Preparation method of organic silicon defoamer

A silicone defoamer and silicone oil technology, applied in separation methods, chemical instruments and methods, foam dispersion/prevention, etc., can solve problems such as delamination and defoamer instability, and achieve increased stability and acid resistance Alkaline properties, soothing strong hydrophobic and oleophobic effects

Active Publication Date: 2017-12-15
GUANGDONG REBON ADVANCED MATERIALS CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention: Aiming at the problem that the current defoamer simply mixes the silicone defoamer and the polyether defoamer, which easily leads to the instability of the defoamer and the occurrence of stratification, the present invention provides a The preparation method of organosilicon defoamer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] A preparation method of an organic silicon defoamer, the preparation method comprising the steps of:

[0020] (1) In parts by weight, take 80-90 parts of silicone oil, 30-35 parts of linolenic acid, 20-25 parts of methyl vinyl dichlorosilane, 8-11 parts of maleic anhydride, 4-7 parts of catalyst and 1 ~3 parts of additives, first put silicone oil, linolenic acid and additives into the reactor, use nitrogen protection, and preheat at 60~65°C for 30~35min;

[0021] (2) After preheating, add methylvinyldichlorosilane, maleic anhydride, and catalyst, heat up to 90-95°C for 2-4 hours, cool down, and collect the reaction mixture;

[0022] (3) According to the mass ratio of 8-11:3-5:13, put the reaction mixture, allyl polyoxyethylene ether and xylene into the reaction kettle, use sodium hydroxide solution to adjust the pH to 8.0-8.5, use Boost the pressure of carbon dioxide to 1.2~1.5MPa, stir at 80~95℃ for 1~3h:

[0023] (4) After stirring, add emulsifier and ammonium glycy...

example 1

[0025] The catalyst of choice is aluminum silicate.

[0026] The choice of additive is phosphomolybdic acid.

[0027] The choice of emulsifier is calcium stearoyl lactylate.

[0028] A preparation method of an organic silicon defoamer, the preparation method comprising the steps of:

[0029] (1) In parts by weight, take 85 parts of silicone oil, 33 parts of linolenic acid, 23 parts of methylvinyldichlorosilane, 10 parts of maleic anhydride, 5 parts of catalyst and 2 parts of additives, first mix the silicone oil, linolenic acid and Put the additive into the reactor, use nitrogen protection, and preheat at 63°C for 33min;

[0030] (2) After preheating, add methylvinyldichlorosilane, maleic anhydride, and catalyst, raise the temperature to 93°C for 3 hours, cool down, and collect the reaction mixture;

[0031] (3) According to the mass ratio of 9:4:13, put the reaction mixture, allyl polyoxyethylene ether and xylene into the reactor, use sodium hydroxide solution to adjust th...

example 2

[0034] The choice of catalyst is any one of aluminum silicate and Lewis acid.

[0035] The choice of additive is any one of titanium dioxide and phosphomolybdic acid.

[0036] The choice of emulsifier is any one in sodium stearoyl lactylate or calcium stearoyl lactylate.

[0037] A preparation method of an organic silicon defoamer, the preparation method comprising the steps of:

[0038] (1) In parts by weight, take 90 parts of silicone oil, 35 parts of linolenic acid, 25 parts of methylvinyldichlorosilane, 11 parts of maleic anhydride, 7 parts of catalyst and 3 parts of additives, first mix the silicone oil, linolenic acid and Put the additive into the reactor, use nitrogen protection, and preheat at 65°C for 35min;

[0039] (2) After preheating, add methylvinyldichlorosilane, maleic anhydride, and catalyst, heat up to 95°C for 4 hours, cool, and collect the reaction mixture;

[0040] (3) According to the mass ratio of 11:5:13, put the reaction mixture, allyl polyoxyethyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of chemical engineering and particularly relates to a preparation method of an organic silicon defoamer. The preparation method comprises the following steps: by taking silicone oil as a base material, modifying the silicone oil by using a methyl vinyl dichlorosilane monomer to increase silicon oxygen bonds in the silicone oil; then performing protection by using maleic anhydride to increase the acid and alkali resistance; and then performing a grafting reaction with allyl polyoxyethylene ether to form the polyether modified organic silicon defoamer. Under the action of ammonium glycyrrhetate, the hydrophobic and lipophobic properties of the defoamer are alleviated, the stability is enhanced, and a layering phenomenon of the defoamer is prevented.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, and in particular relates to a preparation method of an organosilicon defoamer. Background technique [0002] Defoamer is a widely used fine chemical, mainly used to eliminate and suppress various harmful foams. As a defoaming agent, it should have basic characteristics such as insoluble or insoluble in the foaming liquid, lower surface tension than the foaming liquid, certain affinity with the foaming liquid, no chemical reaction with the foaming liquid, and low volatility. . There are many types of defoamers, and those commonly used in industry can be roughly divided into three categories: organic defoamers (alcohols, lipids, amides, etc.), silicone defoamers and polyether defoamers. Among them, silicone and polyether defoamers are the most widely used and used in large amounts. Silicone defoamers have attracted widespread attention due to their insoluble properties, low surface te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D19/04
CPCB01D19/0409
Inventor 王秀凤刘芳尹凯欣
Owner GUANGDONG REBON ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com