Warm mix polymer modified asphalt mixture and preparation method thereof

A technology for modifying asphalt and polymers, applied in the direction of climate change adaptation, etc., can solve the problems of poor thermal stability and anti-aging performance of asphalt, environmental pollution, etc., and achieve improved anti-aging performance, shortened reaction time, and stable performance Effect

Active Publication Date: 2017-05-10
CHINA PETROLEUM & CHEM CORP +1
View PDF15 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] In order to solve the problem that the processing and use temperature of polymer modified asphalt mixture is high in the prior art, which may easily cause environmental pollution or the heat stability and anti-aging performance of the asphalt are not good even though the use temperature can be reduced after adding warm mix agent , the present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Warm mix polymer modified asphalt mixture and preparation method thereof
  • Warm mix polymer modified asphalt mixture and preparation method thereof
  • Warm mix polymer modified asphalt mixture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0062] Example 1

[0063] (1) Preparation of warm mixing agent

[0064] Using Ni metal as a catalyst, the CO obtained after coal gasification is combined with H 2 The synthesis reaction is carried out to obtain mixed alkanes with 90% carbon number of alkanes.

[0065] ① Weigh 1000g of the above mixed alkanes, about 1.2mol, put it in a closed container, heat to 480℃, add 3g of catalyst anhydrous CuCl 2 , Keep this temperature and introduce 0.89 mol of chlorine, and blow in nitrogen to keep the pressure of the reaction vessel at 3MPa, and react for 30min to obtain the intermediate;

[0066] ②Weigh 7000g of the minus four-line extraction oil with 70% aromatic content, and add 441g of complex [Cu(NH 3 ) 4 ]SO 4 And 44.1g of catalyst Cu, packed in another airtight container and heated to 350°C, reacted at this temperature for 180min at a constant temperature to obtain the aromatic complex component;

[0067] ③Introduce the aromatic complex component into the above intermediate, keep the temp...

Example Embodiment

[0073] Example 2

[0074] (1) Preparation of warm mixing agent

[0075] Using Co metal as a catalyst, the CO obtained after coal gasification is combined with H 2 The synthesis reaction is carried out to obtain mixed alkanes with 90% carbon number of alkanes from 30 to 130.

[0076] ① Weigh 3500g of the above mixed alkanes, about 4.5mol, place them in a closed container, heat to 400℃, add 31.5g of catalyst anhydrous MnCl 2 , Keep this temperature and introduce 1.16mol of chlorine, and pass nitrogen into the reaction vessel to keep the pressure of the reaction vessel at 5MPa, and react for 60min to obtain the intermediate;

[0077] ②Weigh 1000g of FCC oil slurry with 63% aromatic content, and add 19g of complex K to it 4 [Fe(CN) 6 ] And 1.9g of catalyst Fe, placed in another airtight container and heated to 270°C, reacted at this temperature for 120 minutes at a constant temperature, to obtain aromatic complex components;

[0078] ③Introduce the aromatic complex component into the above ...

Example Embodiment

[0084] Example 3

[0085] (1) Preparation of warm mixing agent

[0086] Using Fe metal as a catalyst, the CO obtained after coal gasification, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which 90% of carbon number is 70-90 alkanes.

[0087] ① Weigh 1000g of the above mixed alkanes, about 0.8mol, put it in a closed container, heat it to 440℃, add 6g catalyst anhydrous NiCl 2 , At this temperature, 0.31 mol of fluorine is introduced, and nitrogen is introduced to keep the pressure of the reaction vessel at 4 MPa, and react for 45 minutes to obtain the intermediate;

[0088] ②Weigh 3500g of refined phenolic extracted oil with 78% aromatic content, and add 164g of complex [Ni(CO) 4 ] And 16.4g of catalyst Ni, packed in another airtight container and heated to 310°C, reacted at this temperature for 160min at a constant temperature to obtain the aromatic hydrocarbon complex component;

[0089] ③Introduce the aromatic complex component into the above intermediate, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a warm mix polymer modified asphalt mixture and a preparation method thereof, wherein the mixture comprises 4.0-6.0 parts of a warm mix polymer modified asphalt, 1.0-3.0 parts of ore powder, and 91.0-95.0 parts of an aggregate, the warm mix polymer modified asphalt comprises 1-7 parts of a warm mix agent, 2-5 parts of a polymer, 88-97 parts of matrix asphalt, and sulfur, and the sulfur accounts for 0.01-0.07% of the total mass of the warm mix agent, the polymer and the matrix asphalt. The warm mix agent preparation method comprises: under the effect of a catalyst, carrying out a reaction on a macromolecule alkane and a halogen to obtain an intermediate; obtaining an aromatic hydrocarbon complexing component from aromatic hydrocarbon oil and a complexing compound under the effect of a catalyst; and introducing the aromatic hydrocarbon complexing component into the intermediate, carrying out a reaction, and aging to obtain the warm mix agent. According to the present invention, by adding the warm mix agent to the asphalt in the mixture, the warm mix effect is provided for the asphalt, the high temperature performance and the low temperature performance of the asphalt are considered, the thermal stability of the asphalt is improved, the aging resistance is improved, the thermal aging of the asphalt is reduced, and the harmful gas generation is reduced.

Description

technical field [0001] The invention relates to a warm-mix polymer modified asphalt mixture and a preparation method thereof, belonging to the field of petroleum industry and basic material chemistry. Background technique [0002] The asphalt mixture used in road engineering in the past is generally divided into two types according to the mixing construction temperature: cold mix asphalt mixture CMA (Cold Mix Asphalt) and hot mix asphalt mixture HMA (Hot Mix Asphalt). Cold-mix asphalt mixture is generally mixed and paved with emulsified asphalt or liquid asphalt and aggregate at room temperature, without heating the aggregate and binder, which can save a lot of energy. However, the initial strength of cold-mix asphalt mixture is low, and it is difficult to meet the requirements of important projects such as expressways and heavy-duty traffic roads. Hot mix asphalt mixture is widely used and has good road performance. However, in the production process of hot mix asphalt mi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/26C04B24/00
CPCY02A30/30
Inventor 陈保莲范思远张静宁爱民李志军程国香
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka