Carbon fiber-polyether urethane as well as preparation method and application thereof

A technology of polyether polyurethane and carbon fiber, which is applied in the field of materials, can solve the problems of single functionality of fiber fabrics, and achieve the effects of ensuring skin-friendly comfort, increasing service life, and convenient cleaning

Inactive Publication Date: 2017-12-12
宋宏婷
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the fiber fabrics in the prior art have relatively single functionality, and cannot satisfy the wearing comfort of the human body while having a good UV protection function.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] An anti-ultraviolet fabric comprising a blended layer consisting of 16.3% chitosan fibers, 19.7% graphene viscose composite fibers and 64% cotton fibers.

[0046] The upper surface of the blended layer is covered with a carbon fiber-polyether polyurethane layer, the lower surface of the blended layer is covered with a crotonate-grafted starch layer, and the thickness of the carbon fiber-polyether polyurethane layer is 400 μm. The thickness of the blended layer is 0.2 cm, and the thickness of the crotonate-grafted starch layer is 600 μm.

[0047] The carbon fiber-polyether polyurethane layer is sprayed on the upper surface of the blended layer after melting the carbon fiber-polyether polyurethane at high temperature, and the crotonate-grafted starch layer is sprayed on the surface after melting the crotonate-grafted starch at high temperature. Blend layer lower surface.

[0048] The blended layer is formed by weaving cotton fibers, chitosan fibers and graphene viscose c...

Embodiment 2

[0050] A kind of anti-ultraviolet fabric of the present invention, wherein cotton fiber is through pretreatment, and the step of pretreatment is,

[0051] Step 1: Take 2.0 mL of 0.1 mol / L citric acid and 18.0 mL of 0.1 mol / L sodium citrate to prepare a citric acid-sodium citrate buffer solution with a pH of 6.4;

[0052] Step 2: soak the cotton fiber completely in the buffer solution, add hydroxycarboxylic acid to the buffer solution according to the mass ratio of cotton fiber: hydroxycarboxylic acid 1:0.04, and add hydroxycarboxylic acid to the buffer solution according to the mass ratio of cotton fiber: carboxylic acid betaine 1:0.08 Add carboxylate betaine to the solution and soak for 30 minutes;

[0053] Step 4: Add pectinase and cellulase to the buffer according to the mass ratio of cotton fiber: pectinase: cellulase 1:0.05:0.02, heat the water bath to 27°C, stir at constant temperature for 5 minutes, and then add cotton fiber: fat Add lipase to the buffer solution at an...

Embodiment 3

[0057] A kind of anti-ultraviolet fabric of the present invention, graphene viscose composite fiber is prepared by following steps,

[0058] Step 1: Add graphite powder and sodium nitrate to the concentrated sulfuric acid at the mass ratio of concentrated sulfuric acid: graphite powder: sodium nitrate 65:1:0.6 in an ice bath, stir and dissolve for 30 minutes, and then add graphite powder: potassium permanganate according to the mass ratio of graphite powder: potassium permanganate Ratio 1:5, add potassium permanganate to the mixed solution, stir for 10 hours, add deionized water to the mixed solution according to the volume ratio of concentrated sulfuric acid: deionized water 1:1, and place the mixture under the condition of a vacuum degree of 0.93 Slowly raise the temperature to 52°C at a rate of 1.2°C / h, keep stirring at a constant temperature of 52°C for 22 hours, then add hydrogen peroxide to the mixed solution according to the volume ratio of concentrated sulfuric acid to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a material, and particularly provides carbon fiber-polyether urethane as well as a preparation method and application thereof. The carbon fiber-polyether urethane provided by the invention has high heat resistance, high elasticity, high tenacity and abrasive resistance and can be applied to fabric, the performance of the fabric is improved, and simultaneously, the combination degree among the raw materials of fabric is increased.

Description

[0001] This application is a divisional application titled "An Anti-ultraviolet Fabric" [0002] The filing date of the original application is: 2015-12-07 [0003] The application number of the original application is: 2015108834059. technical field [0004] The invention relates to materials, especially a carbon fiber-polyether polyurethane and its preparation method and application. Background technique [0005] With the development of technology and the continuous progress of society, while people's living standards have been greatly improved, people's requirements for quality of life are also getting higher and higher. Today, when the global environment is destroyed, returning to nature and returning to nature has become a measure of people's quality of life. Important standards, wearing energy-saving and environmentally friendly fiber products is the fashion pursuit of people today. With the development of high technology, the development of new textile fiber raw mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/76C08G18/48C08G18/10C08G18/32C08K9/06C08K7/06D06M15/568D06M15/263D06M13/207D06M13/463D06M16/00D06M11/61D01F2/08C08F251/00C08F220/04D06M101/10D06M101/06
CPCC08F251/00C08G18/10C08G18/4854C08G18/7671C08K7/06C08K9/06D01F2/08D06M11/61D06M13/207D06M13/463D06M15/263D06M15/568D06M16/003D06M2101/06D06M2101/10D06M2200/25D06M2200/30C08G18/3206C08F220/04
Inventor 宋宏婷
Owner 宋宏婷
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com