Superhydrophobic paper and preparation method thereof
A super-hydrophobic paper and super-hydrophobic technology, applied in the field of functional paper, can solve the problems of complex preparation process and procedure, poor scratch resistance, unfavorable impregnation of wax substances, etc., to improve super-hydrophobic performance, reduce surface energy, roughness added effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0032] A preparation method of superhydrophobic paper, comprising the following steps:
[0033] (1) Hydroxylation modification of the paper: soak the paper in a sodium hydroxide solution with a pH value of 10 for 5 minutes, take it out, place it in the middle of a double-layer polyethylene film, and bake it at 110°C for 3 minutes.
[0034](2) The paper is etched by the plasma etching method, and the process of the plasma etching method for the paper fiber is: SF 6 The flow rate is 100 sccm, O 2 flow rate of 30 sccm, C 4 f 8 The flow rate is 6sccm, the power is 800W, the RF power is 25W, the RF frequency is 300Hz, the duty cycle is 25%, the etching temperature is 25°C, and the chamber pressure is 80mT.
[0035] (3) Put the etched paper in the vapor of perfluorodecyltriethoxysilane, let it stand at 200°C for 1.5h, and then cool it to room temperature to obtain fluorine-modified paper.
[0036] (4) Use Ar as the gas source to perform plasma pretreatment on the paper. The spec...
Embodiment 2
[0040] A preparation method of superhydrophobic paper, comprising the following steps:
[0041] (1) Hydroxylation modification of the paper: soak the paper in a sodium hydroxide solution with a pH value of 11.7 for 8 minutes, take it out, place it in the middle of a double-layer polyethylene film, and bake it at 110°C for 3 minutes.
[0042] (2) The paper is etched by the plasma etching method, and the process of the plasma etching method for the paper fiber is: SF 6 The flow rate is 200 sccm, O 2 The flow rate is 45 sccm, C 4 f 8 The flow rate is 120sccm, the power is 1000W, the RF power is 15W, the RF frequency is 400Hz, the duty cycle is 20%, the etching temperature is 30°C, and the chamber pressure is 50mT.
[0043] (3) After the etched paper was placed in the vapor of perfluorooctane sulfonic acid, it was allowed to stand at 180°C for 1.5h, and then cooled to room temperature to obtain fluorine-modified paper.
[0044] (4) Use Ar as the gas source to perform plasma pr...
Embodiment 3
[0048] A preparation method of superhydrophobic paper, comprising the following steps:
[0049] (1) Hydroxylation modification of the paper: soak the paper in a sodium hydroxide solution with a pH value of 12 for 3 minutes, take it out, place it in the middle of a double-layer polyethylene film, and bake it at 110°C for 3 minutes.
[0050] (2) The paper is etched by the plasma etching method, and the process of the plasma etching method for the paper fiber is: SF 6 The flow rate is 10 sccm, O 2 The flow rate is 5 sccm, C 4 f 8 The flow rate is 100sccm, the power is 300W, the RF power is 50W, the RF frequency is 500Hz, the duty cycle is 50%, the etching temperature is 10°C, and the chamber pressure is 10mT.
[0051] (3) Put the etched paper in the vapor of octadecyltrichlorosilane, let it stand at 100°C for 2 hours, and then cool it to room temperature to obtain fluorine-modified paper.
[0052] (4) Use Ar as the gas source to perform plasma pretreatment on the paper. The s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com