D7/62C09D7/63C09D7/65C09D7/70C09D175/16C08L33/00C08L83/04C08L1/286C08K13/06C08K9/06C08K7/06C08K3/346C08K3/34C08K5/42C08G18/0823C08G18/6588
Inventor 樊世新
Owner 滁州市瑞景园林股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka