Processing Technology of Polymer Synthetic Paper

A processing technology and technology of synthetic paper, applied in other household appliances, flat products, household appliances, etc., can solve the problems of air environment damage, complex production process, poor paper toughness, etc., and achieve the effect of high definition

Active Publication Date: 2022-04-19
河北凯成包装股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the process of paper production, a large amount of wood pulp is needed, so a large amount of forest resources need to be cut down. At the same time, the production process will cause pollution to water resources and damage to the air environment. The production process is relatively complicated, and the paper toughness Poor, unable to meet the needs of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing Technology of Polymer Synthetic Paper
  • Processing Technology of Polymer Synthetic Paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The polymer synthetic paper includes the following raw materials in parts by weight:

[0047]80 parts of polyvinyl chloride, 1.15 parts of calcium zinc stabilizer, 1.62 parts of XT-1 rare earth stabilizer, 1.73 parts of dibutyltin maleate laurate, 22 parts of diethyl phthalate, 7 parts of ACR tensile modification agent, 2.5 parts of monoglyceride stearate, 4.4 parts of polyethylene wax, 130 parts of calcium carbonate, 18 parts of talcum powder, 19 parts of starch, 5 parts of white carbon black, 13 parts of titanium dioxide;

[0048] Comprise 0.43 part of zinc stearate, 0.43 part of calcium stearate, 0.07 part of magnesium oxide and 0.22 part of glass fiber in the calcium zinc stabilizer;

[0049] Among them, the particle diameter of calcium carbonate is 6000 mesh, the particle diameter of talcum powder is 1500 mesh, the particle diameter of starch is 100 mesh, the particle diameter of white carbon black is 1000 mesh, and the particle diameter of titanium dioxide is 500 ...

Embodiment 2

[0058] The polymer synthetic paper includes the following raw materials in parts by weight:

[0059] 90 parts of polyvinyl chloride, 1.05 parts of calcium zinc stabilizer, 1.24 parts of XT-2 rare earth stabilizer, 1.71 parts of dibutyltin dilaurate, 28 parts of dioctyl phthalate, 4 parts of ACR tensile modifier, 2 parts of monoglyceride stearate, 5 parts of polyethylene wax, 145 parts of calcium carbonate, 12 parts of talc, 17 parts of starch, 7 parts of white carbon black, 12 parts of titanium dioxide;

[0060] Comprise 0.42 part of zinc stearate, 0.37 part of calcium stearate, 0.08 part of magnesium oxide and 0.18 part of glass fiber in the calcium zinc stabilizer;

[0061] Among them, the particle diameter of calcium carbonate is 7000 mesh, the particle diameter of talcum powder is 2000 mesh, the particle diameter of starch is 200 mesh, the particle diameter of white carbon black is 2000 mesh, and the particle diameter of titanium dioxide is 600 mesh;

[0062] The processi...

Embodiment 3

[0070] The polymer synthetic paper includes the following raw materials in parts by weight:

[0071] 95 parts of polyvinyl chloride, 1.15 parts of calcium zinc stabilizer, 1.15 parts of XT-1 rare earth stabilizer, 1.9 parts of dibutyltin maleate laurate, 26 parts of dioctyl phthalate, 5 parts of ACR tensile modification agent, 2.2 parts of monoglyceride stearate, 4.6 parts of polyethylene wax, 150 parts of calcium carbonate, 20 parts of talcum powder, 23 parts of starch, 4 parts of white carbon black, 10 parts of titanium dioxide;

[0072] Comprise 0.49 part of zinc stearate, 0.37 part of calcium stearate, 0.1 part of magnesium oxide and 0.18 part of glass fiber in the calcium zinc stabilizer;

[0073] Among them, the particle diameter of calcium carbonate is 6500 mesh, the particle diameter of talcum powder is 2000 mesh, the particle diameter of starch is 150 mesh, the particle diameter of white carbon black is 1500 mesh, and the particle diameter of titanium dioxide is 700 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing technology of polymer synthetic paper. In the production process of synthetic paper, no water is needed, and many organic chlorides such as strong acid, strong alkali and bleaching powder are not added. Several important links such as washing and bleaching. Fundamentally eliminate the pollution caused by the "three wastes" in the papermaking process. In addition, the synthetic paper produced has no fibers, and the clarity is higher after inkjet to EP brush. In addition, the surface of the synthetic paper is not coated, and it will not chemically react with the ink to cause color cast and decolorization.

Description

technical field [0001] The invention relates to the field of paper, in particular to a processing technology of polymer synthetic paper. Background technique [0002] Nowadays, paper has become an indispensable part of people's life. As the most traditional and oldest information recording carrier, it is widely used in packaging materials, sanitary materials, environmental protection tableware and other fields. China has become the largest of paper products consuming countries. With the rapid development of the economy and the continuous improvement of people's living standards, people's excessive use and over-reliance on paper makes people's demand for paper still increase year by year. At present, in the process of paper production, a large amount of wood pulp is needed, so a large amount of forest resources need to be cut down. At the same time, the production process will cause pollution to water resources and damage to the air environment. The production process is rel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L23/06C08L3/02C08K13/04C08K7/14C08K5/098C08K3/22C08K3/26C08K3/34C08K3/36C08K5/12B29D7/01
Inventor 成学庆成文龙张珊珊孙宏宇
Owner 河北凯成包装股份有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com