Durable PVC (polyvinyl chloride) bionic bait

A bionic bait and durable technology, applied in the field of durable PVC bionic bait, can solve the problems of environmental pollution, performance degradation, short life, etc., achieve high recycling rate, excellent extraction resistance, and improve service life

Inactive Publication Date: 2017-10-10
界首市汇珠渔具有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use rate of bionic bait is high in developed cities. Bionic bait is more popular abroad. Many people in foreign countries pay more attention to environmental protection. Traditional domestic bait pollutes the environment. In recent years, people's awareness of environmental protection has gradually improved. The use of bionic bait The development will have broad prospects. Most of the existing bionic baits have a service life of half a year to one year. Often after high temperature in summer and low temperature in winter, the performance is greatly reduced, and the problem of short life still exists, and the pollution produced is relatively serious.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Durable PVC (polyvinyl chloride) bionic bait

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A durable PVC bionic bait is made of the following components in parts by weight: 70 parts of polyvinyl chloride, 15 parts of dihexyl phthalate, 7.5 parts of dibutyl sebacate, 7.5 parts of epoxy soybean oil, Trityl phosphate 5.5 parts, citrate 3.5 parts, glycol fatty acid ester 2.5 parts, dipentaerythritol ester 2.0 parts, glycol benzoate 1.5 parts, zinc stearate 1.3 parts, calcium stearate 1.1 part, 1.0 part of calcium lime powder, 2.0 parts of talcum powder, 0.3 part of aluminate coupling agent, 0.2 part of titanium dioxide, 0.1 part of antibacterial agent, and its preparation method comprises the following steps:

[0015] (1) Polyvinyl chloride, dihexyl phthalate, dibutyl sebacate, epoxidized soybean oil, trityl phosphate, citrate, glycol fatty acid ester, dipentaerythritol ester, di Add the polyalcohol benzoate into the high-speed mixer, mix for 3 minutes, add the remaining ingredients and mix for 4 minutes;

[0016] (2) Extrude the mixed and masticated material th...

Embodiment 2

[0021] A durable PVC bionic fishing bait is made of the following components in parts by weight: 75 parts of polyvinyl chloride, 16 parts of dihexyl phthalate, 8.5 parts of dibutyl sebacate, 8.0 parts of epoxy soybean oil, Trityl phosphate 6.0 parts, citrate 4.0 parts, glycol fatty acid ester 2.7 parts, dipentaerythritol ester 2.3 parts, glycol benzoate 1.7 parts, zinc stearate 1.4 parts, calcium stearate 1.2 parts, 1.1 parts of calcium lime powder, 2.2 parts of talcum powder, 0.4 part of aluminate coupling agent, 0.3 part of titanium dioxide, 0.2 part of antibacterial agent, and its preparation method comprises the following steps:

[0022] (1) Polyvinyl chloride, dihexyl phthalate, dibutyl sebacate, epoxidized soybean oil, trityl phosphate, citrate, glycol fatty acid ester, dipentaerythritol ester, di Add the polyalcohol benzoate into the high-speed mixer, mix for 4 minutes, add the remaining ingredients and mix for 5 minutes;

[0023] (2) Extrude the mixed and masticated m...

Embodiment 3

[0028] A durable PVC bionic fishing bait is made of the following components in parts by weight: 80 parts of polyvinyl chloride, 17 parts of dihexyl phthalate, 9.5 parts of dibutyl sebacate, 8.5 parts of epoxy soybean oil, Trityl phosphate 6.5 parts, citrate 4.5 parts, glycol fatty acid ester 3.0 parts, dipentaerythritol ester 2.5 parts, glycol benzoate 2.0 parts, zinc stearate 1.5 parts, calcium stearate 1.3 parts, 1.2 parts of calcium lime powder, 2.5 parts of talcum powder, 0.5 part of aluminate coupling agent, 0.4 part of titanium dioxide, 0.3 part of antibacterial agent, and its preparation method comprises the following steps:

[0029] (1) Polyvinyl chloride, dihexyl phthalate, dibutyl sebacate, epoxidized soybean oil, trityl phosphate, citrate, glycol fatty acid ester, dipentaerythritol ester, di Add the polyalcohol benzoate into the high-speed mixer, mix for 5 minutes, add the remaining ingredients and mix for 6 minutes;

[0030] (2) Extrude the mixed and masticated m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of research, development and processing of fishing gear and discloses durable PVC (polyvinyl chloride) bionic bait. The bait is prepared from the components as follows: PVC, DHP (dihexyl phthalate), dibutyl sebacate, epoxidized soybean oil, tricresyl phosphate, citrate, diol fatty acid ester, dipentaerythritol, diol benzoate, zinc stearate, calcium stearate, ash calcium powder, talcum powder, an aluminate coupling agent, titanium dioxide and an antibacterial agent, the PVC is used as the main material, the rest components are added to enhance the performance of PVC, the PVC has excellent low-temperature resistance, the brittle temperature of a product can be decreased to subzero 70 DEG C-subzero 30 DEG C, the low-temperature softness is better, the heat resistance and weather resistance are higher, the service life of the bionic bait can be prolonged, the recycling rate is high, and the used inorganic antibacterial agent can be dispersed uniformly in the biotic bait and can play the antibacterial role for a long term.

Description

technical field [0001] The invention belongs to the technical field of research and development and processing of fishing gear, and in particular relates to a durable PVC bionic fishing bait. Background technique [0002] The bionic bait is manufactured using the law of "big fish eat small fish". When it floats in the sea, other sea fish will think it is a small fish when they see it, and once they bite it, they will be fooled. The hooks on the bionic bait are professional and powerful. The use rate of bionic bait is high in developed cities. Bionic bait is more popular abroad. Many people in foreign countries pay more attention to environmental protection. Traditional domestic bait pollutes the environment. In recent years, people's awareness of environmental protection has gradually improved. The use of bionic bait The development will have broad prospects. Most of the existing bionic baits have a service life of half a year to one year. After the high temperature in summ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08K13/02C08K5/12C08K5/11C08K5/098C08K3/32C08K3/22C08K5/103C08K5/10
CPCC08L27/06C08K2003/2241C08K2003/328C08K2201/014C08L2201/08C08L91/00C08K13/02C08K5/12C08K5/11C08K5/098C08K3/32C08K3/22C08K5/103C08K5/10
Inventor 朱银忠
Owner 界首市汇珠渔具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap