Preparation method of high-strength glass fiber non-woven wallpaper

A glass fiber and non-woven technology, which is applied in the field of preparation of high-strength glass fiber non-woven wallpaper, can solve problems such as insufficient breaking strength and poor air permeability, and achieve improved flexural strength, omission of the coating process, and high breaking strength and the effect of improving the flexural strength

Inactive Publication Date: 2017-12-29
汪逸凡
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem mainly solved by the present invention is: aiming at the problems of poor air permeability and insufficient breaking strength of traditional glass fiber non-woven wallpaper, a preparation method of high-strength glass fiber non-woven wallpaper is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022]Mix glass fiber and coupling agent in a beaker at a mass ratio of 1:10, soak for 4 hours, filter to obtain a filter cake, move the filter cake into an oven, and dry it for 60 minutes at a temperature of 85°C, then Under the condition of temperature of 150°C, heat preservation reaction for 90 minutes to obtain pretreated glass fiber; mix rubber emulsion and peroxide initiator in a beaker at a mass ratio of 12:1, and move the beaker into a digital speed measuring constant temperature magnetic stirrer, At a temperature of 50°C and a rotational speed of 320r / min, stir and react at a constant temperature for 3 hours, then add pretreated glass fibers 0.6 times the mass of the rubber emulsion into the flask, and move the flask to room temperature, soak for 4 hours, Filtrate to obtain preliminary grafted glass fibers, hang and dry the preliminary grafted glass fibers until there is no more dripping of the emulsion, then move the dried preliminary grafted glass fibers into a vacuu...

example 2

[0024] Mix glass fiber and coupling agent in a beaker at a mass ratio of 1:10, soak for 4 hours, filter to obtain a filter cake, move the filter cake into an oven, and dry it for 60 minutes at a temperature of 85°C, then Under the condition of temperature of 150°C, heat preservation reaction for 90 minutes to obtain pretreated glass fiber; cut aramid fiber to 4mm to obtain aramid staple fiber, mix aramid staple fiber and coupling agent at a mass ratio of 1:10, soak After 7 hours, filter to obtain pretreated aramid staple fiber; mix the dry acidified grafted glass fiber with the pretreated aramid staple fiber at a mass ratio of 5:1, add water six times the mass of the dry acidified grafted glass fiber, and At a temperature of 75°C and a rotation speed of 300r. / min, stir and react for 150 minutes, then filter to obtain mixed glass fibers, move the mixed glass fibers into a drying oven, and dry at a temperature of 95°C for 70 minutes to obtain modified Glass fiber: Mix the modifi...

example 3

[0026] Mix glass fiber and coupling agent in a beaker at a mass ratio of 1:10, soak for 4 hours, filter to obtain a filter cake, move the filter cake into an oven, and dry it for 60 minutes at a temperature of 85°C, then Under the condition of temperature of 150°C, heat preservation reaction for 90 minutes to obtain pretreated glass fiber; mix rubber emulsion and peroxide initiator in a beaker at a mass ratio of 12:1, and move the beaker into a digital speed measuring constant temperature magnetic stirrer, At a temperature of 50°C and a rotational speed of 320r / min, stir and react at a constant temperature for 3 hours, then add pretreated glass fibers 0.6 times the mass of the rubber emulsion into the flask, and move the flask to room temperature, soak for 4 hours, Filtrate to obtain preliminary grafted glass fibers, hang and dry the preliminary grafted glass fibers until there is no more dripping of the emulsion, then move the dried preliminary grafted glass fibers into a vacu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of high-strength glass fiber non-woven wallpaper, and belongs to the technical field of decorative materials. The preparation method comprises the following steps: firstly, performing a reaction on rubber molecule-grafted glass fiber and pretreated aramid staple fiber to obtain modified glass fiber, then mixing the modified glass fiber with water, adding a dispersant, stirring for mixing to obtain mixed liquid, adjusting the pH of a mixed liquid system to 3-4 by using a hydrochloric acid solution, transferring the mixed liquid to a pulping machine, and pulping to obtain a pulp; transferring the pulp to a wet net forming machine, performing wet net forming, drying and performing hot rolling to obtain preformed glass fiber non-woven wallpaper, transferring the preformed glass fiber non-woven wallpaper to a blast dryer, and performing blast drying to obtain the high-strength glass fiber non-woven wallpaper. The glass fiber non-woven wallpaper prepared according to the preparation method provided by the invention has excellent breaking strength and fracture resistance, and has a breathability improved to a certain extent.

Description

technical field [0001] The invention discloses a preparation method of high-strength glass fiber non-woven wallpaper, which belongs to the technical field of decorative materials. Background technique [0002] In recent years, indoor fires have occurred frequently. Once the traditional wallpaper is burned, it will release a large amount of poisonous gas, or the wallpaper itself will burn, causing secondary damage. The use of firewall paper can effectively prevent the fire from spreading and reduce the damage caused by the fire. The glass fiber has a circular cross-section and a constant diameter, and the dimensional stability of the fiber is high. It has water and oil resistance, good acid and alkali resistance and heat resistance, and has good sound absorption effect. Glass fiber is used as the fiber raw material, and the wet non-woven production process is adopted to produce glass fiber wallpaper. This glass fiber wet-laid wallpaper has the advantages of non-combustibil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/20D21H21/08D21H21/14
CPCD21H27/20D21H21/08D21H21/14
Inventor 汪逸凡徐颜峰张琳
Owner 汪逸凡
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products