Rubber material of baseball core

A technology of rubber materials and baseball cores, applied in the field of rubber, can solve the problems of incompatibility between durability and batting effect, and the coordination of synthetic rubber's impact resistance, resilience and weight, etc., to improve batting effect, increased durability, increased impact resistance and elastic effects

Inactive Publication Date: 2017-06-13
天长市良文运动器材有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Baseball needs to have appropriate impact resistance, elasticity and light weight to maintain the durability and batting effect of the baseball, but the coordination of the existing synthetic rubber against impact, resilience and weight is not very good, durability and The batting effect can't be both

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of rubber material for baseball core, its raw material comprises by weight: 70 parts of natural rubber, 30 parts of isoprene rubber, 60 parts of filler, 1.5 parts of tributyl citrate, 1.5 parts of methyl epoxy acetyl linoleate, 45 parts of nano-magnesium hydroxide, 12 parts of zinc borate, 2 parts of Si69, 1.5 parts of sulfur, 0.6 parts of dicumyl peroxide, 0.2 parts of accelerator D, 0.25 parts of accelerator TMTD, 5 parts of Ca / Zn composite stabilizer, Antioxidant 264 0.5 part, antioxidant 1010 0.3 part, polyethylene wax 3 parts;

[0020] Wherein, the raw materials of the filler include: modified montmorillonite, hollow glass microspheres, and modified microcrystalline cellulose.

Embodiment 2

[0022] A kind of rubber material for baseball core, its raw material comprises by weight: 60 parts of natural rubber, 40 parts of isoprene rubber, 50 parts of filler, 2 parts of tributyl citrate, 1 part of methyl epoxy acetyl linoleate, 50 parts of nano-magnesium hydroxide, 10 parts of zinc borate, 3 parts of Si69, 1 part of sulfur, 0.7 parts of dicumyl peroxide, 0.1 part of accelerator D, 0.3 parts of accelerator TMTD, 4 parts of Ca / Zn composite stabilizer, Antioxidant 264 0.6 part, antioxidant 1010 0.2 part, polyethylene wax 4 parts;

[0023] Among them, the raw materials of the filler include: 400-mesh modified montmorillonite, 800-mesh hollow glass microspheres, γ-aminopropyltriethoxysilane modified microcrystalline cellulose, among which, modified montmorillonite, hollow glass microspheres The weight ratio of beads to γ-aminopropyltriethoxysilane modified microcrystalline cellulose is 1:7:1;

[0024] In the preparation process of modified montmorillonite, in a nitrogen a...

Embodiment 3

[0026] A kind of rubber material for baseball core, its raw material comprises by weight: 80 parts of natural rubber, 20 parts of isoprene rubber, 70 parts of filler, 1 part of tributyl citrate, 2 parts of methyl epoxy acetyl linoleate, 40 parts of nano-magnesium hydroxide, 15 parts of zinc borate, 1 part of Si69, 2 parts of sulfur, 0.5 parts of dicumyl peroxide, 0.3 parts of accelerator D, 0.2 parts of accelerator TMTD, 6 parts of Ca / Zn composite stabilizer, Antioxidant 264 0.4 part, antioxidant 1010 0.4 part, polyethylene wax 2 parts;

[0027] Among them, the raw materials of the filler include: 500-mesh modified montmorillonite, 600-mesh hollow glass microspheres, γ-aminopropyltriethoxysilane modified microcrystalline cellulose, among which, modified montmorillonite, hollow glass microspheres The weight ratio of beads to γ-aminopropyltriethoxysilane modified microcrystalline cellulose is 2:5:2;

[0028] In the preparation process of modified montmorillonite, in a nitrogen ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber material of a baseball core. The rubber material is prepared from the following raw materials in parts by weight: 60 to 80 parts of natural rubber, 20 to 40 parts of isoprene rubber, 50 to 70 parts of filler, 1 to 2 parts of tributyl citrate, 1 to 2 parts of epoxy acetyl methyl linoleate, 40 to 50 parts of nanometer magnesium hydroxide, 10 to 15 parts of zinc borate, 1 to 3 parts of Si69, 1 to 2 parts of sulfur, 0. 5 to 0.7 part of dicumyl peroxide, 0.1 to 0.3 part of accelerant D, 0.2 to 0.3 part of accelerant TMTD, 4 to 6 parts of Ca / Zn (calcium / zinc) composite stabilizer, 0.4 to 0.6 part of anti-aging agent, 0.2 to 0.4 part of antioxidant, and 2 to 4 parts of polyethylene wax, wherein the filler comprises modified montmorillonite, hollow glass microbeads, and modified microcrystalline cellulose. The rubber material has the advantages that the anti-impact property, toughness and elasticity are good, the weight is light, and the durability and ball striking effect are better.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a rubber material for a baseball core. Background technique [0002] Softball is designed to promote baseball and softball. It is similar in nature to baseball and softball. Its competitiveness and fun can be compared with regular baseball and softball. It is characterized by simplified game rules, low requirements for venue conditions, and the number of people who can participate Many, safe, very suitable for carrying out on campus, from which you can experience the fun of baseball and softball. [0003] The baseball used in soft baseball is divided into hollow ball and solid ball. The core material of solid ball is generally cork or synthetic rubber. Cork is the bark of the oak tree. The main component is cork fiber. Its source is limited, and a large amount of use will consume natural resources. Moreover, the baseball made of cork is not stable in coagulation during molding, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L23/06C08L1/04C08K13/06C08K9/04C08K5/11C08K5/14C08K3/38C08K3/22C08K3/34C08K7/28
CPCC08L7/00C08K2201/011C08L2201/02C08L2205/035C08L2205/04C08L9/00C08L23/06C08L1/04C08K13/06C08K9/08C08K5/11C08K5/14C08K2003/387C08K2003/2224C08K3/346C08K7/28
Inventor 周良正
Owner 天长市良文运动器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com