Carbon-black-based water-based paint as well as preparation method and application thereof

A water-based, carbon black-based technology, applied in paper coatings, hyaluronic acid coatings, chitin polysaccharide coatings, etc., can solve the problems of prominent environmental pollution, complex production equipment, high production costs, etc., to achieve improved opacity and high production efficiency , The effect of low production energy consumption

Active Publication Date: 2017-12-22
ZHEJIANG XINFENG SPECIAL PAPER
View PDF11 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the Yuguo bag paper factory basically adopts the lamination method to produce the outer bag paper. The inner surface is black because the carbon black is dyed in the pulp. This not only complicates the production equipment, but also increases the production cost. Moreover, the loss of carbon black is serious and the environment is polluted. protrude

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Stir 384g of distilled water and 3g of sodium hexametaphosphate with a high-speed disperser at a speed of 1000r / min for 10min to dissolve the dispersant.

[0020] (2) Add 55g of kaolin, 20g of heavy calcium carbonate, 25g of carbon black in sequence, and add 0.5g of polyether defoamer, and continue stirring at a speed of 4000r / min for 15min to fully disperse the pigment.

[0021] (3) After the pigment is dispersed, add 20g of modified starch, 5g of carboxymethyl cellulose and 1g of modified chitosan, stir at a speed of 2000r / min for 5min, then add a certain amount of NaOH and stir at a low speed of 200r / min for 5min , adjust the pH of the solution to 10. After filtering, the finished mixture is obtained.

Embodiment 2

[0023] (1) Stir 384g of distilled water and 3g of sodium hexametaphosphate with a high-speed disperser at a speed of 1000r / min for 10min to dissolve the dispersant.

[0024] (2) Add 60g of kaolin, 20g of heavy calcium carbonate, 20g of carbon black in sequence, and add 0.5g of polyether defoamer, and continue stirring at a speed of 4000r / min for 15min to fully disperse the pigment.

[0025] (3) After the pigment is dispersed, add 20g of modified starch, 5g of carboxymethyl cellulose and 1g of modified chitosan, stir at a speed of 2000r / min for 5min, then add a certain amount of NaOH and stir at a low speed of 200r / min for 5min , adjust the pH of the solution to 10. After filtering, the finished mixture is obtained.

Embodiment 3

[0027] (1) Stir 384g of distilled water and 3g of sodium hexametaphosphate with a high-speed disperser at a speed of 1000r / min for 10min to dissolve the dispersant.

[0028] (2) Add 65g of kaolin, 20g of heavy calcium carbonate, 15g of carbon black, and 0.5g of polyether defoamer in sequence, and continue stirring at a speed of 4000r / min for 15min to fully disperse the pigment.

[0029] (3) After the pigment is dispersed, add 20g of modified starch, 5g of carboxymethyl cellulose and 1g of modified chitosan, stir at a speed of 2000r / min for 5min, then add a certain amount of NaOH and stir at a low speed of 200r / min for 5min , adjust the pH of the solution to 10. After filtering, the finished mixture is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to carbon-black-based water-based paint as well as a preparation method and application thereof. The carbon-black-based water-based paint uses carbon black, kaolin and calcium carbonate as pigments to be subjected to high-speed shearing dispersion for a certain time together with sodium hexametaphosphate dispersing agent solution and polyether type defoaming agents so as to prepare pigment water phase dispersion liquid; then, ingredients such as carboxymethyl cellulose, adhesive modification starch and antibacterial agent modification chitosan are added according to the specific programs; the carbon-black-based water-based paint is obtained through high-speed shearing dispersion. The carbon-black-based water-based paint is mainly applied to surface coating of fruit bearing bag outer bag paper; the process is simple; the production cost is low; the utilization rate of carbon black is improved; the cleanness and the environment protection of production workshops are facilitated.

Description

technical field [0001] The invention relates to the technical field of carbon black pigment and fruit-growing bag paper, in particular to a carbon black-based water-based coating and a preparation method thereof, which is mainly used for surface coating of fruit-growing bag paper. Background technique [0002] Carbon black is a kind of amorphous carbon, which is a product obtained by incomplete combustion or thermal decomposition of carbon-containing substances under the condition of insufficient air. Carbon black has excellent colorability, weather resistance and chemical stability, and is an indispensable ideal black pigment in the coatings industry. [0003] The carbon black paint involved in the present invention is mainly applied to the surface coating of fruit bag paper. Fruit bag paper is a kind of special paper used for fruit bagging during the growth period of fruit trees. It is a high-tech and high value-added agricultural technical paper for bagging and protectin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D103/04C09D101/28C09D105/08C09D7/12D21H19/38D21H19/40D21H19/44D21H19/46D21H19/52D21H19/54D21H19/62D21H19/64D21H21/12
CPCC08K2003/265C08L2205/03C09D103/04D21H19/385D21H19/40D21H19/44D21H19/46D21H19/52D21H19/54D21H19/62D21H19/64D21H21/12
Inventor 唐艳军王小宇张恺杰
Owner ZHEJIANG XINFENG SPECIAL PAPER
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More