Low-gloss bending-resistant heat transfer printing powder coating used for section aluminum and a preparing method thereof
A powder coating, low-gloss technology, applied in powder coatings, polyester coatings, coatings, etc., can solve problems such as unsatisfactory, low gloss, mechanical properties of coating films, and decreased storage stability of weather-resistant powder coatings, so as to avoid Effects of residual paper printing, reducing gloss, and improving transfer effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0034] Example 1
[0035] Prepare low-gloss and anti-bending thermal transfer powder coatings for aluminum profiles according to the following steps:
[0036] (1) According to the following A component formula, put the raw materials into the mixing tank according to their corresponding mass percentages for pre-mixing, and the time is 3-4 minutes;
[0037] A component:
[0038]
[0039] Wherein, the saturated carboxyl-terminated polyester resin A is a high-toughness carboxyl polyester resin with an acid value of 46 mgKOH / g, a viscosity of 7500 mPa·s at 200°C, and a glass transition temperature of 67°C; The median particle size of extinct barium is 5.8μm;
[0040] (2) Use a twin-screw extruder to melt, knead, disperse and extrude the pre-mixed raw materials uniformly. The temperature in zone I of the extruder is set to 115°C, and the temperature in zone II of the extruder is set to 115°C. The output screw frequency is 30Hz; then it is compressed and crushed;
[0041] (3) The crushed mate...
Example Embodiment
[0055] Example 2
[0056] Prepare low-gloss and anti-bending thermal transfer powder coatings for aluminum profiles according to the following steps:
[0057] (1) According to the following A component formula, put the raw materials into the mixing tank according to their corresponding mass percentages for pre-mixing, and the time is 3-4 minutes;
[0058] A component:
[0059]
[0060] Wherein, the saturated carboxyl-terminated polyester resin A is a high-toughness carboxyl polyester resin with an acid value of 47 mgKOH / g, a viscosity of 7700 mPa·s at 200°C, and a glass transition temperature of 67°C; The median particle size of extinct barium is 5.7μm;
[0061] (2) Use a twin-screw extruder to melt, knead, uniformly disperse and extrude the pre-mixed raw materials. The temperature in zone I of the extruder is set to 118°C, and the temperature in zone II of the extruder is set to 115°C. The output screw frequency is 33Hz; then press and crush;
[0062] (3) The crushed materials are gra...
Example Embodiment
[0075] Example 3
[0076] Prepare low-gloss and anti-bending thermal transfer powder coatings for aluminum profiles according to the following steps:
[0077] (1) According to the following A component formula, put the raw materials into the mixing tank according to their corresponding mass percentages for pre-mixing, and the time is 3-4 minutes;
[0078] A component:
[0079]
[0080]
[0081] Wherein, the saturated carboxyl-terminated polyester resin A is a high-toughness carboxyl polyester resin with an acid value of 50 mgKOH / g, a viscosity of 7800 mPa·s at 200°C, and a glass transition temperature of 67°C; The median diameter of extinction barium is 5.5μm;
[0082] (2) Use a twin-screw extruder to melt, mix, disperse and extrude the pre-mixed raw materials uniformly. The temperature in zone I of the extruder is set to 120°C, and the temperature in zone II of the extruder is set to 120°C. The output screw frequency is 40Hz; then it is compressed and crushed;
[0083] (3) The crushed...
PUM
Property | Measurement | Unit |
---|---|---|
Acid value | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap