Gradual change type peacock blue glaze ceramic and preparation process thereof

A preparation process, blue glaze technology, applied in the field of ceramic products, can solve the problem of uncontrollable color of firing results, achieve the effect of improving economic benefits and market competitiveness, smooth joints, and unique artistic effects

Active Publication Date: 2017-08-18
德化县如瓷生活文化有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above two kinds of peacock blues have their own characteristics in terms of performance effects, but in terms of production technology, they all belong to the artistic effect produced by the kiln transformation process. As we all know, the kiln transformation effect and the firing results are all random and uncontrollable. The development of a peacock blue glazed ceramic with stable effect and gradient can not only meet the aesthetic needs of consumers, but also provide a brand-new ceramic product, which has positive significance for promoting the development of ceramic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0027] Gradient peacock blue glazed ceramics, including the ceramic body, including the light-colored glaze set on the surface of the ceramic body and the dark-colored glaze set on the part of the light-colored glaze, the thickness of the light-colored glaze is 0.2mm, and the thickness of the dark-colored glaze is 0.5-0.8 mm

[0028] Light-colored glaze, its weight parts are as follows: light-colored glaze, its weight parts are as follows: transparent frit 23 parts, feldspar 27 parts, quartz 12 parts, kaolin 16 parts, manganese oxide 8 parts, iron hydroxide 6 parts, cobalt 4 parts , 4 parts of barium carbonate;

[0029] Dark glaze, its parts by weight are as follows: 23 parts of quartz, 24 parts of talc, 11 parts of potassium feldspar, 12 parts of calcite, 11 parts of titanium, 6 parts of mica, 6 parts of chalk, 4 parts of tanzanite, 2 parts of iron oxide, tin 1 serving.

[0030] The preparation process of gradient peacock blue glazed ceramics, the preparation of the above g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to gradual change type peacock blue glaze ceramic and a preparation process thereof. The gradual change type peacock blue glaze ceramic comprises light-colored glaze on the surface of a ceramic blank body, and dark-colored glaze on the local part of the light-colored glaze. For the gradual change type peacock blue glaze ceramic, the surface of the light-colored glaze is thin and transparent, and has glassy luster; manganese oxide, iron hydroxide, and cobalt are introduced as color agents, so that the light-colored glaze displays slightly light blue; the dark-colored glaze is arranged in the surface of light-colored glaze, is bright, and has a strong glassy texture, the overall ceramic is blue-green; the combined degree of the light-colored glaze and the dark-colored glaze is high; the combined part is smooth, and free of cracking; and the overall color of the ceramic can be adjusted according to the thickness of the dark-colored glaze, from shallow to deep, to form a variety of lines, thus forming a unique artistic effect. The gradual change type peacock blue glaze ceramic is stable in effect, can be produced in a large quantity, increases the yield, reduces the production cost of materials, and improve the economic efficiency and market competitiveness.

Description

technical field [0001] The invention belongs to the field of ceramic products, and in particular relates to a gradient peacock blue glazed ceramic and a preparation process. Background technique [0002] Among the color glazes, peacock blue glaze is also called malachite green glaze or turquoise blue, which is a kind of medium temperature glaze with copper as the colorant. According to the variety of production, peacock blue glaze can be divided into three categories: peacock blue monochromatic glaze, peacock blue blue and white, and mixed colored porcelain related to peacock blue. Among them, peacock blue blue and white is a combination of low-temperature peacock blue and underglaze blue and white. It is made by covering the surface of painted cobalt with low-temperature peacock blue glaze and fired. The mixed colored porcelain related to peacock blue is peacock blue and yellow, brown, etc. Combination of low-temperature colored glazes. The traditional peacock blue glaze ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/20
CPCC03C8/20
Inventor 徐海燕
Owner 德化县如瓷生活文化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products