A kind of acrylate glue used for bonding the reinforcing ribs of the roof panel of the motor vehicle

A technology of acrylate glue and methyl methacrylate, which is applied in the direction of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., can solve the problems of adhesive detachment, danger, etc., to avoid explosion, High shear strength, odor reduction effect

Active Publication Date: 2019-10-11
HUBEI HUITIAN NEW MATERIALS STOCK CO LTD +3
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing glue is usually used in a relatively fixed environment. When it is in a state of high-frequency vibration, the glue is prone to detachment, which is more dangerous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] 305g of dibutyl phthalate, 10g of bisphenol A type epoxy resin, 151g of high rubber powder, 103g of benzoyl peroxide and 11.5g of castor oil were mixed uniformly to obtain an oxidizing agent.

[0040] Mix 206.5g methyl methacrylate, 103.1g impact modifier, 101.5g chlorosulfonated polyethylene, 10g triethylenediamine, 5.1g paraffin, 10.8g acrylic acid, 3.2g stabilizer and 12g organomodified bentonite Evenly, the reducing agent is obtained.

[0041] In parts by volume, 1 part of oxidizing agent and 8 parts of reducing agent are uniformly mixed to obtain acrylate glue.

[0042]In this example, the impact modifier is a mixture of ABS, ACR and MBS with a mass ratio of 1:1:1, the paraffin wax has a melting point of 47°C, and the stabilizer is hydroquinone, naphthoquinone, or benzoquinone. Mixture, its mass ratio is 1:2:3.

[0043] Using aluminum alloy as a test piece, the tensile shear strength and peel strength of the prepared acrylic adhesive were tested. At the same time...

Embodiment 2

[0046] 405g of dibutyl phthalate, 27g of bisphenol A type epoxy resin, 25g of high rubber powder, 170g of benzoyl peroxide and 23g of castor oil were mixed evenly to obtain an oxidizing agent.

[0047] 250g methyl methacrylate, 120g impact modifier, 135g chlorosulfonated polyethylene, 17g triethylenediamine, 6g paraffin, 23.5g acrylic acid, 4.2g stabilizer and 14.5g organically modified bentonite were mixed uniformly to obtain reducing agent.

[0048] In parts by volume, 1 part of oxidizing agent and 15 parts of reducing agent are uniformly mixed to obtain acrylate glue.

[0049] In this embodiment, ABS and MBS with a mass ratio of 1:2 are selected as the impact modifier, paraffin with a melting point of 50° C. is selected as the paraffin, and Na salt is used as the stabilizer.

[0050] Using aluminum alloy as a test piece, the tensile shear strength and peel strength of the prepared acrylic adhesive were tested. At the same time, the acrylic adhesive was placed at room tempe...

Embodiment 3

[0053] Mix 50g of dibutyl phthalate, 5g of bisphenol A type epoxy resin, 20g of high rubber powder, 20g of benzoyl peroxide and 5g of castor oil to obtain an oxidizing agent.

[0054] Mix 54g methyl methacrylate, 20g impact modifier, 15g chlorosulfonated polyethylene, 3g triethylenediamine, 1g paraffin, 5g acrylic acid, 0.6g stabilizer and 1.5g organically modified bentonite to obtain a reduced agent.

[0055] In parts by volume, 1 part of oxidizing agent and 10 parts of reducing agent are uniformly mixed to obtain acrylate glue.

[0056] In this embodiment, ACR is selected as the impact modifier, paraffin wax with a melting point of 49°C is selected as the paraffin, and hydroquinone and Na salt with a mass ratio of 3:2 are selected as the stabilizer.

[0057] Using aluminum alloy as a test piece, the tensile shear strength and peel strength of the prepared acrylic adhesive were tested. At the same time, the acrylic adhesive was placed at room temperature, under the condition...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
shear strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an acrylic glue used for bonding the roof reinforcement rib of a motor vehicle, and relates to the field of acrylic structural glue. The acrylic glue includes 1 part of oxidizing agent and 7 to 15 parts of reducing agent in parts by volume; parts by mass, The oxidizing agent includes 30-50 parts of dibutyl phthalate, 1-5 parts of bisphenol A epoxy resin, 15-20 parts of high rubber powder, 10-20 parts of benzoyl peroxide and 1-5 parts of Castor oil; in parts by mass, the reducing agent includes 20 to 54 parts of methyl methacrylate, 10 to 20 parts of impact modifier, 10 to 15 parts of chlorosulfonated polyethylene, and 1 to 3 parts of triethylenediamine , 0.5-1 part of paraffin, 1-5 parts of acrylic acid, 0.3-1 part of stabilizer, 1.2-1.6 parts of organically modified bentonite. The acrylic glue of the present invention can be closely connected with the adhesive under high-frequency vibration state, and does not fall off after long-term use.

Description

technical field [0001] The invention relates to the field of acrylic structural adhesives, in particular to an acrylic adhesive used for bonding the reinforcing ribs of the roof plates of motor vehicles. Background technique [0002] When the high-speed EMU vehicles are running, their components are in a state of high-frequency vibration for a long time. In order to ensure safety, the fatigue resistance of the components becomes a key factor in quality inspection. The middle roof is the top assembly part of the high-speed EMU. Its use The area is very large, and it is necessary to use a large number of ribs to reinforce the middle roof to increase the fatigue resistance of the middle roof. In actual installation, the ribs are usually fixed to the middle roof with glue. [0003] However, the existing viscose is usually used in a relatively fixed environment. When it is in a state of high-frequency vibration, the viscose is prone to detachment, which is relatively dangerous. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/08C09J11/06C09J11/04
Inventor 刘苏宇韩胜利张浩军章锋吴正明
Owner HUBEI HUITIAN NEW MATERIALS STOCK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com