Acid and alkali resistant metal powder coating and preparation method thereof

A metal powder, acid and alkali resistant technology, applied in powder coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve the problems of large differences in quality and poor consistency of metal powder coatings, and achieve protection from acid and alkali corrosion, reduce Interfering factors, effect of particle uniformity

Active Publication Date: 2017-12-12
ZHANGJIAGANG JIANGNAN POWDER COATING
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Using a bonding machine to bond powder coatings and metallic pigments is a relatively good method for preparing metal powder coatings. In the current preparation method, ingredients are often added manually, resulting in a large difference in the quality of the produced metal powder coatings. , poor consistency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acid and alkali resistant metal powder coating and preparation method thereof
  • Acid and alkali resistant metal powder coating and preparation method thereof
  • Acid and alkali resistant metal powder coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Produce a kind of acid and alkali resistant metal powder coating, its specific steps are as follows:

[0049] a. Weigh the raw materials and prepare the following raw materials in parts by mass:

[0050] Bisphenol A epoxy resin 35kg;

[0051] Hydroxy acrylic resin 25kg;

[0052] Phenolic resin 15kg;

[0053] 2-methylimidazole 2kg;

[0054] Aluminum silver powder 9kg;

[0055] Sand texture agent 2kg;

[0056] Titanium dioxide 16kg;

[0057] Calcium carbonate 12kg;

[0058] Benzoin 0.5kg;

[0059] White carbon black 0.4kg;

[0060] b. Add the bisphenol A epoxy resin, hydroxyacrylic resin, 2-methylimidazole, sanding agent, titanium dioxide, calcium carbonate and benzoin prepared in step a into the Misekra tank of the mixer for pre-mixing , the mixing time is: 2 minutes at low speed, 6 minutes at high speed; 100r / min at low speed and 300r / min at high speed;

[0061] c, the phenolic resin prepared in step a is added in the resin breaker and carried out micro-grindi...

Embodiment 2

[0072] Produce a kind of acid and alkali resistant metal powder coating, its specific steps are as follows:

[0073] a. Weigh the raw materials and prepare the following raw materials in parts by mass:

[0074] Bisphenol A type epoxy resin 40kg;

[0075] Hydroxy acrylic resin 30kg;

[0076] Phenolic resin 18kg;

[0077] 2-methylimidazole 3.6kg;

[0078] Aluminum silver powder 10.6kg;

[0079] Sand texture agent 2kg;

[0080] Titanium dioxide 16.8kg;

[0081] Calcium carbonate 13.2kg;

[0082] Benzoin 0.5kg;

[0083] White carbon black 0.4kg;

[0084] b. Add the bisphenol A epoxy resin, hydroxyacrylic resin, 2-methylimidazole, sanding agent, titanium dioxide, calcium carbonate and benzoin prepared in step a into the Misekra tank of the mixer for pre-mixing , the mixing time is: 2 minutes at low speed, 6 minutes at high speed; 100r / min at low speed and 300r / min at high speed;

[0085] c, the phenolic resin prepared in step a is added in the resin breaker and carried ou...

Embodiment 3

[0096] Produce a kind of acid and alkali resistant metal powder coating, its specific steps are as follows:

[0097] a. Weigh the raw materials and prepare the following raw materials in parts by mass:

[0098] Bisphenol A epoxy resin 45kg;

[0099] Hydroxy acrylic resin 35kg;

[0100] Phenolic resin 20kg;

[0101] 2-Methylimidazole 4kg;

[0102] Aluminum silver powder 12kg;

[0103] Sand texture agent 2kg;

[0104] Titanium dioxide 18kg;

[0105] Calcium carbonate 14kg;

[0106] Benzoin 0.5kg;

[0107] White carbon black 0.4kg;

[0108] b. Add the bisphenol A epoxy resin, hydroxyacrylic resin, 2-methylimidazole, sanding agent, titanium dioxide, calcium carbonate and benzoin prepared in step a into the Misekra tank of the mixer for pre-mixing , the mixing time is: 2 minutes at low speed, 6 minutes at high speed; 100r / min at low speed and 300r / min at high speed;

[0109] c, the phenolic resin prepared in step a is added in the resin breaker and carried out micro-grind...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acid and alkali resistant metal powder coating and a preparation method thereof. The powder coating comprises the following used materials in parts by mass: 35-45 parts of bisphenol A epoxy resin, 25-35 parts of hydroxy acrylic resin, 15-20 parts of phenolic resin, 2-4 parts of 2-methylimidazole, 9-12 parts of aluminum-silver powder, 2 parts of a sand ripple agent, 16-18 parts of titanium dioxide, 12-14 parts of calcium carbonate, 0.5 part of benzoin and 0.4 part of white carbon black. The prepared powder material has excellent acid and alkali resistance, and due to usage of an automatic feed bonding machine in the preparation process, the obtained powder has high and stable quality.

Description

technical field [0001] The invention belongs to the technical field of powder coatings, in particular to an acid-alkali-resistant metal powder coating and a preparation method thereof. Background technique [0002] Powder coating is a new type of solvent-free, easy-to-operate, 100% solid powdered environmentally friendly coating. Powder coating has high utilization efficiency and is widely used in household appliances, automobiles, construction, petroleum and petrochemical industries. A variety of powder coatings for pigments, it can display a bright, luxurious decorative effect, ideal for spraying indoor and outdoor objects such as furniture, accessories and automobiles. Existing metal powder coatings are usually not resistant to acid and alkali corrosion, and tend to be blackened and damaged after contact with acid or alkali liquids. [0003] Using a bonding machine to bond powder coatings and metal pigments is a relatively good method for preparing metal powder coatings ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D133/00C09D5/03C09D5/10C09D7/12B01J19/00B01J19/18
CPCB01J19/0013B01J19/18B01J2219/00094C08K2003/0806C08K2003/0812C08K2003/2241C08K2003/265C08L2312/00C09D5/035C09D5/103C09D163/00C08L33/00C08K13/02C08K3/08C08K3/36C08K3/26C08K3/22
Inventor 黎永新田晖华鹤林陈传东
Owner ZHANGJIAGANG JIANGNAN POWDER COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap