[0028] A method for electroless silver-tungsten alloy plating on a rhinestone pavilion, comprising the steps of:
[0029] Step 1. Scrub the rhinestones that wrap the crown and expose the pavilion after absorbing the film through a scrubbing machine. During the scrubbing process, circulate and spray the scrubbing solution on the brush through a corrosion-resistant pump; the composition of the scrubbing solution includes in parts by weight: 1 part of alumina powder, 1 part of calcium carbonate powder, 2 parts of gelatin, 2 parts of glycerin, 1 part of sodium lauryl sulfate, 93 parts of water.
[0030] Step 2. Put the water drill treated in step 1 into an ultrasonic wave equipped with a degreasing liquid and clean it for 15 minutes, and then rinse it with clear water; the composition of the degreasing liquid includes by weight: 6 parts of sodium phosphate, 6 parts of sodium carbonate, 1 part of sodium silicate, 87 parts of water.
[0031] Step 3. Put the rhinestones treated in s...
Embodiment 2
[0038] A method for electroless silver-tungsten alloy plating on a rhinestone pavilion, comprising the steps of:
[0039] Step 1. Scrub the rhinestones that wrap the crown and expose the pavilion after absorbing the film through a scrubbing machine. During the scrubbing process, circulate and spray the scrubbing solution on the brush through a corrosion-resistant pump; the composition of the scrubbing solution includes in parts by weight: 1 part of alumina powder, 1 part of calcium carbonate powder, 2 parts of gelatin, 2 parts of glycerin, 1 part of sodium lauryl sulfate, 93 parts of water.
[0040] Step 2. Put the water drill treated in step 1 into an ultrasonic wave equipped with a degreasing solution for cleaning for 30 minutes, and then rinse it with clean water; the composition of the degreasing solution includes by weight: 6 parts of sodium phosphate, 6 parts of sodium carbonate, 1 part of sodium silicate, 87 parts of water.
[0041] Step 3. Put the rhinestones treated ...
Embodiment 3
[0048] A method for electroless silver-tungsten alloy plating on a rhinestone pavilion, comprising the steps of:
[0049] Step 1. Scrub the rhinestones that wrap the crown and expose the pavilion after absorbing the film through a scrubbing machine. During the scrubbing process, circulate and spray the scrubbing solution on the brush through a corrosion-resistant pump; the composition of the scrubbing solution includes in parts by weight: 1 part of alumina powder, 1 part of calcium carbonate powder, 2 parts of gelatin, 2 parts of glycerin, 1 part of sodium lauryl sulfate, 93 parts of water.
[0050] Step 2. Put the water drill treated in step 1 into an ultrasonic wave equipped with a degreasing liquid and clean it for 20 minutes, and then rinse it with clear water; the composition of the degreasing liquid includes by weight: 6 parts of sodium phosphate, 6 parts of sodium carbonate, 1 part of sodium silicate, 87 parts of water.
[0051] Step 3. Put the rhinestones treated in s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap