High-temperature-resisting and environment-friendly solid glue and preparation method thereof

A technology of solid glue and high temperature resistance, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of environmental pollution, viscosity reduction, easy leakage, etc., and achieve simple preparation process, Good adhesion and good oxidation resistance

Inactive Publication Date: 2018-02-23
ANHUI TUQIANG STATIONERY MFG
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Liquid glue is not as convenient to use as solid glue. Liquid glue is easy to leak if it is overturned on the ground, and the bottle mouth of liquid glue is generally used with a sponge. After the sponge has been used with glue, if it is not used for a day or two, or the lid is forgotten Yes, the surface glue will evaporate and solidify when it encounters wind, so the sponge will harden, making subsequent use extremely inconvenient
The solid glue sold in the general market is white, but it will deteriorate at high temperature, its viscosity will be greatly reduced (adhesion ability varies), and it will emit toxic odor gas, which generally pollutes the environment. Some disadvantages, some long-term contact will cause damage to the user's body and pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The high-temperature-resistant environmental protection solid glue described in this embodiment contains the following components: 40 parts of light nano-calcium carbonate, 20 parts of deionized water, 10 parts of aluminum silicate ceramic fiber, 10 parts of sodium stearate, 4 parts of ethylene, 5 parts of straw ashes, 5 parts of grass ash, 8 parts of acrylamide, 1 part of calcium formate, 1 part of polyhydroxy acid-based high-performance water reducer, 1 part of lignin, 3 parts of silane-based water repellent, 3 parts of diatomaceous earth , 1 part of titanium dioxide, 3 parts of nano-titanium dioxide, 1 part of active agent, and 0.5 part of preservative.

[0018] As a further improvement, the active agent is a transparent soap base, and the preservative is a mixture of propyl ester and ethyl ester.

[0019] As a further improvement, the length of the lignin is 1 mm, and the length of the aluminum silicate ceramic fiber is 0.8 mm.

[0020] Specifically, the preparatio...

Embodiment 2

[0028] The high-temperature-resistant environmental protection solid glue described in this embodiment contains the following components: 50 parts of light nano-calcium carbonate, 25 parts of deionized water, 12 parts of aluminum silicate ceramic fiber, 12 parts of sodium stearate, 5 parts of ethylene, 6 parts of straw ashes, 6 parts of grass ash, 10 parts of acrylamide, 2 parts of calcium formate, 2 parts of polyhydroxy acid-based high-performance water reducer, 2 parts of lignin, 4 parts of silane-based water repellent, 4 parts of diatomaceous earth , 2 parts of titanium dioxide, 4 parts of nano-titanium dioxide, 1.5 parts of active agent, and 0.75 parts of preservative.

[0029] As a further improvement, the active agent is a transparent soap base, and the preservative is a mixture of propyl ester and ethyl ester.

[0030] As a further improvement, the length of the lignin is 1 mm, and the length of the aluminum silicate ceramic fiber is 0.95 mm.

[0031] Specifically, the...

Embodiment 3

[0039] The high-temperature-resistant environmental protection solid glue described in this embodiment contains the following components: 60 parts of light nano-calcium carbonate, 30 parts of deionized water, 15 parts of aluminum silicate ceramic fiber, 15 parts of sodium stearate, 6 parts of ethylene, 7 parts of straw ashes, 7 parts of grass ash, 12 parts of acrylamide, 3 parts of calcium formate, 3 parts of polyhydroxy acid-based high-performance water reducer, 3 parts of lignin, 5 parts of silane-based water repellent, 5 parts of diatomaceous earth , 3 parts of titanium dioxide, 5 parts of nano-titanium dioxide, 2 parts of active agent, and 1 part of preservative.

[0040] As a further improvement, the active agent is a transparent soap base, and the preservative is a mixture of propyl ester and ethyl ester.

[0041] As a further improvement, the length of the lignin is 1 mm, and the length of the aluminum silicate ceramic fiber is 1.1 mm.

[0042] Specifically, the prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-temperature-resisting and environment-friendly solid glue. The high-temperature-resisting and environment-friendly solid glue is prepared from the following components: 40to 60 parts of light nano calcium carbonate, 20 to 30 parts of deionized water, 10 to 15 parts of aluminum silicate ceramic fibers, 10 to 15 parts of sodium stearate, 4 to 6 parts of ethylene, 5 to 7parts of straw ashes, 5 to 7 parts of grass ashes, 8 to 12 parts of acrylamide, 1 to 3 parts of calcium formate, 1 to 3 parts of polycarboxylate-type high-performance water reducer, 1 to 3 parts of xylogen, 3 to 5 parts of silylation water repellent, 3 to 5 parts of diatomite, 1 to 3 parts of titanium dioxide, 3 to 5 parts of nano titanium dioxide, 1 to 2 parts of active agent and 0.5 to 1 part of preservative. The solid glue disclosed by the invention has the advantages of high-temperature resistance, high hardness, good moisture retention, smoothness without dropping residues while smearing, good adhesion, good oxidation resistance, environmental protection and no toxicity; in addition, the preparation process is simple and feasible, and actual service requirements are met.

Description

technical field [0001] The invention relates to a high-temperature-resistant environment-friendly solid glue and a preparation method thereof, belonging to the technical field of bonding solid glue. Background technique [0002] Our common adhesive papers are liquid glue and solid glue. Liquid glue is not as convenient to use as solid glue. Liquid glue is easy to leak if it is overturned on the ground, and the mouth of the bottle of liquid glue is generally used with a sponge. After the sponge is used for glue, if it is not used for a day or two, or the lid is forgotten Yes, the surface glue will evaporate, solidify and harden when exposed to wind, so the sponge will harden, making subsequent use extremely inconvenient. The solid glue sold in the general market is white, but it will deteriorate at high temperature, its viscosity will be greatly reduced (adhesion ability varies), and it will emit toxic odor gas, which generally pollutes the environment. Some disadvantages, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J4/02C09J11/04C09J11/06C09J11/08C09J9/00C09D5/34
CPCC09D5/34C09J4/00C09J9/00C09J11/04C09J11/06C09J11/08
Inventor 赵强
Owner ANHUI TUQIANG STATIONERY MFG