Heat-insulation type concrete for civil construction and preparation method thereof

A technology of concrete and civil engineering, applied in the field of concrete, to achieve the effect of good waterproof, simple preparation, and improved anti-crack and anti-seepage performance

Inactive Publication Date: 2017-10-13
山东励仙电力工程有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of foamed concrete has the functions of light weight, waterproof, fire resistance, heat preservation, frost resistance, crack resistance and earthquake resistance, etc., and is especially suitable for engineering insulation layers in cold regions and underground engineering water blocking and earthquake resistance layers; but the performance of the invention can still be used. be further strengthened

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of thermal insulation concrete for civil engineering of the present embodiment includes the following raw materials in parts by weight:

[0029] 90 parts of cement, 20 parts of fly ash, 40 parts of fine sand, 10 parts of ceramsite, 5 parts of cast stone powder, 6 parts of zeolite powder, 60 parts of water, 1 part of fiber, 0.5 parts of waterproofing agent, 1 part of foaming agent, suspension 0.2 part of agent, 0.1 part of activator.

[0030] Preferably, the cement is ordinary portland cement, the particle size of the fine sand is 0.2 mm, the particle size of the ceramsite is 0.3 mm, and the mesh number of the cast stone powder and the zeolite powder is 100 mesh.

[0031] Preferably, the fibers are polypropylene fibers and glass fibers with a weight ratio of 3:1.

[0032] Preferably, the waterproofing agent is a mixture of ferric chloride, zirconia, paraffin, and rubber.

[0033] Preferably, the foaming agent is a mixture of calcium carbonate, water glass, sodiu...

Embodiment 2

[0043] A kind of thermal insulation concrete for civil engineering, comprising the following raw materials in parts by weight:

[0044] 95 parts of cement, 23 parts of fly ash, 45 parts of fine sand, 15 parts of ceramsite, 6 parts of cast stone powder, 8 parts of zeolite powder, 65 parts of water, 1.5 parts of fiber, 0.8 parts of waterproofing agent, 2 parts of foaming agent, suspension 0.6 parts of agent, 0.15 parts of activator.

[0045] Preferably, the cement is ordinary portland cement, the particle size of the fine sand is 0.25 mm, the particle size of the ceramsite is 0.4 mm, and the mesh numbers of the cast stone powder and the zeolite powder are 200 mesh.

[0046] Preferably, the fibers are polypropylene fibers and glass fibers with a weight ratio of 3:1.

[0047] Preferably, the waterproofing agent is a mixture of ferric chloride, zirconia, paraffin, and rubber.

[0048] Preferably, the foaming agent is a mixture of calcium carbonate, water glass, sodium dodecylbenz...

Embodiment 3

[0058] A kind of thermal insulation concrete for civil engineering, comprising the following raw materials in parts by weight:

[0059] 100 parts of cement, 25 parts of fly ash, 50 parts of fine sand, 20 parts of ceramsite, 8 parts of cast stone powder, 9 parts of zeolite powder, 70 parts of water, 2 parts of fiber, 1 part of waterproofing agent, 3 parts of foaming agent, suspension 0.8 parts of agent, 0.2 parts of activator.

[0060] Preferably, the cement is ordinary Portland cement, the particle size of the fine sand is 0.3 mm, the particle size of the ceramsite is 0.5 mm, and the mesh numbers of the cast stone powder and the zeolite powder are 200 mesh.

[0061] Preferably, the fibers are polypropylene fibers and glass fibers with a weight ratio of 3:1.

[0062] Preferably, the waterproofing agent is a mixture of ferric chloride, zirconia, paraffin, and rubber.

[0063] Preferably, the foaming agent is a mixture of calcium carbonate, water glass, sodium dodecylbenzenesul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses heat-insulation type concrete for civil construction and belongs to the technical field of concrete. The heat-insulation type concrete is prepared from the following raw materials in parts by weight: 90 to 100 parts of cement, 20 to 25 parts of fly ash, 40 to 50 parts of fine sand, 10 to 20 parts of ceramsite, 5 to 8 parts of cast stone powder, 6 to 9 parts of zeolite powder, 60 to 70 parts of water, 1 to 2 parts of fiber, 0.5 to 1 part of a waterproof agent, 1 to 3 parts of a de-foaming agent, 0.2 to 0.8 part of a suspension agent and 0.1 to 0.2 part of an activating agent. The invention further discloses a preparation method of the heat-insulation type concrete for the civil construction. The heat-insulation type concrete for the civil construction is simple to prepare and has relatively excellent waterproof, fireproof and heat-insulation capabilities.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a thermal insulation concrete for civil engineering and a preparation method thereof. Background technique [0002] Thermal insulation concrete, also known as aerated concrete, foam concrete, and foamed concrete, belongs to the category of thermal insulation materials. It covers the surface of thermal equipment and pipelines, which can prevent or reduce heat exchange with the outside world and reduce heat dissipation. Special concrete with certain physical and mechanical properties. [0003] Insulation concrete is made of foam by mechanical means, and then the foam is mixed into the mixture composed of siliceous materials, calcium materials, etc. Specifications, cured lightweight concrete with a large number of closed pores. Foam concrete has a large number of closed small pores, which has good thermal insulation performance and can be used as wall thermal insulation material....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/10C04B111/27C04B111/28
CPCC04B28/04C04B2111/27C04B2111/28C04B18/08C04B14/06C04B18/027C04B14/04C04B14/047C04B14/42C04B16/0633C04B22/12C04B22/06C04B24/36C04B24/24C04B22/10C04B12/04C04B24/20C04B24/10C04B24/08C04B24/003C04B24/00C04B22/126C04B22/147C04B22/124C04B22/149C04B22/00C04B38/10
Inventor 伍文慧
Owner 山东励仙电力工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com