A technology of coating material and production process, which is applied in the field of environment-friendly interior wall coating material and its production process, can solve the problems of narrow use, achieve the effects of reducing heat loss, simple production process, and cool and comfortable texture

Inactive Publication Date: 2017-10-13
合肥永泰新型建材有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among the existing diatomite products, most of them only use the advantages of diatomite itself, and often have relatively simple functions and narrow uses.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly inner wall coating material and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An environment-friendly interior wall coating material, including the following raw materials: 225g of diatomite, 120g of bentonite, 50g of sepiolite, 52g of calcined kaolin, 28g of calcium hydroxide powder, 14g of bamboo charcoal fiber, 6g of polyester fiber, perboric acid Sodium 2.6g, nanometer zinc oxide 4g, calcium perborate 0.6g, dispersant sodium hexametaphosphate 0.4g, wetting agent Dynol 960 1g, defoamer polydimethylsiloxane 0.2g.

[0032] The production process of the above-mentioned environment-friendly interior wall coating material comprises the following steps:

[0033] (1) After natural drying, weathering and crushing of diatomite, soak in deionized water for 30-40 minutes, centrifuge for 5-10 minutes, filter with 20-40 mesh filter cloth, and dry the filtrate at 50-60°C for 6 ~8 hours to obtain purified diatomaceous earth, the moisture content is kept below 5%;

[0034] (2) Mix the purified diatomite, calcined kaolin, calcium hydroxide powder, bamboo char...

Embodiment 2

[0037] An environment-friendly interior wall coating material, comprising the following raw materials: 230g of diatomite, 124g of bentonite, 36g of sepiolite, 44g of calcined kaolin, 30g of calcium hydroxide powder, 12g of bamboo charcoal fiber, 10g of polyester fiber, perboric acid Sodium 3.2g, nano-zinc oxide 4g, calcium perborate 1g, dispersant PEG400 0.8g, wetting agent Dynol 980 1.4g, defoamer polyoxyethylene polyoxypropanolamine ether 0.4g.

[0038] The production process of the above-mentioned environment-friendly interior wall coating material comprises the following steps:

[0039] (1) After natural drying, weathering and crushing of diatomite, soak in deionized water for 30-40 minutes, centrifuge for 5-10 minutes, filter with 20-40 mesh filter cloth, and dry the filtrate at 50-60°C for 6 ~8 hours to obtain purified diatomaceous earth, the moisture content is kept below 5%;

[0040] (2) Mix the purified diatomite, calcined kaolin, calcium hydroxide powder, bamboo cha...

Embodiment 3

[0043] An environment-friendly interior wall coating material, comprising the following raw materials: 218g of diatomite, 127g of bentonite, 50g of sepiolite, 52g of calcined kaolin, 28g of calcium hydroxide powder, 16g of bamboo charcoal fiber, 10g of polyester fiber, perboric acid Sodium 3g, nano zinc oxide 6g, calcium perborate 0.4g, dispersant 5040 0.6g, wetting agent Dynol 960 1.2g, defoamer polyoxypropylene glyceryl ether 0.6g.

[0044] The production process of the above-mentioned environment-friendly interior wall coating material comprises the following steps:

[0045] (1) After natural drying, weathering and crushing of diatomite, soak in deionized water for 30-40 minutes, centrifuge for 5-10 minutes, filter with 20-40 mesh filter cloth, and dry the filtrate at 50-60°C for 6 ~8 hours to obtain purified diatomaceous earth, the moisture content is kept below 5%;

[0046] (2) Mix the purified diatomite, calcined kaolin, calcium hydroxide powder, bamboo charcoal fiber and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly inner wall coating material and a production process thereof. The coating material is prepared form the following raw materials in parts by weight: 100 to 120 parts of diatomite, 50 to 70 parts of bentonite clay, 15 to 30 parts of meerschaum, 20 to 30 parts of calcined kaolin, 8 to 20 parts of calcium hydroxide powder, 5 to 10 parts of bamboo carbon fibers, 1 to 5 parts of polyester fibers, 0.6 to 2 parts of sodium perborate, 1 to 3 parts of nano zinc oxide, 0.2 to 0.6 part of calcium perborate, 0.1 to 0.5 part of dispersant, 0.2 to 0.8 part of wetting agent, and 0.1 to 0.3 part of anti-foaming agent. The production process of the coating material comprises the following steps: purifying the diatomite, mixing the diatomite, and carrying out ball-milling on the diatomite. According to the environment-friendly inner wall coating material disclosed by the invention, all components are safe and environment-friendly, heat insulation and flame retardance performance are excellent, and the inner wall coating material is antibacterial and bacteriostatic, water-proof, mildew-proof and corrosion-resistant; the production process is simple, is saving in energy sources, and is suitable for massive production.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an environment-friendly interior wall coating material and a production process thereof. Background technique [0002] With the development of society and the improvement of living standards, people's awareness of environmental protection and health has been significantly enhanced, and the requirements for the comfort and safety of the living environment are getting higher and higher. Indoor temperature, air relative humidity, and air quality are important environmental parameters for living comfort. Diatom mud is an indoor coating material based on diatomaceous earth, which is a single-celled aquatic plankton that lived millions of years ago. The main component of diatomite is protein, which is light, soft and porous, with a porosity of more than 90% and a specific surface area of ​​65m2. 2 / g, which determines its strong physical adsorption performance and ion exch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/02C04B111/28C04B111/27C04B111/20
CPCC04B30/02C04B2111/00482C04B2111/20C04B2111/2092C04B2111/27C04B2111/28C04B2201/20C04B2201/32C04B14/08C04B14/104C04B14/042C04B14/106C04B22/064C04B14/386C04B16/0683C04B22/0013C04B22/06C04B22/16C04B24/42C04B2103/0068C04B2103/408C04B24/32
Inventor 伍志远
Owner 合肥永泰新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap