Preparation method of thermal insulation material

A technology of thermal insulation material and slurry, applied in glass manufacturing equipment, manufacturing tools, glass molding and other directions, can solve problems such as river silting, dust generation, air pollution, etc., and achieve the effect of simple production process, cost saving and quality improvement.

Inactive Publication Date: 2017-05-24
SHIHEZI UNIVERSITY
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If a large amount of fly ash is not treated, it will generate dust and pollute the atmosphere; if it is discharged into the water system, it will cause river silting, and the toxic chemicals in it will also cause harm to humans and organisms

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0024] A method for preparing an insulating material, comprising:

[0025] (1) After the fly ash is ground by the cement test mill, it is standby after passing through a 200-mesh sieve;

[0026] (2) after the glass powder is passed through a 200-mesh sieve after being ground by a cement test mill, it is for subsequent use;

[0027] (3) by mass the fly ash obtained by 15 parts of step (1), the glass powder obtained by 85 parts of step (2), 2 parts of sodium carbonate, 4 parts of titanium dioxide powder, 2 parts of borax, 30 parts After the water is stirred evenly, a slurry is obtained;

[0028] (4) Put the slurry obtained in step (3) into the cement mortar test mold, then vibrate and compact it on the cement mortar shaker platform, then put it into an electric blast drying box and dry it to form a green body;

[0029] (5) Step (4) green body is put into high-temperature resistance furnace and fired, and the firing system is as follows:

[0030] In the preheating stage, the t...

specific Embodiment 2

[0037] A method for preparing an insulating material, comprising:

[0038] (1) After the fly ash is ground by the cement test mill, it is standby after passing through a 200-mesh sieve;

[0039] (2) after the glass powder is passed through a 200-mesh sieve after being ground by a cement test mill, it is for subsequent use;

[0040] (3) by mass the fly ash obtained by 5 parts of step (1), the glass powder obtained by 95 parts of step (2), 6 parts of sodium carbonate, 8 parts of titanium dioxide powder, 4 parts of borax, 35 parts After the water is stirred evenly, a slurry is obtained;

[0041] (4) Put the slurry obtained in step (3) into the cement mortar test mold, then vibrate and compact it on the cement mortar shaker platform, then put it into an electric blast drying box and dry it to form a green body;

[0042] (5) Step (4) green body is put into high-temperature resistance furnace and fired, and the firing system is as follows:

[0043] In the preheating stage, the te...

specific Embodiment 3

[0050] A method for preparing an insulating material, comprising:

[0051] (1) After the fly ash is ground by the cement test mill, it is standby after passing through a 200-mesh sieve;

[0052] (2) after the glass powder is passed through a 200-mesh sieve after being ground by a cement test mill, it is for subsequent use;

[0053] (3) by mass the fly ash obtained by 10 parts of step (1), the glass powder obtained by 90 parts of step (2), 4 parts of sodium carbonate, 3 parts of titanium dioxide powder, 3 parts of borax, 33 parts of After the water is stirred evenly, a slurry is obtained;

[0054] (4) Put the slurry obtained in step (3) into the cement mortar test mold, then vibrate and compact it on the cement mortar shaker platform, then put it into an electric blast drying box and dry it to form a green body;

[0055] (5) Step (4) green body is put into high-temperature resistance furnace and fired, and the firing system is as follows:

[0056] In the preheating stage, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a thermal insulation material. The preparation method comprises the following steps that 1, pulverized fuel ash is screened by a 200-mesh screen for usage after cement test grinding; 2, glass powder is screened by a 200-mesh screen for usage after cement test grinding; 3, 5-15 parts of pulverized fly ash, 85-95 parts of glass powder, 2-6 parts of sodium carbonate, 2-8 parts of titanium dioxide powder, 2-4 parts of borax and 30-35 parts of water are stirred evenly, and then slurry is obtained; 4, the slurry is put into a cement mortar test mold, then vibration and compaction are performed on a cement mortar jolt ramming table, then the cement mortar is put into an electrothermal blowing dry box, and drying is performed to form a blank; 5, the blank is put into a high-temperature resistance furnace, and sintering is performed to obtain the thermal insulation material.

Description

technical field [0001] The invention belongs to the field of inorganic material science and engineering, and in particular relates to a preparation method of a thermal insulation material. Background technique [0002] In recent years, fire accidents caused by building exterior wall insulation materials have occurred frequently, and the use of organic insulation materials has been greatly restricted. [0003] Fly ash is the fine ash collected from the flue gas after coal combustion. Fly ash is the main solid waste discharged from coal-fired power plants. The main oxides of fly ash in thermal power plants in my country are: silicon dioxide, aluminum oxide, ferrous oxide, ferric oxide, calcium oxide, titanium oxide, etc. With the development of the power industry, the discharge of fly ash from coal-fired power plants has increased year by year, becoming one of the largest industrial wastes in my country. If a large amount of fly ash is not treated, it will generate dust and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C11/00C03C6/00C03B19/08
CPCC03C11/007C03B19/08C03C1/002
Inventor 秦子鹏申鹏飞田艳李刚马玉薇
Owner SHIHEZI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap