Easy-adhesive composition, optical film using same, and manufacturing method thereof

A technology for bonding compositions and optical films, which is applied in chemical instruments and methods, synthetic resin layered products, polarizing elements, etc., can solve problems such as poor adhesion and insufficient adhesion of polarizers, and maintain close adhesion Excellent adhesion, high adhesion effect

Active Publication Date: 2019-09-10
OKURA IND
View PDF21 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, acrylic resin films have problems of poor adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-adhesive composition, optical film using same, and manufacturing method thereof
  • Easy-adhesive composition, optical film using same, and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5 and comparative example 1～10

[0100] 1. Manufacture of easy-bonding composition

[0101] Each component shown in Tables 1 and 2 was mixed so that it might become the solid content amount (unit: part by weight) shown in Tables 1 and 2, and the easily-adhesive composition was manufactured. In addition, ion-exchange water was used as the aqueous solvent of an easily-adhesive composition, and it prepared so that the solid content might become 8 weight%.

[0102] 2. Fabrication of Optical Films

[0103] Using a single-screw extruder (φ=20.0mm, L / D=25) and a hanger-shaped T-die (width 150mm), at 280°C, the acrylic resin composition [Tg: 135°C, melt viscosity: 700Pa·s (The temperature is 270°C, the shear rate is 100 (1 / sec))] pellets are melt-extruded, and the above-mentioned resin composition in a molten state is discharged onto a cooling roll maintained at 110°C to form an acrylic resin with a thickness of 100 μm membrane. Next, the easily-adhesive composition obtained above was coated on one surface of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The object of the present invention is to provide an easy-adhesive composition that not only suppresses the decrease in initial performance when used under high temperature and high humidity for a long time, but also satisfies the heat and humidity resistance in a more severe environment, and provides an adhesive composition for use in thermoplastic resin films. An optical film having an easily bonding layer formed from the easily bonding composition provided on at least one surface. The invention provides an easy-adhesive composition, which contains: 100 parts by weight of a water-dispersible polyurethane resin having a carboxyl group, 1-25 parts by weight of a water-soluble carbodiimide compound, and 1-25 parts by weight of a water-dispersible carbon diimide An imine compound; an optical film comprising an easily bonding layer formed from the easily bonding composition provided on at least one surface of a thermoplastic resin film.

Description

technical field [0001] The present invention relates to an easily bonding composition and an optical film having an easily bonding layer composed of the easily bonding composition. The present invention also relates to a method for producing the optical film, a polarizer (polarizing plate, polarizing plate) and an image display device including the optical film. Background technique [0002] Acrylic resin films made of (meth)acrylic polymers typified by polymethyl methacrylate are known to have excellent optical properties such as light transmittance, and are known to have excellent balance between mechanical strength and moldability. Accordingly, acrylic resin films have been used as optical films incorporated in image display devices such as liquid crystal display devices (LCD), plasma display panels (PDP), and organic EL display devices (OLED). [0003] An optical film is usually used in a laminated state with other functional films. For example, when the optical film i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04B32B27/30B32B27/40C09D5/00C09D7/63G02B5/30
CPCB32B27/30B32B27/40C09D5/00C09D175/04G02B5/30C09D7/40C09D7/63
Inventor 吉泽正浩松本匡弘
Owner OKURA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap