Building material and preparation method thereof

A technology for building materials and raw materials, applied in the field of building materials, can solve the problems of high requirements for thermal insulation, environmental protection and energy saving, and achieve the effects of light weight, small thermal conductivity and small particle size

Inactive Publication Date: 2017-08-29
HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the existing building materials still have deficiencies when applied to buildings with high requirements for flexural and compressive strength, thermal insulation and environmental protection and energy saving, the purpose of the present invention is to provide a building material and its preparation method. Advanced building materials have the advantages of high flexural and compressive strength, good thermal insulation performance, environmental protection and energy saving

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A building material comprising the following raw materials in parts by weight: 6 parts of nano titanium dioxide, 10 parts of asphalt, 14 parts of bauxite, 10 parts of tricalcium silicate, 6 parts of polypropylene resin, 7 parts of quartz stone, 6 parts of calcium acetate, 22 parts of polyamide fiber, 17 parts of sepiolite powder, 23 parts of bentonite, 18 parts of electric furnace slag powder, 16 parts of floating beads, 20 parts of waste rock wool board, 17 parts of inorganic adhesive, 0.7 part of foaming agent, 0.5 part of retarder , 0.5 parts of water reducing agent and 11 parts of water.

[0046] The building material prepared under this formula has reached the best in terms of flexural and compressive strength, thermal insulation performance, environmental protection and energy saving.

[0047] Electric furnace slag powder and waste rock wool boards are added to the raw materials of the present invention. These industrial wastes and construction wastes have been le...

Embodiment 2

[0068] A building material comprising the following raw materials in parts by weight: 5 parts of nano titanium dioxide, 7 parts of asphalt, 11 parts of bauxite, 8 parts of tricalcium silicate, 4 parts of polypropylene resin, 6 parts of quartz stone, 5 parts of calcium acetate, 17 parts of polyamide fiber, 13 parts of sepiolite powder, 21 parts of bentonite, 15 parts of electric furnace slag powder, 11 parts of floating beads, 17 parts of waste rock wool board, 15 parts of inorganic adhesive, 0.5 part of foaming agent, 0.3 part of retarder , 0.2 parts of water reducer and 8 parts of water.

[0069] Electric furnace slag powder and waste rock wool boards are added to the raw materials of the present invention. These industrial wastes and construction wastes have been left in cities for a long time, not only occupying urban land, but also polluting the local environment. Now these industrial wastes and construction wastes are recycled and reused. The purpose of energy saving and ...

Embodiment 3

[0090] A building material comprising the following raw materials in parts by weight: 7 parts of nano-titanium dioxide, 13 parts of pitch, 17 parts of bauxite, 12 parts of tricalcium silicate, 8 parts of polypropylene resin, 8 parts of quartz stone, 7 parts of calcium acetate, 27 parts of polyamide fiber, 21 parts of sepiolite powder, 25 parts of bentonite, 21 parts of electric furnace slag powder, 21 parts of floating beads, 23 parts of waste rock wool board, 19 parts of inorganic adhesive, 0.9 part of foaming agent, 0.7 part of retarder , 0.8 parts of water reducing agent and 14 parts of water.

[0091] Electric furnace slag powder and waste rock wool boards are added to the raw materials of the present invention. These industrial wastes and construction wastes have been left in cities for a long time, not only occupying urban land, but also polluting the local environment. Now these industrial wastes and construction wastes are recycled and reused. The purpose of energy sav...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Meshaaaaaaaaaa
Login to View More

Abstract

The invention provides a building material and a preparation method thereof, which relates to the technical field of the building material. The building material comprises the following raw materials in parts by weight: 5-7 parts of nano titanium dioxide, 7-13 parts of asphalt, 11-17 parts of bauxitic clay, 8-12 parts of tricalcium silicate, 4-8 parts of polypropylene resin, 6-8 parts of quartz stone, 5-7 parts of calcium acetate, 17-27 parts of polyarmide fiber, 13-21 parts of meerschaum powder, 21-25 parts of bentonite, 15-21 parts of electric furnace slag powder, 11-21 parts of floating beads, 17-23 parts of waste rock wool plate, 15-19 parts of an inorganic adhesive, 0.5-0.9 parts of a foaming agent, 0.3-0.7 parts of a delayed coagulant, 0.2-0.8 parts of a water reducer, and 8-14 parts of water. The preparation method comprises the following steps: 1) weighing the raw materials; 2) milling the materials; 3) heating the materials; 4) roasting the materials; 5) crushing; 6) stirring; and 7) moulding and demoulding, piling and performing maintenance. The method solves the problem that the current environmental protection building materials used for the buildings having high compressive strength, heat insulation, and environmental protection and energy saving requirements are insufficient.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a building material and a preparation method thereof. Background technique [0002] With the progress of society and the improvement of people's living standards, people's requirements for building materials are getting higher and higher, especially for building materials in building materials. question. [0003] In the Chinese patent document announced on February 3, 2016, a flexural and compressive nano-building material and its preparation method (authorized announcement number CN104261758B), the building material includes the following raw materials in parts by weight: nano-titanium dioxide is 5-8 7-15 parts of heated pitch, 11-19 parts of bauxite, 8-13 parts of tricalcium silicate, 4-9 parts of polypropylene resin, 6-10 parts of 400-mesh quartz stone powder, Calcium acetate is 5-9 parts, water is 15-23 parts. The preparation method includes heating, mixing, m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/26C04B38/02
CPCC04B28/26C04B2201/32C04B2201/50C04B14/305C04B24/36C04B14/303C04B14/043C04B24/2611C04B14/06C04B24/04C04B16/0691C04B14/042C04B14/104C04B18/141C04B18/082C04B18/16C04B22/10C04B2103/22C04B2103/302C04B38/02
Inventor 王磊
Owner HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products