Refractory bricks prepared from pebbles in Changjiang River, and preparation method of refractory bricks
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of refractory bricks and pebbles, which is applied in the field of Yangtze River pebble refractory bricks and its preparation, can solve the problems of low refractoriness, high cost, and low strength, and achieve the effects of good high temperature resistance, good thermal shock resistance, and high strength
Inactive Publication Date: 2017-05-24
MAANSHAN BAOLONG NEW BUILDING MATERIALS
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The invention provides a foamed thermal insulation refractory brick produced using coal gangue as the main raw material and its preparation method, although it solves the problems of low refractoriness, poor molding, low strength and high cost of lightweight refractory thermal insulation bricks in the domestic market , but with the rapid development of science and technology and the continuous improvement of the economic level, higher requirements are put forward for the comprehensive performance of refractory bricks, and a kind of refractory brick with better comprehensive performance is needed in the market
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0016] A Yangtze River pebble refractory brick, made of the following materials (kg): Yangtze River pebble 20, coal slime 32, boehmite 20, magnesite tailings 18, spinel 12, silica powder 17, and vanadium iron slag 21 , Andalusite 18, Furnace Ash 20, Bauxite 30, Phyllite 15, Sulfite Pulp 10, Yellow River Silt 12.
[0017] A method for preparing Yangtze River pebble refractory bricks consists of the following steps:
[0018] (1) Mix the Yangtze River pebbles, silica powder and andalusite evenly, crush them, pass through an 80-mesh sieve, add 40% sodium carbonate and 35% sodium nitrate equivalent to the mass of the mixed powder, dry ball milling at 1000r / min for 15min, and then Calcined at 960°C for 2.5h and cooled to room temperature;
[0019] (2) Mix boehmite, magnesite tailings and spinel evenly, crush them, pass through a 100-mesh sieve, add the calcined powder in step (1), mix well, and then add 55% sulfuric acid equivalent to the mass of the mixed powder Sodium and 20% sodium ch...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
flame retardant
aaaaa
aaaaa
flexural strength
aaaaa
aaaaa
softening point
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses refractory bricks prepared from pebbles in Changjiang River, and a preparation method of the refractory bricks. The refractory bricks are prepared from the following raw materials in parts by weight: 16-24 parts of the pebbles in Changjiang River, 24-38 parts of coal slime, 15-25 parts of boehmite, 12-23 parts of tailings of magnesite, 10-15 parts of spinel, 13-21 parts of silica powder, 16-28 parts of vanadium iron slag, 14-22 parts of andalusite, 15-25 parts of furnace ash, 25-35 parts of bauxite, 11-19 parts of phyllite, 8-14 parts of sulphite pulp and 10-15 parts of sediment in Yellow River. The pebbles in Changjiang River not only can be compounded with the raw materials such as the andalusite, the boehmite, the tailings of the magnesite and the spinel so as to be used as a refractory raw material of the refractory bricks, but also can be compounded with the raw materials such as the furnace ash, the sediment in Yellow River, the vanadium iron slag and the phyllite so as to be used as a filling material of the refractory bricks, so that the refractory bricks prepared from the pebbles in Changjiang River is excellent in comprehensive performance; the refractory bricks have the characteristics of being high in strength, high in refractoriness under load, good in high temperature resistance, high in acid and alkaline corrosion resistance, good in thermal shock resistance, and the like.
Description
Technical field [0001] The invention relates to a Yangtze River pebble refractory brick and a preparation method thereof, belonging to the field of refractories. Background technique [0002] Refractory brick is a kind of building material brick, and its properties are the same as its name, "refractory". It is a refractory made of refractory clay or other refractory materials, which can withstand various physical and chemical changes and mechanical effects at high temperatures. Refractory bricks are not common in our lives, but they appear in some buildings that are closely related to our lives, such as house construction, kiln construction, and thermal equipment. [0003] The patent number is: 201510494613.X. The invention patent discloses a foamed thermal insulation refractory brick produced from coal gangue and its preparation method. Its raw material composition is 40-60 parts of coal gangue and bauxite tailings in parts by weight. 30-50 parts, 2-15 parts of fly ash, 0-15 par...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.