Manganese-rich slow-release compound fertilizer
A slow-release compound fertilizer and manganese-enriched technology, applied in the agricultural field, can solve the problems of poor lodging resistance, insufficient grain, and reduced yield, and achieve the effects of less side components, convenient storage and application, and improved utilization.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] Example 1 Preparation of superabsorbent resin
[0031] A superabsorbent resin for manganese-rich slow-release compound fertilizer, the preparation method of which is:
[0032] Polyethylene glycol dimethacrylate is dissolved in water, the amount of water used for 1.2g polyethylene glycol dimethacrylate is 20.0ml, ammonium persulfate is dissolved in water, and the amount of water used for every 0.4g ammonium persulfate is 12.0ml, put 30g acrylic acid monomer and 20g 2-acrylamido-2-methylpropanesulfonic acid monomer into the reactor, add the previously prepared polyethylene glycol dimethacrylate aqueous solution and ammonium persulfate aqueous solution Also added to the reactor, heated to 70°C in a water bath for 6 hours to generate a transparent elastic substance, the transparent elastic substance was taken out from the reactor, cut into pieces, dried at 70°C for 7 hours, and stored after cooling. Can.
Embodiment 2
[0034] A manganese-rich slow-release compound fertilizer, made from the following raw materials in parts by weight: 31 parts of brown manganese ore, 27 parts of manganese ore, 21 parts of pyrolusite, 15 parts of manganese chloride, 12 parts of manganese sulfate, 54 parts of calcium nitrate, phosphoric acid 41 parts of potassium dihydrogen, 6 parts of white bark, 7 parts of masson pine bark, 3 parts of drunken michelia leaves, 5 parts of acacia leaves, 26 parts of rape straw, 20 parts of manure, 2 parts of brown sugar powder, 7 parts of banana peel part, 0.6 part of composite microorganism and 2 parts of superabsorbent resin prepared in Example 1. Wherein, the composite microorganisms are composed of microorganisms in the following weight ratios: Streptomyces costa Rica: Paecilomyces lilacinus: Stemoborbium azurite = 3:6:5, and the microorganisms have been activated and are directly used for fermentation.
[0035] The present invention also provides a preparation method of the ...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com