Waterborne ceramic digital spray-painting ink and a preparing method thereof

A digital inkjet and ink technology, applied in ink, household utensils, applications, etc., can solve the problems of unstable properties of the sol, expensive production costs, and complicated processes, and achieve stable color rendering, low production costs, and simple production processes Effect

Inactive Publication Date: 2017-06-30
QINGDAO AGRI UNIV
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process is complicated and the production cost is expensive; at the same time, the properties of the sol solution are unstable, and precipitation will occur after long-term storage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of water-based ceramic digital printing ink, it is made up of the raw material of following percentage by weight: water is 25%, glycerine is 5%, propylene glycol is 5%, ethylene glycol is 10%, polyethylene glycol is 15%, positive Butanol is 10%, dispersant is 2.5%, coupling agent is 0.4%, surfactant is 0.4%, defoamer is 0.4%, anti-settling agent is 1%, sterilant is 0.3%, cobalt blue pigment 25%.

[0028] Mix water, glycerol, propylene glycol, ethylene glycol, polyethylene glycol, n-butanol, dispersant, coupling agent, surfactant, defoamer, anti-settling agent, sterilant, and pigment mixture in proportion Grind evenly with a sand mill at 2000 rpm for 5 hours until the particle size is about 300nm, and test its viscosity and surface tension. The high temperature is 1300°C, the flash point is <60°C, and the stability is no delamination and precipitation in the thermal test (60°C) for 72 hours, and the water-based ceramic digital inkjet ink is obtained. Wherein, th...

Embodiment 2

[0030] A kind of water-based ceramic digital printing ink, it is made up of the raw material of following percentage by weight: water is 30%, glycerine is 10%, propylene glycol is 5%, ethylene glycol is 5%, polyethylene glycol is 11%, positive Butanol is 9%, dispersant is 2.5%, coupling agent is 0.4%, surfactant is 0.4%, defoamer is 0.4%, anti-settling agent is 1%, sterilant is 0.3%, red brown pigment 25%.

[0031] Water, glycerol, propylene glycol, ethylene glycol, polyethylene glycol, n-butanol, dispersant, coupling agent, surfactant, defoamer, anti-settling agent, sterilizer, red brown pigment mixture according to Mix evenly with a sand mill at 2000 rpm for 5 hours until the particle size is about 300nm. Test its viscosity and surface tension. The parameters meet the following standards: particle size is 300nm, surface tension is 35mN / m, viscosity is 25cps, and solid content is 30%. , the high temperature resistance is 1400°C, the flash point is <60°C, and the stability is...

Embodiment 3

[0033] A kind of water-based ceramic digital printing ink, it is made up of the raw material of following percentage by weight: water is 34%, glycerine is 10%, propylene glycol is 10%, ethylene glycol is 5%, polyethylene glycol is 5%, positive Butanol is 5%, dispersant is 3.5%, coupling agent is 0.4%, surfactant is 0.4%, defoamer is 0.4%, anti-settling agent is 1%, sterilant is 0.3%, praseodymium yellow pigment 25%.

[0034] Water, glycerol, propylene glycol, ethylene glycol, polyethylene glycol, n-butanol, dispersant, coupling agent, surfactant, defoamer, anti-sedimentation agent, sterilizer, praseodymium yellow pigment mixture according to Mix evenly with a sand mill at 2000 rpm for 5 hours until the particle size is about 350nm. Test its viscosity and surface tension. The parameters meet the following standards: particle size is 350nm, surface tension is 40mN / m, viscosity is 30cps, and solid content is 30%. , the high temperature resistance is 1500°C, the flash point is <6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Flash pointaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The objective of the invention is to provide waterborne ceramic digital spray-painting ink and a preparing method thereof to overcome defects of present waterborne ceramic digital spray-painting ink. To achieve the objective, the provided ink is prepared by mixing water, glycerol, propylene glycol, glycol, polyethylene glycol, n-butanol, a dispersant, a coupling agent, a surfactant, a defoamer, an anti-settling agent, a sterilizing agent and pigment. The water, the glycerol, the propylene glycol, the glycol, the polyethylene glycol, the n-butanol, the dispersant, the coupling agent, the surfactant, the defoamer, the anti-settling agent, the sterilizing agent and the pigment are fully mixed according to a ratio, the mixture is ground by a sand mill for 5 h at a speed of 2000 r / min until the granularity is about 150-350 nm, viscosity and surface tension of the product are tested, and the ink is obtained when the viscosity and surface tension are qualified.

Description

technical field [0001] The invention relates to a ceramic digital inkjet ink, in particular to a water-based ceramic digital inkjet ink and a preparation method thereof. Background technique [0002] Along with the progress of society, although oil-based ceramic digital inkjet ink has played a huge role in our lives, the organic substances such as benzene contained in them are harmful to the human body, and their harm cannot be eliminated for a long time. Meet the requirements of building an environment-friendly society, and will gradually be replaced by environment-friendly products. The water-based ceramic digital inkjet printing ink has gradually entered our sight in line with the trend of the times. Because they do not contain organic substances such as benzene, they are harmless to the environment and are environmentally friendly products, which will gradually become the mainstream of future products. [0003] Foreign experts started to research and develop digital cer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/30C09D11/322
CPCC09D11/30C09D11/322
Inventor 刘清芝李清杨登峰
Owner QINGDAO AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com