Fiber-enhanced aerogel-polymer composite material and preparation method thereof

A composite material and fiber-reinforced technology, which is applied in the field of preparation of fiber-reinforced aerogel-polymer composite materials, can solve the problems of low grade and unsatisfactory comprehensive performance, and achieves the promotion of industrial upgrading and high durability. The effect of heat resistance and simple and easy process

Inactive Publication Date: 2017-08-29
浙江圣润纳米科技有限公司
View PDF5 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Rubber is an elastomer with excellent stretchability, but its overall performance is not satisfactory. In the process of producing rubber products, it is usually necessary to add ca

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber-enhanced aerogel-polymer composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] According to the method of patent CN2014102703529, a glass fiber mat reinforced silica airgel board is prepared, the size of the silica airgel board is 300mm*300mm*10mm, and the density of the silica airgel is 100kg / m 3 , the average pore size is 36nm, the porosity is 90%, and the hydrophobicity is 99.8%. Polymer adopts unsaturated polyester resin, gets unsaturated polyester resin 1000g, benzoyl peroxide 8g, tert-butyl peroxybenzoate 7g is made into unsaturated polyester resin glue. The composite process adopts resin transfer molding. The glass fiber reinforced silica airgel plate is pre-laid in the closed mold cavity, the mold is locked, and the unsaturated polyester resin glue is injected into the mold cavity with pressure. After the reinforcement material is soaked Curing at room temperature, and then demoulding to form a composite material.

Embodiment 2

[0053] According to the method of patent CN2015102953891, the carbon fiber unidirectional cloth reinforced silica-titania airgel cloth is prepared, and the size of the silica-titania airgel cloth is 300mm*300mm*2mm, wherein the silica-titania airgel cloth The density is 80kg / m 3 , the average pore size is 45nm, the porosity is 93%, and the hydrophobicity is 99.8%. The polymer adopts epoxy resin, take bisphenol A type epoxy resin E-54 --- 700g; polyethersulfone (PES) --- 100g; maleic rosin --- 250g, mix and heat to 55 ° C, keep warm for 1 hour, to get epoxy resin glue. Vacuum bag / autoclave forming process is used to lay carbon fiber unidirectional cloth reinforced silica-titania airgel cloth in the mold, and the upper layer is laid with diversion net and diversion tube, and then the bag is made and sealed to make the interior in a vacuum And generate negative pressure to eliminate air bubbles, then introduce epoxy resin glue, and obtain carbon fiber unidirectional fabric rein...

Embodiment 3

[0055] According to the method of patent CN2015102953891, the zirconia airgel sheet is reinforced with basalt fiber cloth, the size of the zirconia airgel sheet is 200mm*200mm*1mm, and the density of the zirconia airgel is 110kg / m 3 , the average pore size is 32nm, the porosity is 90%, and the hydrophobicity is 99.8%. Polymer adopts phenolic resin, take phenolic resin 450g, hexamethylenetetramine 40g, polystyrene 67g, mix and stir to obtain phenolic resin glue. Using the winding molding process, the basalt fiber cloth reinforced zirconia airgel cloth tape impregnated with phenolic resin glue is wound on the mandrel according to certain rules, and then solidified and demoulded to become a composite material. Sand and paint the cured composite material.

[0056] Table 1 Test data of fiber reinforced airgel-polymer composites

[0057] serial number

[0058] Note: The comparison item is the composite material obtained by using the same type of fiber and polymer and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Average pore sizeaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a fiber-enhanced aerogel-polymer composite material and a preparation method thereof. Fiber-enhanced aerogel is taken as a reinforcement material, and polymer is taken as a substrate and fills a three-dimensional nanometer hole structure of aerogel to form a composite material having a structure of interlacing polymer with a nanometer three-dimensional network of aerogel. The polymer-based composite material has improved thermal resistance, wear resistance, aging resistance, compression strength, impact resistance, and fracture resistance, and is improved in or endowed with features with the respect to sound, light, electricity, magnetism and heat. The method is simple and easy in technical process and beneficial for industrial massive production, and can promote upgrading of conventional polymer-based composite material industry. The fiber-enhanced aerogel-polymer composite material has high application value in the fields of national defense and military, space and aeronautics, high-speed trains, ships and vessels, automobiles, leisure sports, offshore oil and gas fields, wind power generation, electrician electric power insulation, bulletproof and anti-explosion area, mechanical electric appliances and buildings.

Description

technical field [0001] The invention relates to a preparation method of a polymer-based composite material, in particular to a preparation method of a fiber-reinforced airgel-polymer composite material. Background technique [0002] Polymer matrix composites are usually fiber-reinforced materials based on organic polymers. Polymers can be classified into resins and rubbers according to their uses, and thermoplastic and thermosetting polymers according to their thermal behavior. Among them, thermosetting resins include unsaturated polyester, vinyl ester, epoxy, phenolic, bismaleimide (BMI), polyimide resin, etc., and thermoplastic resins such as polypropylene (PP), polycarbonate (PC ), nylon (NYLON), polyether ether ketone (PEEK), polyether sulfone (PES), etc. The fiber reinforced materials of composite materials mainly include glass fiber, carbon fiber, boron fiber, aramid fiber, ultra-high molecular weight polyethylene fiber, silicon carbide fiber, asbestos fiber, whisker...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08L61/06C08L81/06C08L93/04C08L25/06C08K7/06C08K3/36C08K3/22C08K7/10C08K7/14
CPCC08K3/36C08K7/14C08K2003/2241C08K2201/001C08K2201/003C08L61/06C08L63/00C08L2201/02C08L2201/08C08L2205/03C08L67/06C08L81/06C08L93/04C08K7/06C08L25/06C08K7/10C08K2003/2244
Inventor 金承黎
Owner 浙江圣润纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap