A kind of weather-resistant hot-melt pressure-sensitive adhesive and preparation method thereof

A hot-melt, pressure-sensitive adhesive technology, used in adhesives, adhesive types, mineral oil hydrocarbon copolymer adhesives, etc., can solve the problem of hot-melt pressure-sensitive adhesives being prone to aging

Active Publication Date: 2018-07-31
XI NIU PI WATERPROOFING TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the defect that ordinary hot-melt pressure-sensitive adhesives are prone to aging after receiving ultraviolet radiation and heat treatment in the prior art, the present invention provides a hot-melt pressure-sensitive adhesive, which has ultraviolet resistance, With the advantages of heat aging resistance, high peel strength and strong adhesion, it is suitable for the production of non-asphalt-based pre-paved waterproof materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of weather-resistant hot-melt pressure-sensitive adhesive and preparation method thereof
  • A kind of weather-resistant hot-melt pressure-sensitive adhesive and preparation method thereof
  • A kind of weather-resistant hot-melt pressure-sensitive adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A weather-resistant hot-melt pressure-sensitive adhesive is composed of the following raw materials by mass percentage: 80% of butyl rubber, 0.5% of hydroxy acrylic resin, 10% of tackifier, 5% of plasticizer, 0.5% of silane coupling agent, Antioxidant 2% and UV Resistant 2%.

[0032] The unsaturation degree of the butyl rubber is 0.5%; the hydroxyl value of the hydroxy acrylic resin is 100; the silane coupling agent is allyl triethoxysilane; the tackifier is C5 Petroleum resin; the plasticizer is polyisobutylene; the molecular weight of the polyisobutylene is less than 3000; the antioxidant is SK1010; the UV-resistant agent is compounded by UV-531 and UV-327, The mass ratio of the two is 1:2.

[0033] The present invention also provides a method for preparing the weather-resistant hot-melt pressure-sensitive adhesive, comprising the following steps:

[0034] (1) Put butyl rubber, plasticizer, tackifier, hydroxy acrylic resin, silane coupling agent into a reactor with ...

Embodiment 2

[0039] A weather-resistant hot-melt pressure-sensitive adhesive is composed of the following raw materials by mass percentage: 56% of butyl rubber, 5% of hydroxy acrylic resin, 20% of tackifier, 12% of plasticizer, 3% of silane coupling agent, Antioxidant 2% and UV Resistant 2%.

[0040] The unsaturation degree of the butyl rubber is 2.0%; the hydroxyl value of the hydroxyacrylic resin is 100; the silane coupling agent is vinyltriethoxysilane; the tackifier is C9 petroleum resin; the plasticizer is naphthenic oil; the viscosity of the naphthenic oil is 60-400CPS at 40°C; the antioxidant is antioxidant 264; the UV-resistant agent is composed of UV- 531 and UV-326 are compounded, and the mass ratio of the two is 1:1.

[0041] The present invention also provides a method for preparing the weather-resistant hot-melt pressure-sensitive adhesive, comprising the following steps:

[0042] (1) Put butyl rubber, plasticizer, tackifier, hydroxy acrylic resin, silane coupling agent into...

Embodiment 3

[0047] A weather-resistant hot-melt pressure-sensitive adhesive is composed of the following raw materials by mass percentage: 70% of butyl rubber, 2% of hydroxy acrylic resin, 15% of tackifier, 10% of plasticizer, 1% of silane coupling agent, Antioxidant 1% and UV Resistant 1%.

[0048] The unsaturation degree of the butyl rubber is 1.0%; the hydroxyl value of the hydroxy acrylic resin is 100; the silane coupling agent is vinyl tris(β-methoxyethoxy) silane; the The tackifier is terpene resin; the plasticizer is white oil; the white oil has a viscosity of 60-400CPS at 40°C; the antioxidant is antioxidant 1035; the UV-resistant The agent is composed of two kinds of UV-531 and UV-329, and the mass ratio of the two is 1:1.2.

[0049] The present invention also provides a method for preparing the weather-resistant hot-melt pressure-sensitive adhesive, comprising the following steps:

[0050] (1) Put butyl rubber, plasticizer, tackifier, hydroxy acrylic resin, silane coupling age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of unsaturationaaaaaaaaaa
degree of unsaturationaaaaaaaaaa
degree of unsaturationaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of development of waterproof materials, and in particular relates to weather-resistant hot-melting type pressure-sensitive adhesive and a preparation method thereof. The weather-resistant hot-melting type pressure-sensitive adhesive consists of the following raw materials in percentage by mass: 56 to 80 percent of butyl rubber, 0.5 to 5 percent of hydroxy acrylic resin, 10 to 20 percent of a thickening agent, 3 to 12 percent of a plasticizer, 0.1 to 3 percent of a silane coupling agent, 0.1 to 2 percent of an antioxidant, and 0.5 to 2 percent of an ultraviolet resisting agent. The weather-resistant hot-melting type pressure-sensitive adhesive has high adhesion property and also has excellent ageing resistance and ultraviolet resistance. Meanwhile, the problem that the butyl rubber and other components are separated due to the butyl rubber is not dissolvable in other components is solved by introducing the coupling agent and the hydroxy acrylic resin. The technical bottleneck that the weather resistance of the product is prolonged only by an ultraviolet additive and an anti-ageing agent because the main raw materials of the traditional hot melt adhesive product have low ultraviolet resistance is broken through. The phenomenon that the life of the product is shortened after the functions of the ultraviolet resisting agent and the anti-ageing agent are attenuated is avoided.

Description

technical field [0001] The invention belongs to the technical field of waterproof material development, and specifically relates to a weather-resistant hot-melt pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] Pressure sensitive adhesive (PSA) refers to a type of adhesive that is sensitive to pressure and can be bonded to the adherend with a little pressure on the finger, without the use of solvents or other auxiliary means. Hot-melt pressure-sensitive adhesive is the third-generation pressure-sensitive adhesive product after solvent-based and emulsion-based pressure-sensitive adhesives. Compared with the previous two, hot-melt pressure-sensitive adhesive has no solvent, which is more conducive to environmental protection and safe production, and has high production efficiency. , the production cost is relatively low, so countries around the world are vigorously developing hot-melt pressure-sensitive adhesives. [0003] At present,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J123/22C09J157/02C09J145/00C09J11/08C09J11/06
CPCC08L2201/08C08L2205/02C08L2205/025C08L2205/035C09J11/06C09J11/08C09J123/22C08L33/00C08L57/02C08L23/22C08L91/00C08L45/00C08L91/06C08K5/00C08K5/5425C08K5/1345
Inventor 卢桂才凌日华陆善庆陈立斌赵晓岚杨建国莫里麟陈柱先
Owner XI NIU PI WATERPROOFING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com