Coating with high adhesion, high mechanical strength, high temperature resistance and anti-corrosion

A technology with strong mechanical strength and strong adhesion, applied in the direction of anti-corrosion coatings, fire-proof coatings, wax coatings, etc., can solve the problems of unsatisfactory economic benefits for users, high production costs of coatings, complicated production processes, etc., and achieve excellent anti-corrosion and moisture-proof performance. The effect of low cost and low production cost

Inactive Publication Date: 2017-09-19
李壮
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are many types of coatings on the market, but with the increase of people's functional requirements for coatings, the existing coatings are not strong in fire resistance, poor in seepage resistance, and poor in crack resistance. and other losses, and the production cost of the coating is high, the production process is complicated, and it is easy to fall off after long-term use, which cannot meet the economic benefits of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A paint with strong adhesion, high mechanical strength, high temperature resistance and anticorrosion, which is prepared by weight parts of the following components: 3-7 parts of silsesquioxane compound, 15-18 parts of dimethyldichlorosilane, 12-14 parts of p-phenylenediamine, 10-15 parts of oxalic acid polyester, 30-50 parts of Portland cement, 10-15 parts of titanium dioxide, 2-5 parts of dispersant, 5-10 parts of talc , 25-35 parts of linseed oil, 30-45 parts of asphalt, 5-15 parts of refined asbestos, 15-20 parts of mixture of chlorinated paraffin and antimony oxide, 2-8 parts of ceramic sand with particle size of 2-8mm, water 30 -40 servings.

[0016] The dispersant is sodium hexametaphosphate. In the mixture of chlorinated paraffin and antimony oxide, the weight ratio of chlorinated paraffin to antimony oxide is 10-18 parts: 5-13 parts, and it also contains 18-25 parts by weight of coagulant.

Embodiment 2

[0018] A paint with strong adhesion, high mechanical strength, high temperature resistance and anticorrosion, which is prepared from the following components in parts by weight: 3 parts of silsesquioxane compound, 15 parts of dimethyldichlorosilane, and p-phenylene 12 parts of diamine, 10 parts of oxalic acid polyester, 30 parts of Portland cement, 10 parts of titanium dioxide, 2 parts of dispersant, 5 parts of talc, 25 parts of linseed oil, 30 parts of asphalt, 5 parts of fine asbestos, 15 parts of a mixture of chlorinated paraffin and antimony oxide, 2 parts of ceramic sand with a particle size of 2-8mm, and 30 parts of water.

[0019] The dispersant is sodium hexametaphosphate. In the mixture of chlorinated paraffin and antimony oxide, the weight ratio of chlorinated paraffin to antimony oxide is 10-18 parts: 5 parts, and it also contains 18 parts by weight of coagulant.

Embodiment 3

[0021] A paint with strong adhesion, high mechanical strength, high temperature resistance and anticorrosion, which is prepared by weight parts of the following components: 7 parts of silsesquioxane compound, 18 parts of dimethyldichlorosilane, and p-phenylene 14 parts of diamine, 15 parts of oxalic acid polyester, 50 parts of Portland cement, 15 parts of titanium dioxide, 5 parts of dispersant, 10 parts of talc, 35 parts of linseed oil, 45 parts of asphalt, 15 parts of fine asbestos, 20 parts of a mixture of chlorinated paraffin and antimony oxide, 8 parts of ceramic sand with a particle size of 2-8mm, and 40 parts of water.

[0022] The dispersant is sodium hexametaphosphate. In the mixture of chlorinated paraffin and antimony oxide, the weight ratio of chlorinated paraffin to antimony oxide is 18 parts: 13 parts, and it also contains 25 parts by weight of coagulant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a coating with strong adhesion, high mechanical strength, high temperature resistance and anticorrosion, which belongs to the technical field of building materials. Prepared from the following components by weight: 3-7 parts of silsesquioxane compound, 15-18 parts of dimethyldichlorosilane, 12-14 parts of p-phenylenediamine, oxalic acid polyester 10-15 parts, 30-50 parts of Portland cement, 10-15 parts of titanium dioxide, 2-5 parts of dispersant, 5-10 parts of talcum powder, 25-35 parts of linseed oil, 30-45 parts of asphalt, fine fine 5-15 parts of asbestos, 15-20 parts of a mixture of chlorinated paraffin and antimony oxide, 2-8 parts of pottery sand with a particle size of 2-8mm, and 30-40 parts of water. The invention has the beneficial effects of strong adhesion, high mechanical strength, good high temperature resistance, excellent anti-corrosion and moisture-proof performance, fast drying speed at low temperature and good storage stability.

Description

Technical field [0001] The invention relates to a component of a building material, in particular to a paint with strong adhesion, high mechanical strength, high temperature resistance and anticorrosion, and belongs to the technical field of building materials. Background technique [0002] Paint is a kind of chemical mixture paint that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. Paint is made of iron oxide or resin and other raw materials to decorate and protect objects. [0003] There are many kinds of coatings on the market, but with the increase of people's functional requirements for coatings, the existing coatings are not strong in fire resistance, poor in seepage resistance, and poor in anti-cracking effect, which are difficult to make up for in case of fire. In addition, the paint production cost is relatively high, the production process is complicated, and it is easy to fall off after long-term use, which cannot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D191/00C09D191/06C09D7/12C09D5/08C09D5/18
CPCC09D191/00C08L2201/02C08L2205/025C08L2205/035C09D5/08C09D5/18
Inventor 李壮
Owner 李壮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com