Waterborne one-component coating and preparation method thereof

A one-component, coating technology, applied in the field of wood lacquer, can solve the problems of small dosage, can not play a significant role, large dosage, storage stability and other problems, achieve good fullness, fast drying, improved collapse resistance Effect

Inactive Publication Date: 2017-06-09
CHENGDU ZHANCHEN PAINT
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the later process, glass powder or transparent powder is used to improve performance, but a ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne one-component coating and preparation method thereof
  • Waterborne one-component coating and preparation method thereof
  • Waterborne one-component coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment 1: a kind of waterborne one-component paint, it is made up of the raw material of following weight part:

[0038]

[0039] Wherein, the alumina slurry is composed of the following raw materials in parts by weight: nano-alumina powder: 20; Tego715W: 2; BYK094: 0.1; Thixol 53L: 0.5; deionized water: 60.

[0040] The preparation method of above-mentioned waterborne one-component paint, it may further comprise the steps:

[0041] S1. Weighing: Weigh each raw material according to the proportion of the above formula, and set aside;

[0042] S2. Preparation of alumina slurry: take the raw material of alumina slurry, disperse deionized water, BYK094, Tego715W and Thixol53L at a speed of 500rad / min for 5min, add nano-alumina powder, adjust the speed to 950rad / min, and disperse 20min;

[0043] S3. Dispersion: Disperse PR-3500, Oubaodi 995, Thixol 53L, AMP-95, and dipropylene glycol methyl ether at a speed of 950rad / min until the oil shrinks, then add Tego715W, TS...

Embodiment 2

[0044]Embodiment 2: a kind of waterborne one-component coating, it is made up of the raw material of following weight part:

[0045]

[0046]

[0047] Wherein, the alumina slurry is composed of the following raw materials in parts by weight: nano-alumina powder: 26; Tego740W: 3; BYK024: 0.5; Coapur830w: 1; deionized water: 72.

[0048] The preparation method of above-mentioned waterborne one-component paint, it may further comprise the steps:

[0049] S1. Weighing: Weigh each raw material according to the proportion of the above formula, and set aside;

[0050] S2. Preparation of alumina slurry: take the raw material of alumina slurry, disperse deionized water, YK024, Tego740W and Coapur830w at a speed of 700rad / min for 7.5min, add nano alumina powder, adjust the speed to 1100rad / min, Disperse for 25 minutes;

[0051] S3. Dispersion: Disperse HEXIOM3000, Oubaodi 995, Coapur830w, AMP-95, and dipropylene glycol butyl ether at a speed of 1100rad / min until the oil shrinks,...

Embodiment 3

[0052] Embodiment 3: a kind of waterborne one-component paint, it is made up of the raw material of following weight part:

[0053]

[0054] Wherein, the alumina slurry is composed of the following raw materials in parts by weight: nano-alumina powder: 25; Tego760W: 5; TEGO foamex 810: 0.8; RM-8W: 2; deionized water: 80.

[0055] The preparation method of above-mentioned waterborne one-component paint, it may further comprise the steps:

[0056] S1. Weighing: Weigh each raw material according to the proportion of the above formula, and set aside;

[0057] S2. Preparation of alumina slurry: take the raw material of alumina slurry, disperse deionized water, TEGO foamex 810, Tego760W and RM-8W at a speed of 600rad / min for 10min, add nano-alumina powder, and adjust the speed to 1000rad / min, disperse for 30min;

[0058] S3. Dispersion: Disperse PR-3500, Oubaodi 995, RM-8W, ammonia water, diethylene glycol monobutyl ether at a speed of 1000rad / min until the oil shrinks, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-based one-component paint and a preparation method thereof. The water-based one-component paint is composed of the following raw materials: nano polyacrylic acid emulsion, water-based polyurethane emulsion, defoamer, dispersant, thickener, pigment, filler , alumina slurry, film-forming aids, pH regulator, anti-mold and bactericide and water; the water-based one-component coating obtained by the present invention has good fullness, good airtightness, excellent adhesion and fast drying, and anti-collapse Strong resistance and high hardness; the water-based one-component paint obtained by the present invention can be used directly by adding water, no use time limit, no water is added for use, and can be used as white putty without collapse; the water-based one-component white background obtained by the present invention The paint is a water-based green environmental protection product; the preparation method of the water-based one-component paint provided by the invention is simple in operation and convenient in preparation, and is suitable for large-scale industrial production.

Description

technical field [0001] The invention relates to the technical field of wood lacquer, in particular to a water-based one-component paint and a preparation method thereof. Background technique [0002] With the further improvement of environmental protection regulations, in order to reduce the load on the earth, new low-VOC or zero-VOC emission coatings have become the focus of research and development. The research, development, promotion and application of water-based wood coatings have attracted more and more attention. In recent years, the research and development of water-based wood paint has achieved unprecedented development in our country. [0003] Water-based wood paint has been successfully applied in home decoration and ordinary furniture, and is expanding its market share. However, in the high-end furniture market controlled by oil-based polyurethane paint, the market share of water-based paint is relatively small. High-grade furniture paint requires high fullnes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D175/04C09D7/12C09D5/34
CPCC09D133/00C08K2201/011C08K2201/014C08L2205/035C09D5/34C09D7/61C08L75/04C08K13/02C08K2003/2227C08K3/34C08K2003/2241C08K2003/265
Inventor 麦毅陈寿生
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap