Heat-resistant cable surface material and preparation method thereof

A surface material and cable technology, which is applied in the field of heat-resistant cable surface material and its preparation, and cable materials, can solve the problems of unusable wire and cable, etc., achieve the effects of increased filling density, guaranteed finishing effect, and simple reaction operation

Inactive Publication Date: 2018-04-03
QINGDAO DONGHAO SOFTWARE TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for some special industries such as petrochemical, steel, aerospace, shipbuilding, military, pharmaceutical, food, plastic machinery, boilers and other industries related to heat and high temperature, wires and cables that can withstand a certain higher temperature are required. The cable obviously can't be used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Synthetic example 1

[0018] Add 1Kg of p-aminobenzoic acid to the dry reactor, then add 25Kg of ethanol, stir under reflux for 50 minutes; then add 100g of imine dibasic acid, reflux for 2 hours; then add 800g of pentaerythritol tetraacrylate, reflux for 2 hours An organic solution is obtained.

Synthetic example 2

[0020] Add 1Kg of ytterbium nitrate into water to prepare an aqueous solution, then add 1Kg of a 20% mass concentration of 20% zirconium oxychloride aqueous solution, stir, then react at 180°C for 10 hours, cool naturally, and centrifuge to obtain a solid; then treat 80 at 1250°C After a few minutes, it was naturally cooled to obtain a powder filler with an average particle size of 80 nm.

Embodiment 1

[0022] Dissolve 30g of tetramethyl bisphenol F cyanate resin monomer into 150g of epoxy resin E44, stir at 150°C for 80 minutes; then add methyl ethyl ketone and stir at 50°C for 10 minutes; add 30g of isotridecyl alcohol Polyoxyethylene ether, stir; then add 230g organic solution, 80g filler, and stir for 1 hour at 60°C; then add 20g polymethylsilsesquioxane (molecular weight of 12,000 to 16,000), and stir to obtain a surface solution; finally, the surface layer The melt is dried at 80°C and cured at 120°C / 1 minute + 150°C / 30 seconds to obtain a heat-resistant cable surface material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a heat-resistant cable surface material. The tetramethylbisphenol F cyanate resin monomer is dissolved in epoxy resin E44, stirred at 150°C for 80 minutes; Stir at ℃ for 10 minutes; then add isomeric tridecanol polyoxyethylene ether, stir; then add organic solution and filler, and stir at 60°C for 1 hour; then add polymethylsilsesquioxane (molecular weight: 1.2 to 16,000) , stirred to obtain a surface layer solution; finally, the surface layer melt was dried at 80°C, cured at 120°C / 1 minute + 150°C / 30 seconds to obtain a heat-resistant cable surface layer material. In the method disclosed by the invention, each raw material is easy to obtain, the utilization rate is high, and the reaction is uniform; the reaction operation is simple, the reaction process is short, the efficiency is high, and it is suitable for industrial production. There are good applications in the field.

Description

Technical field [0001] The invention relates to a cable material, in particular to a heat-resistant cable surface material and a preparation method thereof, and belongs to the technical field of electronic materials. Background technique [0002] The history of the use of composite materials can be traced back to ancient times. The rice straw or wheat straw reinforced clay used from ancient times to the present and the reinforced concrete that has been used for hundreds of years are both composites of two materials. Composite materials can be divided into two categories: structural composite materials and functional composite materials. Functional composite materials are generally composed of functional body components and matrix components. The matrix not only plays the role of forming a whole, but also can produce synergy or strengthen the function. It is a material that provides other physical properties in addition to mechanical properties, such as: conductive, superconducti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L79/04C08L83/04C08K9/00C08K5/29C08K3/28
CPCC08L63/00C08K2201/003C08L2201/08C08L2203/202C08L2205/035C08L79/04C08L83/04C08K9/00C08K5/29C08K3/28
Inventor 盖浩然
Owner QINGDAO DONGHAO SOFTWARE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap