Microbial carrier basalt fiber material and preparation method thereof

A technology of basalt fiber and microbial carrier, which is applied to glass manufacturing equipment, manufacturing tools, etc. fixed on or in an inorganic carrier, can solve the problems of destroying chemical bonds on the surface of basalt fibers, small microbial load, and poor chemical bonding ability, etc. Achieve the effect of easy growth, reproduction and diffusion, large microbial load, and large bonding force

Inactive Publication Date: 2017-05-10
SICHUAN LIJIU INTPROP SERVICE CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the disadvantages of low microbial load and weak adhesion caused by the direct use of basalt fiber as a microbial water purification material carrier due to the high surface energy of basalt fiber and poor chemical bonding ability with microorganisms, and to provide a microbial carrier basalt Fiber material and preparation method thereof; the present invention uses high-energy rays and modifiers to treat the surface of basalt fibers, destroys the chemical bonds on the surface of basalt fibers, forms surface defects, increases active sites, and reduces surface energy, thereby making the surface of basalt fibers and microorganisms The bonding ability is enhanced to increase the load of microorganisms, thereby improving the purification efficiency of microbial load purification materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Crushing the basalt ore to obtain basalt ore powder with a particle size of 0.5mm;

[0030] (2) Heat the powder obtained in step 1 and melt it at a temperature of 1250°C to form a spinning melt;

[0031] (3) Drawing the spinning melt obtained in step 2 at a speed of 2000m / min to obtain basalt fiber precursors with a diameter of 5 μm;

[0032] (4) Surface-treat the basalt fiber precursors obtained in step 3 with ultraviolet rays in an ethanol solution at a temperature of 60°C, and control the UV equivalent dose received by the basalt fiber precursors at 0.1Sv;

[0033] (5) Resolving and twisting the ultraviolet-treated raw silk obtained in step 4 to obtain a microbial carrier basalt fiber material.

Embodiment 2

[0035] (1) Crushing the basalt ore to obtain basalt ore powder with a particle size of 1.0mm;

[0036] (2) Heat the powder obtained in step 1, and melt it at a temperature of 1350°C to form a spinning melt;

[0037] (3) Drawing the spinning melt obtained in step 2 at a speed of 2500m / min to obtain a basalt fiber precursor with a diameter of 10 μm;

[0038] (4) Surface-treat the basalt fiber precursors obtained in step 3 with X-rays in an acetic acid solution at a temperature of 100°C, and control the X-ray equivalent dose received by the basalt fiber precursors at 10 Sv;

[0039] (5) Decomposing and twisting the X-ray-treated precursor obtained in step 4 to obtain the microbial carrier basalt fiber material.

Embodiment 3

[0041] (1) Crushing the basalt ore to obtain basalt ore powder with a particle size of 0.1mm;

[0042] (2) Heat the powder obtained in step 1 and melt it at a temperature of 1100°C to form a spinning melt;

[0043](3) Drawing the spinning melt obtained in step 2 at a speed of 3000m / min to obtain basalt fiber precursors with a diameter of 1 μm;

[0044] (4) Surface-treat the basalt fiber precursors obtained in step 3 with ultraviolet rays in a tartaric acid solution at a temperature of 80°C, and control the UV equivalent dose received by the basalt fiber precursors at 0.01Sv;

[0045] (5) Resolving and twisting the ultraviolet-treated raw silk obtained in step 4 to obtain a microbial carrier basalt fiber material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a microbial carrier basalt fiber material and a preparation method thereof. According to the microbial carrier basalt fiber material and the preparation method disclosed by the invention, the surfaces of basalt fibers are treated by using high-energy rays and a modifier, chemical bonds on the surfaces of the basalt fibers are damaged to form surface defects, active sites are increased, and surface energy is reduced, so that the bonding ability between the surfaces of the basalt fibers and microorganisms is enhanced, the loading capacity of the microorganisms is increased, and further the purification efficiency of a microbial supported purification material is improved.

Description

technical field [0001] The invention relates to the field of microbial fiber carrier materials, in particular to a microbial carrier basalt fiber material and a preparation method thereof. Background technique [0002] Basalt fiber is a new type of inorganic environmentally friendly green high-performance fiber material, and it is one of the four high-performance fibers that will be developed in my country in the future. The basalt rock material composed of basalt is melted at high temperature and then prepared by spinning process. Basalt continuous fiber not only has good stability, but also has various excellent properties such as electrical insulation, corrosion resistance, combustion resistance, and high temperature resistance. Moreover, the production process of basalt fiber produces less waste and less environmental pollution. It can be directly transferred to the ecological environment without any harm, so it is a veritable green and environmental protection material....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B37/00C03C13/06C03C25/62C12N11/14
CPCY02P40/57C03B37/00C03C13/06C03C25/6226C03C25/624C03C25/6266C12N11/14
Inventor 不公告发明人
Owner SICHUAN LIJIU INTPROP SERVICE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com