an elastic concrete

A technology of elastic concrete and rubber particles, applied in the field of elastic concrete, can solve the problems of high cost, achieve the effects of increasing service life, improving comfort, and reducing impact damage

Active Publication Date: 2020-05-08
建德市晶磊混凝土有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, some sports fields are laid with plastic track, the main component is polyurethane material, which is expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An elastic concrete, consisting of the following raw materials in parts by weight: 30 parts of cement, 20 parts of slag powder, 40 parts of rubber particles, 3 parts of composite fiber, 0.01 part of polyoxyethylene sorbitan monostearate, 60 parts of emulsified asphalt 10 parts of water-based epoxy resin, 2 parts of polycarboxylate superplasticizer, 0.01 part of defoamer, 2 parts of calcium metaaluminate, 3 parts of modified zeolite powder, 60 parts of sand, and 10 parts of water.

[0027] The cement is P.O42.5 cement.

[0028] The specific surface area of ​​the slag powder is not less than 400m2 / kg, and the 28d activity is not less than 75%.

[0029] The particle size of the rubber particles is between 20-30 mesh.

[0030] The composite fiber is composed of sepiolite powder, wollastonite powder, polyvinyl alcohol fiber, polypropylene fiber, polyacrylonitrile fiber and polyurethane fiber.

[0031] The emulsified asphalt is cationic emulsified asphalt with a solid conte...

Embodiment 2

[0036] An elastic concrete, consisting of the following raw materials in parts by weight: 40 parts of cement, 10 parts of slag powder, 80 parts of rubber particles, 1 part of composite fiber, 0.05 parts of polyoxyethylene sorbitan monostearate, 30 parts of emulsified asphalt 30 parts of water-based epoxy resin, 0.5 parts of polycarboxylate superplasticizer, 0.05 parts of defoamer, 1 part of calcium metaaluminate, 8 parts of modified zeolite powder, 50 parts of sand, and 20 parts of water.

[0037] The rubber particles are polysulfide rubber particles with particle diameters between 20-60 mesh.

[0038] The composite fiber is composed of sepiolite powder, polypropylene fiber and polyacrylonitrile fiber.

[0039] Described polyoxyethylene sorbitan monostearate is polyoxyethylene (60) sorbitan monostearate, and molecular formula is: C 64 h 126 o 26 .

[0040] The defoamer is polyoxyethylene polyoxypropylene pentaerythritol ether.

[0041] The modified zeolite powder is obtai...

Embodiment 3

[0043] An elastic concrete is composed of the following raw materials in parts by weight: 32 parts of cement, 17 parts of slag powder, 63 parts of rubber particles, 2 parts of composite fiber, 0.02 part of polyoxyethylene sorbitan monostearate, 50 parts of emulsified asphalt 15 parts of water-based epoxy resin, 1.5 parts of polycarboxylate superplasticizer, 0.04 parts of defoamer, 1.3 parts of calcium metaaluminate, 7 parts of modified zeolite powder, 54 parts of sand, and 15 parts of water.

[0044] The cement is P.O42.5 cement.

[0045] The specific surface area of ​​the slag powder is not less than 400m2 / kg, and the 28d activity is not less than 75%.

[0046] The rubber particles are polysulfide rubber particles with a particle size between 30-40 mesh.

[0047]The composite fiber is composed of wollastonite powder and polyvinyl alcohol fiber, wherein the diameter of the wollastonite powder fiber is between 0.1-1um and the length is between 10-20um; the fiber diameter of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
specific surface areaaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of new materials and discloses elastic concrete. The elastic concrete comprises the following raw materials in parts by weight: 30-40 parts of cement, 10-20 parts of slag powder, 40-80 parts of rubber particles, 1-3 parts of a composite fiber, 0.01-0.05 part of polyoxyethylene sorbitan monostearate, 30-60 parts of emulsified asphalt, 10-30 parts of water-borne epoxy resin, 0.5-2 parts of a polycarboxylate superplasticizer, 0.01-0.05 part of a defoamer, 1-2 parts of calcium metaaluminate, 3-8 parts of modified zeolite powder, 50-60 parts of sand and10-30 parts of water. The elastic concrete is compounded by inorganic materials, is low in price, high in elasticity, good in flexibility and excellent in anti-freezing property, can be used for outdoor works, can effectively absorb an impact force brought by exercise, improves the degree of comfort during exercise and reduces injuries of the impact force on a body; and as the rubber particles arelow in heat conductivity coefficient and high in flexibility, an outdoor sport field can be prevented from free-thaw damages, and the service life of the field is prolonged.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to elastic concrete. [0002] technical background [0003] With the development of urban construction and the improvement of people's living standards, people expect the ground of leisure, fitness and entertainment venues such as sports fields and exhibition halls to have a certain degree of elasticity and noise reduction. At present, some sports grounds are laid with plastic track, and the main component is polyurethane material, which is expensive. [0004] At the same time, with the rapid development of the automobile industry, the generation and accumulation of a large number of waste rubber tires has constituted a serious "black pollution". Processing waste rubber materials and mixing them into concrete can not only solve the problem of environmental pollution caused by waste rubber, but also make good use of the elasticity of rubber powder to prepare concret...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2201/50C04B18/141C04B16/04C04B14/042C04B14/043C04B16/0641C04B16/0633C04B16/0658C04B16/0675C04B24/32C04B24/36C04B24/281C04B24/24C04B24/003C04B22/0093C04B14/047C04B14/06
Inventor 程业秀
Owner 建德市晶磊混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap