Carbon nanotube/micro-expansion graphite composite heat-conducting silicone grease and preparation method thereof

A technology of thermal conductive silicone grease and micro-expanded graphite, which is applied in the field of carbon nanotube/micro-expanded graphite composite thermal conductive silicone grease and its preparation, and achieves the effects of simple preparation process, good interface contact and large reserves

Inactive Publication Date: 2018-02-23
郴州国盛新材科技有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no research on the application of micro-expanded graphite in thermally conductive silicone grease materials in the prior art. How to apply micro-expanded graphite in thermally conductive silicone grease materials and exert its excellent thermal conductivity, softness, resilience and plasticity is worthy of our attention. research

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The present embodiment provides a kind of preparation method of micro-expanded graphite material, comprises the following steps:

[0034] S11. Get the microcrystalline graphite raw material with carbon content of 70% and the flake graphite raw material with carbon content of 85%, the mass ratio of flake graphite and microcrystalline graphite is 2:1, crushing and grinding, until particle size is 300 purpose mixed graphite powder;

[0035] S12. Place the mixture obtained in S11 in a muffle furnace, slowly heat up to 350° C. under a nitrogen atmosphere, keep it warm for 30 minutes, and air-cool to room temperature for use;

[0036] S13. Perform chemical intercalation treatment on the mixture after S12 heat treatment to obtain expandable mixed graphite, wherein the specific steps of chemical intercalation treatment are as follows: S131. Mix perchloric acid and microcrystalline graphite powder at a liquid-solid ratio of 10:1L / Kg mix and stir evenly; S132. Add strong oxidant...

Embodiment 2

[0039] This embodiment provides a method for preparing a carbon nanotube / micro-expanded graphite composite heat-conducting silicone grease, using the micro-expanded graphite material in Example 1.

[0040] S1. Immerse the micro-expanded graphite in the ferric nitrate aqueous solution, filter it after ultrasonic vibration for a certain period of time, and dry it in vacuum. Put the dried material in the furnace, raise the temperature to 650°C under the protective gas atmosphere, and then pass in C2H2 gas to keep it warm 40min, then cooled to room temperature under a protective gas atmosphere to obtain a carbon nanotube / micro-expanded graphite composite material for subsequent use;

[0041] S2. Take 400 parts of absolute ethanol and put it into the reaction kettle, take 3% coupling agent of thermally conductive filler and add it into the reaction kettle, and stir at a constant temperature of 60°C and 100r / min for 10min to obtain an ethanol solution;

[0042] S3. Add the composite...

Embodiment 3

[0046] This embodiment provides a method for preparing a carbon nanotube / micro-expanded graphite composite heat-conducting silicone grease, using the micro-expanded graphite material in Example 1.

[0047]S1. Immerse the micro-expanded graphite in the ferric nitrate aqueous solution, filter it after ultrasonic vibration for a certain period of time, and dry it in vacuum. Put the dried material in the furnace, raise the temperature to 700°C under the protective gas atmosphere, and then pass in C2H2 gas to keep it warm 50min, then cooled to room temperature under a protective gas atmosphere to obtain a carbon nanotube / micro-expanded graphite composite material for subsequent use;

[0048] S2. Put 400 parts of absolute ethanol into the reactor, take 8% coupling agent of thermally conductive filler and add it into the reactor, stir at a constant temperature of 100°C and 300r / min for 30min to obtain an ethanol solution;

[0049] S3. Add the composite material in step S1 into the et...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses carbon nanotube / micro-expansion graphite composite heat-conducting silicone grease and a preparation method thereof. The preparation comprises the following steps: firstly preparing a carbon nanotube / micro-expansion graphite composite material, adding to an ethanol solution, and carrying out ultrasonic stirring until ethanol is completely evaporated, so as to obtain a modified compound heat-conducting filling; and adding the heat-conducting filling, methyl phenyl silicone oil, a crosslinking agent, a structure improver and an antioxidant into an internal mixer, carryingout internal mixing, so as to obtain the composite heat-conducting silicone grease. The prepared heat-conducting silicone grease has excellent thermal stability, is low in oil separation value and does not crack and atomize after being used for a long time. Meanwhile, a preparation process is simple and short in cycle and has important significance to the improvement of the quality in industry products.

Description

technical field [0001] The invention relates to a carbon nanotube / micro-expanded graphite composite heat-conducting silicone grease and a preparation method thereof, which are mainly applicable to the fields of encapsulation and heat dissipation of high-power electronic components. Background technique [0002] Thermally conductive silicone grease is a kind of high thermal conductive silicone material, which can maintain the paste shape for a long time at the temperature of -50~300°C. It is widely used between the heating element and the heat dissipation base of high-power electronic components, effectively reducing the interface contact heat. resistance. With the development of high-power and intensive electronic components, there is an increasing demand for high-performance thermally conductive silicone grease with high thermal conductivity, excellent thermal stability, and low oil separation value. [0003] Micro-expanded graphite is a kind of graphite interlayer compoun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08K7/24C08K9/06C08K7/00C08K13/06C08K5/14C08K3/36C08K5/18C09K5/14
CPCC08K3/36C08K5/14C08K5/18C08K7/00C08K7/24C08K9/06C08K9/12C08K13/06C08K2201/011C08K2201/014C08L83/04C08L2203/20C09K5/14
Inventor 李丽萍
Owner 郴州国盛新材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap