Color glass wall brick and production process thereof

A technology for colored glass and production process, applied in glass production and other directions, can solve the problems of low compressive strength of colored glass wall tiles, low utilization rate of waste broken glass, etc., and achieve adjustable crushing fineness and low power consumption. , the effect of high crushing efficiency

Inactive Publication Date: 2017-10-03
HEFEI LIYUTAI GLASS PROD CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the utilization rate of waste cullet is very low and the compressive strength of the prepared colored glass wall bricks is not high in the existing production process of colored glass wall bricks, the purpose of the present invention is to provide a colored glass wall brick Body brick and its production process, the prepared colored glass wall brick has the advantages of energy saving, environmental protection and high compressive strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A colored glass wall brick, comprising the following raw materials in parts by weight: 80 parts of waste glass, 5 parts of fluorite, 2 parts of potassium feldspar, 2 parts of anorthite, 2.5 parts of soda ash, 4 parts of dolomite and 0.3 parts of coloring agent share.

[0031] The colored glass wall brick also includes 3 parts by weight of kaolin, which is rich in alumina and silicon dioxide.

[0032] The colorant is an oxide of chromium, copper, manganese or cobalt, which can make the glass stained stably.

[0033] A production process of colored glass wall bricks, comprising the following steps:

[0034] (1) take raw materials according to the parts by weight of colored glass wall bricks;

[0035] (2) Sieve the waste glass after pulverizing first, then sort the waste glass after the sieving to remove impurities, and then wash it with water;

[0036] (3) Mix and pulverize fluorite, potassium feldspar, anorthite and dolomite to obtain a pulverized mixture;

[0037] (...

Embodiment 2

[0045] A colored glass wall brick, comprising the following raw materials in parts by weight: 75 parts of waste glass, 4 parts of fluorspar, 1 part of potassium feldspar, 1 part of anorthite, 2 parts of soda ash, 1 part of dolomite and 0.2 parts of coloring agent share.

[0046] The colored glass wall brick also includes 2 parts by weight of kaolin, which is rich in alumina and silicon dioxide.

[0047] The colorant is an oxide of chromium, copper, manganese or cobalt, which can make the glass stained stably.

[0048] A production process of colored glass wall bricks, comprising the following steps:

[0049] (1) take raw materials according to the parts by weight of colored glass wall bricks;

[0050] (2) Sieve the waste glass after pulverizing first, then sort the waste glass after the sieving to remove impurities, and then wash it with water;

[0051] (3) Mix and pulverize fluorite, potassium feldspar, anorthite and dolomite to obtain a pulverized mixture;

[0052] (4) m...

Embodiment 3

[0060] A colored glass wall brick, comprising the following raw materials in parts by weight: 85 parts of waste glass, 6 parts of fluorite, 3 parts of potassium feldspar, 3 parts of anorthite, 5 parts of soda ash, 7 parts of dolomite and 0.4 parts of colorant share.

[0061] The colored glass wall brick also includes 4 parts by weight of kaolin, which is rich in alumina and silica.

[0062] The colorant is an oxide of chromium, copper, manganese or cobalt, which can make the glass stained stably.

[0063] A production process of colored glass wall bricks, comprising the following steps:

[0064] (1) take raw materials according to the parts by weight of colored glass wall bricks;

[0065] (2) Sieve the waste glass after pulverizing first, then sort the waste glass after the sieving to remove impurities, and then wash it with water;

[0066] (3) Mix and pulverize fluorite, potassium feldspar, anorthite and dolomite to obtain a pulverized mixture;

[0067] (4) mix the waste gl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a color glass wall brick and a production process thereof, and relates to the technical field of glass production. The color glass wall brick is prepared from the following raw materials in parts by weight: 75 to 85 parts of waste and old glass, 4 to 6 parts of fluorite, 1 to 3 parts of potassium feldspar, 1 to 3 parts of anorthite, 2 to 5 parts of sodium carbonate, 1 to 7 parts of dolomite and 0.2 to 0.4 part of coloring agents. The production process comprises the following steps of (1) raw material weighing; (2) smashing; (3) mixing; (4) smelting; (5) pressing formation; (6) annealing cooling. The color glass wall brick and the production process thereof disclosed by the invention solve the problems that in the production process of the existing color glass wall brick, the utilization rate of waste and old broken glass is very low, and the compressive strength of the prepared color glass wall brick is low.

Description

technical field [0001] The invention belongs to the technical field of glass production, and in particular relates to a colored glass wall brick and a production process thereof. Background technique [0002] In China, more than 12 million tons of waste cullet are not used in scientific and high-end recycled products every year. Most of the waste cullets are low-end and low-quality recycled products, which are usually discarded or buried deep in various types of garbage as solid waste, which not only causes serious environmental pollution, but also wastes precious glass resources. [0003] Existing glass, such as flat glass, daily-use glass, decorative glass, electronic glass, automotive glass, etc., can be described as diverse in variety and complicated in style. But no matter which kind of glass is inseparable from the most basic glass production process, that is to say, any kind of glass in the world must go through batching, mixing various raw materials into batching ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C6/06C03C6/02C03C1/04C03C1/10C03B1/00
CPCC03B1/00C03C1/002C03C1/04C03C1/10Y02P40/50
Inventor 武娟
Owner HEFEI LIYUTAI GLASS PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com